This study aimed to synthesize a novel elastomeric ligature with dimethylaminohexadecyl methacrylate (DMAHDM) grafted, providing a new strategy for improving the issue of enamel demineralization during fixed orthodontics. DMAHDM was incorporated into elastomeric ligatures at different mass fractions using ultraviolet photochemical grafting. The antibacterial properties were evaluated and the optimal DMAHDM amount was determined based on cytotoxicity assays. Moreover, tests were conducted to evaluate the in vivo changes in the mechanical properties of the elastomeric ligatures. To assess the actual in vivo effectiveness in preventing enamel demineralization, a rat demineralization model was established, with analyses focusing on changes in surface microstructure, elemental composition, and nanomechanical properties. Elastomeric ligatures with 2% DMAHDM showed excellent biocompatibility and the best antibacterial properties, reducing lactic acid production by 65.3% and biofilm bacteria by 50.0% within 24 h, without significant mechanical property differences from the control group (p > 0.05). Most importantly, they effectively prevented enamel demineralization in vivo, enhancing elastic modulus by 73.2% and hardness by 204.8%. Elastomeric ligatures incorporating DMAHDM have shown great potential for application in preventing enamel demineralization, providing a new strategy to solve this issue during fixed orthodontics.
Asunto(s)
Esmalte Dental , Elastómeros , Desmineralización Dental , Desmineralización Dental/prevención & control , Animales , Elastómeros/química , Ratas , Esmalte Dental/efectos de los fármacos , Antibacterianos/farmacología , Antibacterianos/química , Metacrilatos/química , Metacrilatos/farmacología , Aparatos Ortodóncicos , Biopelículas/efectos de los fármacos , MasculinoRESUMEN
Bone defects caused by tumors, osteoarthritis, and osteoporosis attract great attention. Because of outstanding biocompatibility, osteogenesis promotion, and less secondary infection incidence ratio, stimuli-responsive biomaterials are increasingly used to manage this issue. These biomaterials respond to certain stimuli, changing their mechanical properties, shape, or drug release rate accordingly. Thereafter, the activated materials exert instructive or triggering effects on cells and tissues, match the properties of the original bone tissues, establish tight connection with ambient hard tissue, and provide suitable mechanical strength. In this review, basic definitions of different categories of stimuli-responsive biomaterials are presented. Moreover, possible mechanisms, advanced studies, and pros and cons of each classification are discussed and analyzed. This review aims to provide an outlook on the future developments in stimuli-responsive biomaterials.
RESUMEN
OBJECTIVES: To synthesize a novel antibacterial orthodontic elastomeric ligature incorporating dimethylaminohexadecyl methacrylate (DMAHDM) for the first time to prevent enamel demineralization during orthodontic therapy. METHODS: Various mass fractions of DMAHDM (ranging from 0 % to 20 %) were grafted onto commercial elastomeric ligatures using an ultraviolet photochemical grafting method and were characterized. The optimal DMAHDM concentration was determined based on biocompatibility and mechanical properties, and the antibacterial efficacy was evaluated in a whole-plaque biofilm model. TaqMan real-time polymerase chain reaction and fluorescence in situ hybridization were used to assess the microbial regulatory ability of the multispecies biofilms. Furthermore, an in vitro tooth demineralization model was established to explore its preventive effects on enamel demineralization. Statistical analysis involved a one-way analysis of variance and LSD post hoc tests at a significance level of 0.05. RESULTS: The elastomeric ligature containing 2 % mass fraction of DMAHDM exhibited excellent mechanical properties, favorable biocompatibility, and the most effective antibacterial ability against microorganisms, which decreased by almost two logarithms (P < 0.05). It significantly reduced the proportion of Streptococcus mutans in the multispecies plaque biofilm by 25 % at 72 h, leading to an enhanced biofilm microenvironment. Moreover, the novel elastomeric ligature demonstrated an obvious preventive effect on enamel demineralization, with an elastic modulus 30 % higher and hardness 62 % higher than those of the control group within 3 months (P < 0.05). SIGNIFICANCE: The integration of DMAHDM with an elastomeric ligature holds significant promise for regulating biofilms and preventing enamel demineralization in orthodontic applications.
