New results on the effect of TiO2 on Pd/La2O3-CeO2-Al2O3 systems for catalytic oxidation of methane in the presence of H2O and SO2 have been received. Low-temperature N2-adsorption, XRD, SEM, HRTEM, XPS, EPR and FTIR techniques were used to characterize the catalyst. The presence of Ce3+ on the catalytic surface and in the volume near the lantana was revealed by EPR and XPS. After aging, the following changes are observed: (i) agglomeration of the Pd-clusters (from 8 nm to 12 nm); (ii) transformation of part of the TiO2 from anatase to larger particles of rutile; and (iii)-the increase in PdO/Pd-ratio above its optimum. The modification by Ti of the La2O3-CeO2-Al2O3 system leads to higher resistance towards the presence of SO2 most likely due to the prevailing formation of unstable surface sulfites instead of thermally stable sulfates. Based on kinetic model calculations, the reaction pathway over the Pd/La2O3-CeO2-TiO2-Al2O3 catalyst follows the Mars-van Krevelen mechanism. For evaluation of the possible practical application of the obtained material, a sample of Pd/La2O3-CeO2-TiO2-Al2O3, supported on rolled aluminum-containing stainless steel (Aluchrom VDM®), was prepared and tested. Methane oxidation in an industrial-scale monolithic reactor was simulated using a two-dimensional heterogeneous reactor model.
RESUMEN
The present paper reports on MnCoFeO4 spinels with peculiar composition and their catalytic behavior in the reactions of complete oxidation of hydrocarbons. The samples were synthesized by solution combustion method with sucrose and citric acid as fuels. All samples were characterized by powder X-ray diffraction, N2-physisorption, scanning electron microscopy, thermal analysis, X-ray photoelectron spectroscopy, and Mössbauer spectroscopy. The catalytic properties of the spinels with Mn:Co:Fe = 1:1:1 composition were studied in reactions of complete oxidation of methane, propane, butane, and propane in the presence of water as model pollutants. Both prepared catalysts are nanosized materials. The slight difference in the compositions, structure, and morphology is due to the type of fuel used in the synthesis reaction. The spinel, prepared with sucrose, shows a higher specific surface area, pore volume, higher amount of small particles fraction, higher thermal stability, and as a result, more exposed active sites on the sample surface that lead to higher catalytic activity in the studied oxidation reactions. After the catalytic tests, both samples do not undergo any substantial phase and morphological changes; thus, they could be applied in low-temperature hydrocarbon oxidation reactions.