RESUMEN
AIM: This in vitro study aimed to compare the light-transmission properties of two chairside CAD/CAM lithium disilicate (LD) ceramics (a novel fully crystallized and a traditional pre-crystallized) across varying thicknesses. MATERIALS AND METHODS: One hundred flat specimens were obtained from precrystallized (e.max CAD, Ivoclar Vivadent, Schaan, Liechtenstein) and fully crystallized (LiSi GC Block; GC, Tokyo, Japan) LD at five different thicknesses (0.5, 0.75, 1.0, 1.50 and 2.0 mm). All specimens were polished with a polishing system for lithium disilicate restorations following recommendations from the manufacturer. Light transmission was evaluated with a radiometer. The statistical analysis between e.max CAD and LiSi GC Block was performed using a Mann-Whitney test for each thickness at a significance level of 0.05 (p < 0.05), followed by a Kruskal-Wallis test to compare the light transmission between the thicknesses of e.max CAD and LiSi GC Block. RESULTS: Light transmittance was significantly affected by ceramic thickness. The 0.5 mm thick specimens exhibited the highest transmittance values compared to all other groups, while a light transmittance of 0.00 was observed in the 2.0 mm thick specimens for both e.max CAD and LiSi GC Block. In the comparison between e.max CAD and LiSi GC Block according to thickness, there was a statistically significant difference exclusively between groups with a thickness of 1.50 mm (p = 0.002). CONCLUSIONS: Light transmission for pre- and fully crystallized CAD/CAM lithium disilicate ceramics only showed a statistical difference at the thickness of 1.50 mm (p = 0.002). E.max CAD demonstrated acceptable light transmission up to a thickness of 1.5 mm. CLINICAL SIGNIFICANCE: A thickness of 2 mm for chairside CAD/CAM lithium disilicate ceramics, whether pre-crystallized or fully crystallized, necessitates the use of dual-cure resin luting cement due to reduced light transmission.
RESUMEN
BACKGROUND: Zirconia is a widely used material in the dental industry due to its excellent mechanical and aesthetic properties. Recently, a new 3D printing process called suspension-enclosing projection stereolithography (SEPS) was introduced to fabricate zirconia dental restorations. However, the effect of the sintering time and temperature on the properties of zirconia produced via SEPS has not been fully investigated. METHODS: Zirconia slurries were prepared with varying percentages of zirconia powders and 3D printing resins, and 5Y-TZP (5 mol% yttria-stabilized zirconia) (n = 40) and 3Y-TZP (3 mol% yttria-stabilized zirconia) (n = 40) bar specimens were fabricated via SEPS manufacturing. The specimens were sintered at different temperatures and dwell times, and their flexural strength, density, and phase composition were measured. The viscosity of the slurries was also measured. Statistical analysis was performed using Welch's ANOVA and Kruskal-Wallis tests to evaluate the impact of the sintering conditions. RESULTS: Significant differences in flexural strength (p < 0.01) were observed between the 5Y-TZP samples, with those sintered at 1530 °C for 120 min showing an average strength of 268.34 ± 44.66 MPa, compared to 174.16 ± 42.29 MPa for those sintered at 1450 °C for 120 min. In terms of density, significant differences (p < 0.01) were noted for the 3Y-TZP specimens, with an average density of 6.66 ± 0.49 g/cm3 for samples sintered at 1530 °C for 120 min, versus 5.75 ± 0.55 g/cm3 for those sintered at 1530 °C for 10 min. X-ray diffraction confirmed the presence of a predominantly tetragonal phase in both materials. CONCLUSIONS: Zirconia printed via SEPS manufacturing can be sintered at a higher temperature with shorter dwell times, thereby producing high density samples. Different sintering conditions can be used to fully sinter 3D-printed zirconia for potential dental applications.