Self-Supporting Flexible Paper-Based Electrode Reinforced by Gradient Network Structure.

At present, the self-supporting paper-based electrode has some problems, such as low mechanical strength and insufficient flexibility, which restrict its application in flexible electronics. In this paper, FWF is used as the skeleton fiber, and the contact area and the number of hydrogen bonds of the fiber are increased by grinding the fiber and adding nanofibers to bridge it, and a level three gradient enhanced skeleton support network structure is constructed, which effectively improves the mechanical strength and foldability of the paper-based electrodes. The tensile strength of FWF15-BNF5 paper-based electrode is 7.4 MPa, the elongation at break is increased to 3.7%, the electrode thickness is as low as 66 µm, the electrical conductivities is 5.6 S cm-1, and the contact angle to electrolyte as low as 45°, which has excellent electrolyte wettability, flexibility, and foldability. After three-layer superimposed rolling, the discharge areal capacity reached 3.3 mAh cm-2 and 2.9 mAh cm-2 at the rate of 0.1 C and 1.5 C, respectively, which was superior to the commercial LFP electrode, it had good cycle stability, and the areal capacity was 3.0 mAh cm-2 and 2.8 mAh cm-2 after 100 cycles at the rate of 0.3 C and 1.5 C.

High-Density Oxygen Doping of Conductive Metal Sulfides for Better Polysulfide Trapping and Li2 S-S8 Redox Kinetics in High Areal Capacity Lithium-Sulfur Batteries.

Exploring new materials and methods to achieve high utilization of sulfur with lean electrolyte is still a common concern in lithium-sulfur batteries. Here, high-density oxygen doping chemistry is introduced for making highly conducting, chemically stable sulfides with a much higher affinity to lithium polysulfides. It is found that doping large amounts of oxygen into NiCo2 S4 is feasible and can make it outperform the pristine oxides and natively oxidized sulfides. Taking the advantages of high conductivity, chemical stability, the introduced large Li-O interactions, and activated Co (Ni) facets for catalyzing Sn 2- , the NiCo2 (O-S)4 is able to accelerate the Li2 S-S8 redox kinetics. Specifically, lithium-sulfur batteries using free-standing NiCo2 (O-S)4 paper and interlayer exhibit the highest capacity of 8.68 mAh cm-2 at 1.0 mA cm-2 even with a sulfur loading of 8.75 mg cm-2 and lean electrolyte of 3.8 µL g-1 . The high-density oxygen doping chemistry can be also applied to other metal compounds, suggesting a potential way for developing more powerful catalysts towards high performance of Li-S batteries.