RESUMEN
OBJECTIVE: Streptococcus mutans (S. mutans) is a major contributor to dental caries, with its ability to synthesize extracellular polysaccharides (EPS) and biofilms. The gcrR gene is a regulator of EPS synthesis and biofilm formation. The objectives of this study were to investigate a novel strategy of combining gcrR gene over-expression with dimethylaminohexadecyl methacrylate (DMAHDM), and to determine their in vivo efficacy in reducing caries in rats for the first time. METHODS: Two types of S. mutans were tested: Parent S. mutans; and gcrR gene over-expressed S. mutans (gcrR OE S. mutans). Bacterial minimum inhibitory concentration (MIC) and minimal bactericidal concentration (MBC) were measured with DMAHDM and chlorhexidine (CHX). Biofilm biomass, polysaccharide, lactic acid production, live/dead staining, colony-forming units (CFUs), and metabolic activity (MTT) were evaluated. A Sprague-Dawley rat model was used with parent S. mutans and gcrR OE S. mutans colonization to determine caries-inhibition in vivo. RESULTS: Drug-susceptibility of gcrR OE S. mutans to DMAHDM or CHX was 2-fold higher than that of parent S. mutans. DMAHDM reduced biofilm CFU by 3-4 logs. Importantly, the combined gcrR OE S. mutans+ DMAHDM dual strategy reduced biofilm CFU by 5 logs. In the rat model, the parent S. mutans group had a higher cariogenicity in dentinal (Dm) and extensive dentinal (Dx) regions. The DMAHDM + gcrR OE group reduced the Dm and Dx caries to only 20 % and 0 %, those of parent S. mutans + PBS control group (p < 0.05). The total caries severity of gcrR OE + DMAHDM group was decreased to 51 % that of parent S. mutans control (p < 0.05). SIGNIFICANCE: The strategy of combining S. mutans gcrR over-expression with antibacterial monomer reducing biofilm acids by 97 %, and reduced in vivo total caries in rats by 48 %. The gcrR over-expression + DMAHDM strategy is promising for a wide range of dental applications to inhibit caries and protect tooth structures.
RESUMEN
Root caries caused by cariogenic bacteria are a burden on a large number of individuals worldwide, especially the elderly. Applying a protective coating to exposed root surfaces has the potential to inhibit the development of caries, thus preserving natural teeth. This study aimed to develop a novel antibacterial coating to combat root caries and evaluate its effectiveness using the antibacterial monomer dimethylaminohexadecyl methacrylate (DMAHDM). DMAHDM was synthesized and incorporated into a resin consisting of 55.8% urethane dimethacrylate (UDMA) and 44.2% TEG-DVBE (UV) at a 10% mass fraction of glass filler. Multiple concentrations of DMAHDM were tested for their impact on the resin's mechanical and physical properties. S. mutans biofilms grown on resin disks were analyzed for antibacterial efficacy. Cytotoxicity was assessed against human gingival fibroblasts (HGFs). The results showed an 8-log reduction in colony-forming units (CFUs) against S. mutans biofilm (mean ± sd; n = 6) (p < 0.05) when 5% DMAHDM was incorporated into the UV resin. There was a 90% reduction in metabolic activity and lactic acid production. A low level of cytotoxicity against HGF was observed without compromising the physical and mechanical properties of the resin. This coating material demonstrated promising physical properties, potent antibacterial effects, and low toxicity, suggesting its potential to protect exposed roots from caries in various dental procedures and among elderly individuals with gingival recession.
RESUMEN
Conventional resin-based sealants release minimal fluoride ions (F) and lack antibacterial activity. The objectives of this study were to: (1) develop a novel bioactive sealant containing calcium fluoride nanoparticles (nCaF2) and antibacterial dimethylaminohexadecyl methacrylate (DMAHDM), and (2) investigate mechanical performance, F recharge and re-release, microleakage, sealing ability and cytotoxicity. Helioseal F served as commercial control. The initial F release from sealant containing 20% nCaF2 was 25-fold that of Helioseal F. After ion exhaustion and recharge, the F re-release from bioactive sealant did not decrease with increasing number of recharge and re-release cycles. Elastic modulus of new bioactive sealant was 44% higher than Helioseal F. The new sealant had excellent sealing, minimal microleakage, and good cytocompatibility. Hence, the nanostructured sealant had substantial and sustained F release and antibacterial activity, good sealing ability and biocompatibility. The novel bioactive nCaF2 sealant is promising to provide long-term F ions for caries prevention.
