RESUMEN
Microstructural evolution and dynamic recrystallization (DRX) behaviors of a Ni-Cr-Mo alloy were researched utilizing hot compressive experiments. The changed features of dislocation, subgrain and grain structure correlating to forming parameters were examined by transmission electron microscope (TEM) and electron backscatter diffraction (EBSD). Results illustrate that the consumption of dislocation and the coarsening of substructure/DRX grain are prominently enhanced with an increased forming temperature. However, the annihilation/interaction of dislocation and the expansion of subgrain/DRX grain boundary can be limited at a larger strain rate. Meanwhile, considering the discrepancy in DRX variation rates concerning the strain rate's ranges, an improved DRX kinetic model was developed. Compared to the classical DRX kinetic model, the good consistency between the forecasted and tested results demonstrates that the established improved DRX kinetic model can precisely characterize the DRX features of the Ni-Cr-Mo alloy over a wide strain rate range. Additionally, the EBSD's quantitative statistical results proved that the variation of DRX grain size can be supremely defined as the power formulation of the forming temperature and strain rate.
RESUMEN
The microstructural variation and high-temperature flow features of a Ti-55511 alloy in the ß region are studied by utilizing double-stage compression with a stepped strain rate. The results demonstrate that the stresses in the latter stage of hot compression markedly reduce as the strain at the previous stage or the strain rate at the previous/latter stage drops. Moreover, the annihilation/interaction of substructures is promoted, and the distinct refinement of the dynamic recrystallization (DRX) in the ß grain can be found. However, the coarsening of the ß grain and the consumption of dislocation substructures are accelerated at high temperatures. Furthermore, the principal DRX nucleation mechanism of the Ti-55511 alloy during double-stage compression with a stepped strain rate in the ß region is discontinuous DRX. Additionally, by using the microstructural variation characteristics related to the forming parameters, a physical mechanism equation is modeled to forecast the forming features, the DRX fraction, and the size of the ß grain in the investigated alloy. The forecasted results are in accordance with the tested results, indicating that the established model can accurately forecast the microstructure variation and flow features of the studied alloy.
RESUMEN
This study takes large size samples after hot-upsetting as research objects and aims to investigate the optimization double-stage annealing parameters for improving the mechanical properties of hot-upsetting samples. The double-stage annealing treatments and uniaxial tensile tests for hot-upsetting GH4169 superalloy were finished firstly. Then, the fracture mode was also studied. The results show that the strength of hot-upsetting GH4169 superalloy can be improved by the double-stage annealing treatment, but the effect of annealing parameters on the elongation of GH4169 alloy at high temperature and room temperature is not significant. The fracture mode of annealed samples at high-temperature and room-temperature tensile tests is a mixture of shear fracture and quasi-cleavage fracture while that of hot-upsetting sample is a shear fracture. The macroscopic expressions for the two fracture modes belong to ductile fracture. Moreover, it is also found that the improvement of strength by the double-stage annealing treatment is greater than the single-stage annealing treatment. This is because the homogeneity of grains plays an important role in the improvement of strength for GH4169 superalloy when the average grain size is similar. Based on a comprehensive consideration, the optimal annealing route is determined as 900 °C × 9-12 h(water cooling) + 980 °C × 60 min(water cooling).
RESUMEN
The hot deformation characteristics of a GH4169 superalloy are investigated at the temperature and strain rate ranges of 1193-1313 K and 0.01-1 s-1, respectively, through Gleeble-3500 simulator. The hot deformed microstructures are analyzed by optical microscopy (OM), transmission electron microscopy (TEM), and electron backscattered diffraction (EBSD) technology. The effects of deformation parameters on the features of flow curves and annealing twins are discussed in detail. It is found that the shapes of flow curves are greatly affected by the deformation temperature. Broad peaks appear at low deformation temperatures or high strain rates. In addition, the evolution of annealing twins is significantly sensitive to the deformation degree, temperature, and strain rate. The fraction of annealing twins first decreases and then rises with the added deformation degree. This is because the initial annealing twin characters disappear at the relatively small strains, while the annealing twins rapidly generate with the growth of dynamic recrystallized grains during the subsequent hot deformation. The fraction of annealing twins is relatively high when the deformation temperature is high or the strain rate is low. In addition, the important role of annealing twins on dynamic recrystallization (DRX) behaviors are elucidated. The obvious bulging at initial twin boundaries, and the coherency of annealing twin boundaries with dynamic recrystallized grain boundaries, indicates that annealing twins can motivate the DRX nucleation during the hot deformation.