RESUMEN
BACKGROUND: The use of 3D printing of hydrogels as a cell support in bio-printing of cartilage, organs and tissue has attracted much research interest. For cartilage applications, hydrogels as soft materials must show some degree of rigidity, which can be achieved by photo- or chemical polymerization. In this work, we combined chemical and UV laser polymeric cross-linkage to control the mechanical properties of 3D printed hydrogel blends. Since there are few studies on UV laser cross-linking combined with 3D printing of hydrogels, the work here reported offered many challenges. METHODS: Polyethylene glycol diacrylate (PEGDA), sodium alginate (SA) and calcium sulphate (CaSO4) polymer paste containing riboflavin (vitamin B2) and triethanolamine (TEOHA) as a biocompatible photoinitiator was printed in an extrusion 3D plotter using a coupled UV laser. The influence of the laser power on the mechanical properties of the printed samples was then examined in unconfined compression stress-strain tests of 1 × 1 × 1 cm3 sized samples. To evaluate the adhesion of the material between printed layers, compression measurements were performed along the parallel and perpendicular directions to the printing lines. RESULTS: At a laser density of 70 mW/cm2, Young's modulus was approximately 6 MPa up to a maximum compression of 20% in the elastic regime for both the parallel and perpendicular measurements. These values were within the range of biological cartilage values. Cytotoxicity tests performed with Vero cells confirmed the cytocompatibility. CONCLUSIONS: We printed a partial tracheal model using optimized printing conditions and proved that the materials and methods developed may be useful for printing of organ models to support surgery or even to produce customized tracheal implants, after further optimization.
RESUMEN
Inspired by chitin based hierarchical structures observed in arthropods exoskeleton, this work reports the capturing of chitin nanowhiskers' chiral nematic order into a chitosan matrix. For this purpose, highly crystalline chitin nanowhiskers (CTNW) with spindle-like morphology and average aspect ratio of 24.9 were produced by acid hydrolysis of chitin. CTNW were uniformly dispersed at different concentrations in aqueous suspensions. The suspensions liquid crystalline phase domain was determined by rheological measurements and polarized optical microscopy (POM). Chitosan (CS) was added to the CTNW isotropic, biphasic and anisotropic suspensions and the solvent was evaporated to allow films formation. The Films' morphologies as well as the mechanical properties were explored. A correlation between experimental results and a theoretical model, for layered matrix' structures with fibers acting as a reinforcement agent, was established. The results evidence the existence of two different layered structures, one formed by chitosan layers induced by the presence of chitin and another formed by chitin nanowhiskers layers. By playing on the ratio chitin/chitosan one layered structure or the other can be obtained allowing the tunning of materials' mechanical properties.
RESUMEN
Specimens of aluminum-based composites reinforced by silicon carbide nanoparticles (Al/SiCnp) produced by powder metallurgy (PM) were anodized under voltage control in tartaric-sulfuric acid (TSA). In this work, the influence of the amount of SiCnp on the film growth during anodizing was investigated. The current density versus time response and the morphology of the porous alumina film formed at the composite surface are compared to those concerning a commercial aluminum alloy (AA1050) anodized under the same conditions. The processing method of the aluminum alloys influences the efficiency of the anodizing process, leading to a lower thicknesses for the unreinforced Al-PM alloy regarding the AA1050. The current density versus time response is strongly dependent on the amount of SiCnp. The current peaks and the steady-state current density recorded at each voltage step increases with the SiCnp volume fraction due to the oxidation of the SiCnp. The formation mechanism of the anodic film on Al/SiCnp composites is different from that occurring in AA1050, partly due the heterogeneous distribution of the reinforcement particles in the metallic matrix, but also to the entrapment of SiCnp in the anodic film.
RESUMEN
Reduction by magnetic nano-Fe(3)O(4)-Ni: a facile, simple and environmentally friendly hydrogen-transfer reaction that takes place over recyclable ferrite-nickel magnetic nanoparticles (Fe(3)O(4)-Ni) by using glycerol as hydrogen source allows aromatic amines and alcohols to be synthesized from the precursor nitroarenes and carbonyl compounds.