Asunto(s)
Antibacterianos , Fluoruro de Calcio , Filtración Dental , Ensayo de Materiales , Metacrilatos , Nanopartículas , Selladores de Fosas y Fisuras , Selladores de Fosas y Fisuras/química , Antibacterianos/farmacología , Antibacterianos/química , Fluoruro de Calcio/química , Metacrilatos/química , Nanopartículas/química , Fluoruros/química , Fluoruros/farmacología , Módulo de Elasticidad , Animales , Ratones , Materiales Biocompatibles/química , Materiales Biocompatibles/farmacología , Propiedades de Superficie , Resinas CompuestasRESUMEN
Osteoporosis is a metabolic disease characterized by bone density and trabecular bone loss. Bone loss may affect dental implant osseointegration in patients with osteoporosis. To promote implant osseointegration in osteoporotic patients, we further used a nonthermal atmospheric plasma (NTAP) treatment device previously developed by our research group. After the titanium implant (Ti) is placed into the device, the working gas flow and the electrode switches are turned on, and the treatment is completed in 30 s. Previous studies showed that this NTAP device can remove carbon contamination from the implant surface, increase the hydroxyl groups, and improve its wettability to promote osseointegration in normal conditions. In this study, we demonstrated the tremendous osteogenic enhancement effect of NTAP-Ti in osteoporotic conditions in rats for the first time. Compared to Ti, the proliferative potential of osteoporotic bone marrow mesenchymal stem cells on NTAP-Ti increased by 180% at 1 day (P = 0.004), while their osteogenic differentiation increased by 149% at 14 days (P < 0.001). In addition, the results indicated that NTAP-Ti significantly improved osseointegration in osteoporotic rats in vivo. Compared to the Ti, the bone volume fraction (BV/TV) and trabecular number (Tb.N) values of NTAP-Ti in osteoporotic rats, respectively, increased by 18% (P < 0.001) and 25% (P = 0.007) at 6 weeks and the trabecular separation (Tb.Sp) value decreased by 26% (P = 0.02) at 6 weeks. In conclusion, this study proved a novel NTAP irradiation titanium implant that can significantly promote osseointegration in osteoporotic conditions.
Asunto(s)
Células Madre Mesenquimatosas , Oseointegración , Osteogénesis , Osteoporosis , Gases em Plasma , Ratas Sprague-Dawley , Titanio , Titanio/farmacología , Animales , Osteogénesis/efectos de los fármacos , Osteoporosis/patología , Osteoporosis/terapia , Osteoporosis/tratamiento farmacológico , Gases em Plasma/farmacología , Gases em Plasma/uso terapéutico , Oseointegración/efectos de los fármacos , Femenino , Ratas , Células Madre Mesenquimatosas/efectos de los fármacos , Diferenciación Celular/efectos de los fármacos , Proliferación Celular/efectos de los fármacos , Prótesis e ImplantesRESUMEN
Background: A major drawback of resin composites is their tendency to accumulate microbial biofilms that can lead to secondary caries. The objective of this study was to compare the mechanical properties and the degree of conversion of commercial resin-based composite materials containing a contact-killing antibacterial agent, dimethylaminohexadecyl methacrylate (DMAHDM), at different concentrations, with a fluoride-releasing composite material. Materials and methods: Four groups were tested: Tetric N Ceram composite material (G1), Tetric Evo Ceram (G2), and Tetric N Ceram with the addition of contact-killing antibacterial agent DMAHDM at concentrations of 3% (G3) and 5% (G4). The mechanical properties, including flexural strength, elastic modulus, and Vickers microhardness and the degree of conversion were investigated. Results: Adding 3 % and 5 % DMAHDM resulted in flexural strength values that were comparable to Tetric Evo Ceram. Tetric N Ceram was comparable to the group containing 3 % DMAHDM (p > 0.05). However, it was significantly greater when compared to Tetric Evo Ceram (93.3 ± 9.4) and 5 % DMAHDM (p < 0.05). Both the elastic modulus and Vickers microhardness values of Tetric N Ceram were significantly higher than those of the other groups (p < 0.05). Furthermore, the elastic modulus of Tetric Evo Ceram showed similar results to groups with 3 % and 5 % DMAHDM. Nevertheless, the Vickers microhardness value is significantly higher when compared to 5 % DMAHDM (0.394 ± 0.021) (p < 0.05) while it was comparable to that of 3 % DMAHDM (0.484 ± 0.016) (p > 0.05). There was no statistically significant difference in the degree of conversion between the groups (p > 0.05). Conclusion: Adding 3% DMAHDM to Tetric N Ceram resulted in flexural strength values that were similar to those of Tetric N Ceram and Tetric Evo Ceram. DMAHDM did not affect the degree of conversion of Tetric N Ceram composite.
