Response of mouse bone marrow mesenchymal stem cells to graphene-containing grid-like bioactive glass scaffolds produced by robocasting.

In the study, three-dimensional, grid-like silicate-based bioactive glass scaffolds were manufactured using a robotic deposition technique. Inks were prepared by mixing 13-93 bioactive glass particles in Pluronic® F-127 solution. After deposition, scaffolds were dried at room temperature and sintered at 690°C for 1 h. The surface of the sintered scaffolds was coated with graphene nanopowder (1, 3, 5, 10 wt%) containing poly(ε-caprolactone) solution. The in vitro mineralization ability of the prepared composite scaffolds was investigated in simulated body fluid. The surface of the simulated body fluid-treated scaffolds was analyzed using scanning electron microscopy to investigate the hydroxyapatite formation. Mechanical properties were tested under compression. Results revealed that graphene coating has no detrimental effect on the hydroxyapatite forming ability of the prepared glass scaffolds. On the other hand, it decreased the compression strength of the scaffolds at high graphene concentrations. The prepared grid-like bioactive glass-based composite scaffolds did not show toxic response to bone marrow mesenchymal stem cells. It was shown that stem cells seeded onto the scaffolds attached and proliferated well on the surface. Cells seeded on the scaffolds surface also demonstrated osteogenic differentiation under in vitro conditions in the absence of transforming growth factors.

Electrically conductive borate-based bioactive glass scaffolds for bone tissue engineering applications.

In this study, electrically conductive, borate-based, porous 13-93B3 bioactive glass composite scaffolds were prepared using a polymer foam replication technique. For this purpose, a slurry containing 40 vol% glass particles and 0-10 wt% graphene nanoplatelets was prepared by dispersing the particles in ethanol in the presence of ethyl cellulose. Composite scaffolds were subjected to a controlled heat treatment, in air atmosphere, to decompose the foam and sinter the glass particles into a dense network. It was found that the applied heat treatment did not influence the structure of graphene in the glass network. Graphene additions did not negatively affect the mechanical properties and enhanced the electrical conductivity of the glass scaffolds. In X-ray diffraction analysis, the crystalline peak corresponding to hydroxyapatite was observed in all the samples suggesting that all of the samples were bioactive after 30 days of immersion in simulated body fluid. However, Fourier transform infrared spectroscopy analysis and scanning electron microscope observations revealed that hydroxyapatite formation rate decreased with increasing graphene concentration especially for samples treated in simulated body fluid for shorter times. Based on the cytotoxicity assay findings, the MC3T3-E1 cell growth was significantly inhibited by the scaffolds containing higher amount of graphene compared to bare glass scaffolds. Best performance was obtained for 5 wt% graphene which yielded an enhancement of electrical conductivity with moderate cellular response and in vitro hydroxyapatite forming ability. The study revealed that the electrically conductive 13-93B3 graphene scaffolds are promising candidates for bone tissue engineering applications.