Here, we combined Cd and In codoping with a simple hydrothermal synthesis method to prepare SnSe powders composed of nanorod-like flowers. After spark plasma sintering, its internal grains inherited well the morphological features of the precursor, and the multiscale microstructure included nanorod-shaped grains, high-density dislocations, and stacking faults, as well as abundant nanoprecipitates, resulting in an ultralow thermal conductivity of 0.15 W m-1 K-1 for the synthesized material. At the same time, Cd and In synergistically regulated the electrical conductivity and Seebeck coefficient of SnSe, leading to an enhanced power factor. Among them, Sn0.94Cd0.03In0.03Se achieved a peak ZT of 1.50 parallel to the pressing direction, representing an 87.5% improvement compared with pure SnSe. Notably, the material possesses isotropic ZT values parallel and perpendicular to the pressing direction, overcoming the characteristic anisotropy in thermal performance observed in previous polycrystalline SnSe-based materials. Our results provide a new strategy for optimizing the performance of thermoelectric materials through structural engineering.
RESUMEN
Here, a high peak ZT of ≈2.0 is reported in solution-processed polycrystalline Ge and Cd codoped SnSe. Microstructural characterization reveals that CdSe quantum dots are successfully introduced by solution process method. Ultraviolet photoelectron spectroscopy evinces that CdSe quantum dots enhance the density of states in the electronic structure of SnSe, which leads to a large Seebeck coefficient. It is found that Ge and Cd codoping simultaneously optimizes carrier concentration and improves electrical conductivity. The enhanced Seebeck coefficient and optimization of carrier concentration lead to marked increase in power factor. CdSe quantum dots combined with strong lattice strain give rise to strong phonon scattering, leading to an ultralow lattice thermal conductivity. Consequently, high thermoelectric performance is realized in solution-processed polycrystalline SnSe by designing quantum dot structures and introducing lattice strain. This work provides a new route for designing prospective thermoelectric materials by microstructural manipulation in solution chemistry.