RESUMEN
The repair and regeneration of critical-sized bone defects remain an urgent challenge. Bone tissue engineering represents an exciting solution for regeneration of large bone defects. Recently, the importance of innervation in tissue-engineered bone regeneration has been increasingly recognized. The cross talk between nerve and bone provides important clues for bone repair and regeneration. Furthermore, the promotion of angiogenesis by innervation can accelerate new bone formation. However, the mechanisms involved in the promotion of vascular and bone regeneration by the nervous system have not yet been established. In addition, simultaneous neurogenesis and vascularization in bone tissue engineering have not been fully investigated. This article represents the first review on the effects of innervation in enhancing angiogenesis and osteogenesis in bone and dental tissue engineering. Cutting-edge research on the effects of innervation through biomaterials on bone and dental tissue repairs is reviewed. The effects of various nerve-related factors and cells on bone regeneration are discussed. Finally, novel clinical applications of innervation for bone, dental, and craniofacial tissue regeneration are also examined.
Asunto(s)
Huesos , Neovascularización Fisiológica , Osteogénesis , Ingeniería de Tejidos , Ingeniería de Tejidos/métodos , Humanos , Animales , Huesos/irrigación sanguínea , Huesos/inervación , Regeneración Ósea/efectos de los fármacos , Diente/inervación , AngiogénesisRESUMEN
OBJECTIVE: The article reviewed novel orthodontic devices and materials with bioactive capacities in recent years and elaborated on their properties, aiming to provide guidance and reference for future scientific research and clinical applications. DATA, SOURCES AND STUDY SELECTION: Researches on remineralization, protein repellent, antimicrobial activity and multifunctional novel bioactive orthodontic devices and materials were included. The search of articles was carried out in Web of Science, PubMed, Medline and Scopus. CONCLUSIONS: The new generation of orthodontic devices and materials with bioactive capacities has broad application prospects. However, most of the current studies are limited to in vitro studies and cannot explore the true effects of various bioactive devices and materials applied in oral environments. More research, especially in vivo researches, is needed to assist in clinical application. CLINICAL SIGNIFICANCE: Enamel demineralization (ED) is a common complication in orthodontic treatments. Prolonged ED can lead to dental caries, impacting both the aesthetics and health of teeth. It is of great significance to develop antibacterial orthodontic devices and materials that can inhibit bacterial accumulation and prevent ED. However, materials with only preventive effect may fall short of addressing actual needs. Hence, the development of novel bioactive orthodontic materials with remineralizing abilities is imperative. The article reviewed the recent advancements in bioactive orthodontic devices and materials, offering guidance and serving as a reference for future scientific research and clinical applications.
Asunto(s)
Caries Dental , Soportes Ortodóncicos , Desmineralización Dental , Humanos , Caries Dental/prevención & control , Estética Dental , Esmalte Dental , Desmineralización Dental/prevención & controlRESUMEN
OBJECTIVES: Dental caries is caused by acids from biofilms. pH-sensitive nanoparticle carriers could achieve improved targeted effectiveness. The objectives of this study were to develop novel mesoporous silica nanoparticles carrying nanosilver and chlorhexidine (nMS-nAg-Chx), and investigate the inhibition of biofilms as well as the modulation of biofilm to suppress acidogenic and promote benign species for the first time. METHODS: nMS-nAg was synthesized via a modified sol-gel method. Carboxylate group functionalized nMS-nAg (COOH-nMS-nAg) was prepared and Chx was added via electrostatic interaction. Minimal inhibitory concentration (MIC), inhibition zone, and growth curves were evaluated. Streptococcus mutans (S. mutans), Streptococcus gordonii (S. gordonii), and Streptococcus sanguinis (S. sanguinis) formed multispecies biofilms. Metabolic activity, biofilm lactic acid, exopolysaccharides (EPS), and TaqMan real-time polymerase chain reaction (RT-PCR) were tested. Biofilm structures and biomass were observed by scanning electron microscopy (SEM) and live/dead bacteria staining. RESULTS: nMS-nAg-Chx possessed pH-responsive properties, where Chx release increased at lower pH. nMS-nAg-Chx showed good biocompatibility. nMS-nAg-Chx exhibited a strong antibacterial function, reducing biofilm metabolic activity and lactic acid as compared to control (p < 0.05, n = 6). Moreso, biofilm biomass was dramatically suppressed in nMS-nAg-Chx groups. In control group, there was an increasing trend of S. mutans proportion in the multispecies biofilm, with S. mutans reaching 89.1% at 72 h. In sharp contrast, in nMS-nAg-Chx group of 25 µg/mL, the ratio of S. mutans dropped to 43.7% and the proportion of S. gordonii and S. sanguinis increased from 19.8% and 10.9 to 69.8% and 56.3%, correspondingly. CONCLUSION: pH-sensitive nMS-nAg-Chx had potent antibacterial effects and modulated biofilm toward a non-cariogenic tendency, decreasing the cariogenic species nearly halved and increasing the benign species approximately twofold. nMS-nAg-Chx is promising for applications in mouth rinse and endodontic irrigants, and as fillers in resins to prevent caries.
