RESUMEN
An efficient carbon-polyaniline (PANI)-coated method was applied for perovskite-type oxide LaFeO3 to enhance its high-temperature electrochemical performance. Transmission electron microscopy (TEM) results reveal that LaFeO3 particles are evenly coated with carbon and PANI hybrid layers after carbon-PANI treatment. The carbon layers prevent the nanosized LaFeO3 particles from aggregation and allow the electrolyte to penetrate in every direction inside the particles. The PANI layers also enhance the electrocatalytic activity, facilitating hydrogen protons transferring from the electrolyte to the electrode interface. The cooperation of carbon and PANI hybrid layers results in a significant enhancement of the electrochemical performance at high temperatures. At an elevated temperature (60 °C), the maximum discharge capacity of the LaFeO3 electrodes remarkably increases from 231 mA h g(-1) to 402 mA h g(-1) and the high rate dischargeability at a discharge current density of 1500 mA g(-1) (HRD1500) increases from 22.7% to 44.3%. Moreover, the hybrid layers mitigate the corrosion of LaFeO3 electrodes by reducing the loss of active materials in the alkaline electrolyte, leading to increase in the capacity retention rate from 67.1% to 77.6% after 100 cycles (S100).