RESUMEN
Bi0.5Pb0.5FeO3 with 1:1 mixture of Bi and Pb having charge degrees of freedom at the A-site of perovskite oxide ABO3 is obtained for the first time by high-pressure synthesis. Comprehensive synchrotron X-ray powder diffraction, optical second harmonic generation, Mössbauer spectroscopy, and hard X-ray photoemission spectroscopy measurements revealed that Bi0.5Pb0.5FeO3 is a canted antiferromagnetic insulator crystalizing in a nonpolar tetragonal I4/mcm structure with â2a × â2a × 2a unit cell and has unusually Pb charge disproportionated Bi3+0.5Pb2+0.25Pb4+0.25Fe3+O3 charge distribution. The valence of transition metal M in Bi0.5Pb0.5MO3 changes from 3.5+ to 3+ and finally to 2+ from Mn to Fe and to Ni, from left to right in the periodic table as the 3d-level becomes deeper. The valences of Bi and Pb increase to compensate for the decrease in the M's valence, and Pb changes from 6s2 (2+) to 6s0 (4+) before Bi changes.
RESUMEN
PbMO3 (M = 3d transition metals) family shows systematic variations in charge distribution and intriguing physical properties due to its delicate energy balance between Pb 6s and transition metal 3d orbitals. However, the detailed structure and physical properties of PbFeO3 remain unclear. Herein, we reveal that PbFeO3 crystallizes into an unusual 2ap × 6ap × 2ap orthorhombic perovskite super unit cell with space group Cmcm. The distinctive crystal construction and valence distribution of Pb2+0.5Pb4+0.5FeO3 lead to a long range charge ordering of the -A-B-B- type of the layers with two different oxidation states of Pb (Pb2+ and Pb4+) in them. A weak ferromagnetic transition with canted antiferromagnetic spins along the a-axis is found to occur at 600 K. In addition, decreasing the temperature causes a spin reorientation transition towards a collinear antiferromagnetic structure with spin moments along the b-axis near 418 K. Our theoretical investigations reveal that the peculiar charge ordering of Pb generates two Fe3+ magnetic sublattices with competing anisotropic energies, giving rise to the spin reorientation at such a high critical temperature.
RESUMEN
Bi and Pb ions with charge degree of freedom depending on 6s2 and 6s0 electronic configurations were combined with the Mn ion in a perovskite oxide. Comprehensive theoretical and experimental investigations revealed the Bi3+0.5Pb2+0.5Mn3+0.5Mn4+0.5O3 charge ordered state with CE-type spin and dz2 orbital orderings as observed in La0.5Ca0.5MnO3, Nd0.5Sr0.5MnO3, and Bi0.5Sr0.5MnO3. The charge and orbital orderings were preserved above 500 K owing to the stereochemical activity of Bi3+ and Pb2+ ions which stabilized the structural distortion.
RESUMEN
The pyrochlore-type Ca2Bi2O7 and Sr2Bi2O7 have been synthesized from a low-temperature hydrothermal route using NaBiO3·nH2O as a starting material. The crystal structures of these compounds were refined using synchrotron powder X-ray diffraction data. The cell parameters were found to be a = 10.75021 (5) Å and 10.94132 (6) Å for Ca2Bi2O7 and Sr2Bi2O7, respectively. Density functional theory calculations showed the metallic band structure, but the negligible mixing of O2 2p bands with the A-site alkaline-earth-metal states and weak overlap with the conduction bands result in the semiconducting behavior.