Asunto(s)
Caries Dental , Nanopartículas , Plata , Humanos , Clorhexidina/farmacología , Clorhexidina/química , Caries Dental/microbiología , Dióxido de Silicio/farmacología , Dióxido de Silicio/química , Antibacterianos/farmacología , Antibacterianos/química , Streptococcus mutans , Nanopartículas/química , Ácido Láctico/análisis , Biopelículas , Concentración de Iones de HidrógenoRESUMEN
OBJECTIVE: Implant-related infections from the adhesion and proliferation of dental plaque are a major challenge for dental implants. The objectives of this study were to: (1) develop novel antibacterial titanium (Ti) healing abutment; (2) investigate the inhibition of implant infection-related pathogenic bacteria and saliva-derived biofilm, and evaluate the biocompatibility of the new material for the first time. METHODS: Dimethylaminohexadecyl methacrylate (DMAHDM) and hydroxyapatite (HAP) were polymerized via polydopamine (PDA) on Ti. Staphylococcus aureus (S. aureus), Streptococcus sanguinis (S. sanguinis) and human saliva-derived biofilms were tested. After 4 weeks of DMAHDM release, the antibacterial efficacy of the DMAHDM remaining on Ti surface and the DMADHM in medium was tested. Biocompatibility was determined using human gingival fibroblasts (HGFs) and periodontal ligament stem cells (PDLSCs). RESULTS: The DMAHDM-loaded coating filled into the nano-voids in Ti surfaces. The modified Ti showed potent antibacterial activity, reducing the CFU of S. aureus, S. sanguinis and saliva-derived biofilms by 8, 7 and 4 log, respectively (P < 0.05). After 4 weeks of release, the modified Ti was still able to reduce S. aureus and S. sanguinis biofilm CFU by 1-3 log (P < 0.05). This provided strong antibacterial function for more than 4 weeks, which were the high-risk period for implant infections. The new material showed excellent biocompatibility when compared to control (P > 0.05). CONCLUSION: Novel DMAHDM-loaded Ti healing abutment had strong antibacterial effects, reducing biofilm CFUs by orders of magnitude, and lasting for over four weeks to cover the high-risk period for implant infections. The novel antibacterial Ti is promising to combat implant-related infections in dental, craniofacial and orthopedic applications.
Asunto(s)
Implantes Dentales , Metilaminas , Titanio , Humanos , Titanio/farmacología , Staphylococcus aureus , Antibacterianos/farmacología , Metacrilatos/farmacología , BiopelículasRESUMEN
Recurrent caries remain a persistent concern, often linked to microleakage and a lack of bioactivity in contemporary dental composites. Our study aims to address this issue by developing a low-shrinkage-stress nanocomposite with antibiofilm and remineralization capabilities, thus countering the progression of recurrent caries. In the present study, we formulated low-shrinkage-stress nanocomposites by combining triethylene glycol divinylbenzyl ether and urethane dimethacrylate, incorporating dimethylaminododecyl methacrylate (DMADDM), along with nanoparticles of calcium fluoride (nCaF2) and nanoparticles of amorphous calcium phosphate (NACP). The biofilm viability, biofilm metabolic activity, lactic acid production, and ion release were evaluated. The novel formulations containing 3% DMADDM exhibited a potent antibiofilm activity, exhibiting a 4-log reduction in the human salivary biofilm CFUs compared to controls (p < 0.001). Additionally, significant reductions were observed in biofilm biomass and lactic acid (p < 0.05). By integrating both 10% NACP and 10% nCaF2 into one formulation, efficient ion release was achieved, yielding concentrations of 3.02 ± 0.21 mmol/L for Ca, 0.5 ± 0.05 mmol/L for P, and 0.37 ± 0.01 mmol/L for F ions. The innovative mixture of DMADDM, NACP, and nCaF2 displayed strong antibiofilm effects on salivary biofilm while concomitantly releasing a significant amount of remineralizing ions. This nanocomposite is a promising dental material with antibiofilm and remineralization capacities, with the potential to reduce polymerization-related microleakage and recurrent caries.
