Direct Printing of 1-D and 2-D Electronically Conductive Structures by Molten Lead-Free Solder.

This study aims to determine the effects of appropriate experimental parameters on the thermophysical properties of molten micro droplets, Sn-3Ag-0.5Cu solder balls with an average droplet diameter of 50 µm were prepared. The inkjet printing parameters of the molten micro droplets, such as the dot spacing, stage velocity and sample temperature, were optimized in the 1D and 2D printing of metallic microstructures. The impact and mergence of molten micro droplets were observed with a high-speed digital camera. The line width of each sample was then calculated using a formula over a temperature range of 30 to 70 °C. The results showed that a metallic line with a width of 55 µm can be successfully printed with dot spacing (50 µm) and the stage velocity (50 mm∙s-1) at the substrate temperature of 30 °C. The experimental results revealed that the height (from 0.63 to 0.58) and solidification contact angle (from 72° to 56°) of the metallic micro droplets decreased as the temperature of the sample increased from 30 to 70 °C. High-speed digital camera (HSDC) observations showed that the quality of the 3D micro patterns improved significantly when the droplets were deposited at 70 °C.

Fabrication of Microdots Using Piezoelectric Dispensing Technique for Viscous Fluids.

A simple microfluidic control method that uses a piezoelectric dispenser head is developed to fabricate microdots. A glycerol mixture was used as the test fluid to simulate conductive metallic solutions. The orifice diameter of the dispenser was 50 µm. Investigations were conducted at room temperature (25 °C). For each bipolar waveform, fluid was extruded in the form of a stretching liquid column, which eventually retracted into the dispenser orifice. Microdots were obtained by governing the liquid transfer process between the dispenser orifice and the target surface, where the gap was smaller than the maximum extrusion length during liquid column formation. Three fluid behaviors were observed using high-speed imaging, namely extrusion, impact on the target surface, and pinch-off of liquid ligament. For gaps of below 70 µm, some of the fluid sticking on the target surface resulted in a microdot diameter of 26 µm (about half of the orifice diameter).