RESUMEN
In this work, we study surface functionalization effects of artificially stacked graphene bilayers (ASGBs) to control its wetting properties via low-damage plasma. The ASGBs were prepared on a SiO2/Si substrate by stacking two monolayer graphene, which was grown by chemical vapor deposition. As a result, the low-damage plasma functionalization of ASGBs could hold both the key characteristics of surface functionalization and electrical transport properties of graphene sheets. To characterize ASGBs, Raman and x-ray photoelectron spectroscopy (XPS) were used to determine the degree of defect formation and functionalization. Meanwhile, the degree of the wettability of the ASGBs surface was determined by optical contact angle (CA) measurements. Based on experimental results, the compositional ratio of C-OH + COOH was found to increase 67% based on the analysis of XPS spectra after low-damage plasma treatment. This treatment effect can also be found with 75.3% decrease in the CA of water droplet on graphene. In addition, we found that the ratio of 2D/(D + G') in Raman spectra shows strong correlation to the measured CA; it can be a reliable indicator of ASGBs surface wettability modification. This work showed that we obtained a higher degree functionalization of ASGBs without degrading the under-layer structure of ASGBs due to the moderate low-damage plasma treatment. The presented process technique of controllable wettability through low-damage plasma treatment can be employed for potential application in graphene-based sensors/devices.
RESUMEN
The interface between LaAlO3 (LAO) and SrTiO3 (STO) has attracted enormous interests due to its rich physical phenomena, such as metallic nature, magnetism and superconductivity. In this work, we report our experimental investigations on the influence of the LAO stoichiometry to the metallic interface. Taking advantage of the oxide molecular beam epitaxy (MBE) technique, a series of high quality LAO films with different nominal La/Al ratios and LAO thicknesses were grown on the TiO2-terminated STO substrates, where systematic variations of the LAO lattice constant and transport property were observed. In particular, the sheet density can be largely reduced by nearly an order of magnitude with merely about 20% increase in the nominal La/Al ratio. Our finding provides an effective method on tuning the electron density of the two-dimensional electron liquid (2DEL) at the LAO/STO interface.