RESUMEN
OBJECTIVES: Composites are commonly used for tooth restorations, but recurrent caries often lead to restoration failures due to polymerization shrinkage-stress-induced marginal leakage. The aims of this research were to: (1) develop novel low-shrinkage-stress (L.S.S.) nanocomposites containing dimethylaminododecyl methacrylate (DMADDM) with nanoparticles of calcium fluoride (nCaF2) or amorphous calcium phosphate (NACP) for remineralization; (2) investigate antibacterial and cytocompatibility properties. METHODS: Nanocomposites were made by mixing triethylene glycol divinylbenzyl ether with urethane dimethacrylate containing 3% DMADDM, 20% nCaF2, and 20% NACP. Flexural strength, elastic modulus, antibacterial properties against Streptococcus mutans biofilms, and cytotoxicity against human gingival fibroblasts and dental pulp stem cells were tested. RESULTS: Nanocomposites with DMADDM and nCaF2 or NACP had flexural strengths matching commercial composite control without bioactivity. The new nanocomposite provided potent antibacterial properties, reducing biofilm CFU by 6 logs, and reducing lactic acid synthesis and metabolic function of biofilms by 90%, compared to controls (p < 0.05). The new nanocomposites produced excellent cell viability matching commercial control (p > 0.05). CONCLUSIONS: Bioactive L.S.S. antibacterial nanocomposites with nCaF2 and NACP had excellent bioactivity without compromising mechanical and cytocompatible properties. The new nanocomposites are promising for a wide range of dental restorations by improving marginal integrity by reducing shrinkage stress, defending tooth structures, and minimizing cariogenic biofilms.
RESUMEN
Oral cavity is an essential reservoir for H. pylori. We aimed to investigate the antibacterial effects of dimethylaminododecyl methacrylate (DMADDM) against H. pylori. Modified giomers were prepared by introducing 0%, 1.25% and 2.5% DMADDM monomers. Broth microdilution assay, spot assay, Alamer Blue assay, PMA-qPCR, crystal violet staining, scanning electron microscopy observation and live/dead bacterial staining were performed to evaluate the antibacterial and antibiofilm effects of DMADDM and modified giomers in vitro. Urease assay, qPCR, hematoxylin-eosin staining and ELISA were performed to evaluate the inflammation levels and colonization of H. pylori in vivo. In vitro experiments indicated that the minimum inhibitory concentration and minimum bactericidal concentration of DMADDM were 6.25 µg/mL and 25 µg/mL, respectively. It inhibited H. pylori in a dose- and time-dependent manner, and significantly reduced the expression of cagA, vacA, flaA and ureB. DMADDM-modified giomers inhibited the formation of H. pylori biofilm and reduced live cells within it. In vivo experiments confirmed that the pretreatment with DMADDM-modified dental resin effectively reduced the gastric colonization of oral-derived H. pylori, suppressed systemic and local gastric inflammation. DMADDM monomers and DMADDM-modified giomers possessed excellent antibacterial and antibiofilm effects on H. pylori. Pretreatment with DMADDM-modified giomers significantly inhibited the gastric infection by H. pylori.
Asunto(s)
Helicobacter pylori , Humanos , Antibacterianos/farmacología , Inflamación , Materiales DentalesRESUMEN
OBJECTIVES: Injectable and self-setting calcium phosphate cement scaffold (CPC) capable of encapsulating and delivering stem cells and bioactive agents would be highly beneficial for dental and craniofacial repairs. The objectives of this study were to: (1) develop a novel injectable CPC scaffold encapsulating human periodontal ligament stem cells (hPDLSCs) and metformin (Met) for bone engineering; (2) test bone regeneration efficacy in vitro and in vivo. METHODS: hPDLSCs were encapsulated in degradable alginate fibers, which were then mixed into CPC paste. Five groups were tested: (1) CPC control; (2) CPC + hPDLSC-fibers + 0% Met (CPC + hPDLSCs + 0%Met); (3) CPC + hPDLSC-fibers + 0.1% Met (CPC + hPDLSCs + 0.1%Met); (4) CPC + hPDLSC-fibers + 0.2% Met (CPC + hPDLSCs + 0.2%Met); (5) CPC + hPDLSC-fibers + 0.4% Met (CPC + hPDLSCs + 0.4%Met). The injectability, mechanical properties, metformin release, and hPDLSC osteogenic differentiation and bone mineral were determined in vitro. A rat cranial defect model was used to evaluate new bone formation. RESULTS: The novel construct had good injectability and physical properties. Alginate fibers degraded in 7 days and released hPDLSCs, with 5-fold increase of proliferation (pï¼0.05). The ALP activity and mineral synthesis of hPDLSCs were increased by Met delivery (pï¼0.05). Among all groups, CPC+hPDLSCs+ 0.1%Met showed the greatest cell mineralization and osteogenesis, which were 1.5-10 folds those without Met (pï¼0.05). Compared to CPC control, CPC+hPDLSCs+ 0.1%Met enhanced bone regeneration in rats by 9 folds, and increased vascularization by 3 folds (pï¼0.05). CONCLUSIONS: The novel injectable construct with hPDLSC and Met encapsulation demonstrated excellent efficacy for bone regeneration and vascularization in vivo in an animal model. CPC+hPDLSCs+ 0.1%Met is highly promising for dental and craniofacial applications.
Asunto(s)
Metformina , Osteogénesis , Ratas , Humanos , Animales , Andamios del Tejido , Ligamento Periodontal , Metformina/farmacología , Regeneración Ósea , Células Madre , Diferenciación Celular , Fosfatos de Calcio/farmacología , Alginatos/farmacología , Células CultivadasRESUMEN
OBJECTIVES: Current dental resins exhibit polymerization shrinkage causing microleakage, which has the potential to cause recurrent caries. Our objectives were to create and characterize low-shrinkage-stress (LSS) composites with dimethylaminododecyl methacrylate (DMADDM) as an antibacterial agent to combat recurrent caries. METHODS: Triethylene glycol divinylbenzyl ether and urethane dimethacrylate were used to reduce shrinkage stress. DMADDM was incorporated at different mass fractions (0%, 1.5%, 3%, and 5%). Flexural strength, elastic modulus, degree of conversion, polymerization stress, and antimicrobial activity were assessed. RESULTS: The composite with 5% DMADDM demonstrated higher flexural strength than the commercial group (p < 0.05). The addition of DMADDM in BisGMA-TEGDMA resin and LSS resin achieved clinically acceptable degrees of conversion. However, LSS composites exhibited much lower polymerization shrinkage stress than BisGMA-TEGDMA composite groups (p < 0.05). The addition of 3% and 5% DMADDM showed a 6-log reduction in Streptococcus mutans (S. mutans) biofilm CFUs compared to commercial control (p < 0.001). Biofilm biomass and lactic acid were also substantially decreased via DMADDM (p < 0.05). CONCLUSIONS: The novel LSS dental composite containing 3% DMADDM demonstrated potent antibacterial action against S. mutans biofilms and much lower polymerization shrinkage-stress, while maintaining excellent mechanical characteristics. The new composite is promising for dental applications to prevent secondary caries and increase restoration longevity.
RESUMEN
OBJECTIVES: To review the literature on recurrent caries models used to evaluate restorative materials, compare reported methodology and parameters, and devise specific recommendations to be considered in future investigations. DATA: The following were extracted: study design, sample characteristics, source of teeth, name of restorations compared including controls, recurrent caries model type, type of demineralizing and remineralizing solutions, type of biofilm used, methods to detect recurrent caries. SOURCES: Literature searches were performed in OVID Medline, EMBASE, SCOPUS, and Cochrane Library. STUDY SELECTION: For a study to be included, it had to examine dental materials for tooth restoration purposes only with a valid control group and evaluate restorative dental materials regardless of the form of the teeth caries model used or nature of the tooth structure used. A total of 91 studies were included. Most of the studies presented were in vitro. Human teeth were the main source of specimens utilized. Around 88% of the studies used specimens without an artificial gap, and 44% used a chemical model. S. mutans was the main bacterial species used in microbial caries models. CONCLUSION: The findings of this review provided an insight into the performance of available dental materials assessed using different recurrent caries models, yet this review cannot be used as a guideline for material selection. Selecting the appropriate restorative material relies on several patient-related factors such as microbiota, occlusion, and diet that are not comprehensively taken into consideration in recurrent caries models and thus hinder reliable comparison. CLINICAL SIGNIFICANCE: Due to the heterogenicity of variables among studies on the performance of dental restorative materials, this scoping review aimed to provide insights for dental researchers concerning the available recurrent caries models, testing methods used, and aspects of comparison between these materials including their characteristics and limitations.
Asunto(s)
Resinas Compuestas , Caries Dental , Humanos , Restauración Dental Permanente/métodos , Susceptibilidad a Caries Dentarias , Diente PrimarioRESUMEN
OBJECTIVE: To provide the first review on cutting-edge research on the development of new bioactive restorations to inhibit secondary caries in enamel and dentin under biofilms. State-of-the-art bioactive and therapeutic materials design, structure-property relationships, performance and efficacies in oral biofilm models. DATA, SOURCES AND STUDY SELECTION: Researches on development and assessment new secondary caries inhibition restorations via in vitro and in vivo biofilm-based secondary caries models were included. The search of articles was carried out in Web of Science, PubMed, Medline and Scopus. CONCLUSIONS: Based on the found articles, novel bioactive materials are divided into different categories according to their remineralization and antibacterial biofunctions. In vitro and in vivo biofilm-based secondary caries models are effective way of evaluating the materials efficacies. However, new intelligent and pH-responsive materials were still urgent need. And the materials evaluation should be performed via more clinical relevant biofilm-based secondary caries models. CLINICAL SIGNIFICANCE: Secondary caries is a primary reason for dental restoration failures. Biofilms produce acids, causing demineralization and secondary caries. To inhibit dental caries and improve the health and quality of life for millions of people, it is necessary to summarize the present state of technologies and new advances in dental biomaterials for preventing secondary caries and protecting tooth structures against oral biofilm attacks. In addition, suggestions for future studies are provided.
Asunto(s)
Caries Dental , Humanos , Caries Dental/terapia , Susceptibilidad a Caries Dentarias , Calidad de Vida , Esmalte Dental , Dentina/química , BiopelículasRESUMEN
Objective: To explore the influence of resin modified glass ionomer cement (RMGIC) adhesives containing protein-repellent and quaternary ammonium salt agents on supragingival microbiome, enamel and gingival health around brackets. Materials and Methods: Ten patients (21.4 ± 3.5 years) about to receive fixed orthodontics were enrolled in this study. Unilateral upper teeth bonded with RMGIC incorporating 2-Methacryloyloxyethyl phosphorylcholine (MPC) and Dimethylaminohexadecyl methacrylate (DMAHDM) were regarded as experimental group (RMD), while contralateral upper teeth bonded with RMGIC were control group (RMGIC), using a split-mouth design. Supragingival plaque was collected from both groups before treatment (T0), and at 1 month (T1) and 3 months (T2) of treatment. High-throughput sequencing was performed targeting v3-v4 of 16S rRNA gene. Streptococcus mutans and Fusobacterium nucleatum quantification was done by qPCR analysis. Bracket failures, enamel decalcification index (EDI), DIAGNODent scores (Dd), plaque index (PI) and gingival index (GI) were monitored at indicated time points. Results: Within 3 months, alpha and beta diversity of supragingival plaque had no difference between RMGIC and RMD groups. From T0 to T2, the relative abundance of Streptococcus depleted in RMD but remained steady in RMGIC group. Streptococcus, Prevotella, and Fusobacterium became depleted in RMD, Haemophilus and Capnocytophaga became depleted in RMGIC group but Prevotella enriched. Quantification of Fusbacterium nucleatum and Streptococcus mutans showed significant difference between RMGIC and RMD groups at T2. Teeth bonded with RMD had significant lower plaque index (PI) and DIAGNODent (Dd) score at T2, compared with teeth bonded with RMGIC (p < 0.05). No difference in bracket failure rate was examined between both groups (p > 0.05). Conclusion: By incorporating MPC and DMAHDM into RMGIC, the material could affect the supragingival microbial composition, inhibit the progress of plaque accumulation as well as the key pathogens S. mutans and F. nucleatum in the early stage of orthodontic treatment.