Etch-and-rinse vs self-etch mode for dentin bonding effectiveness of universal adhesives.

In this study, dentin bond fatigue resistance and interfacial science characteristics of universal adhesives through etch-and-rinse and self-etch modes were investigated. Resin composite was bonded to human dentin with four universal adhesives, namely, Adhese Universal, All-Bond Universal, G-Premio Bond, and Scotchbond Universal Adhesive. The initial bond strengths, bond fatigue strengths, and interfacial science characteristics of the universal adhesives with dentin through etch-and-rinse and self-etch modes were determined. Bond fatigue resistance (initial bond strength and bond fatigue strength) of universal adhesives in etch-and-rinse mode showed no significant difference in contrast to that in self-etch mode and was material-dependent regardless of the etching mode. Although phosphoric acid conditioning of dentin did not have a strong impact on the bond fatigue resistance, surface free energy and parameters of dentin were significantly decreased by etching and by application of universal adhesives regardless of etching mode. Changes in γS and γSh for when universal adhesive was applied to etched and ground dentin were significantly different depending on the adhesive. The results suggest that bonding performance of universal adhesives was effective in both etching modes; however, bonding mechanisms may be different for each.

Effect of a coating material containing surface reaction-type pre-reacted glass-ionomer filler on prevention of primary enamel demineralization detected by optical coherence tomography.

We used optical coherence tomography to examine the effect of a coating material containing surface reaction-type pre-reacted glass-ionomer (S-PRG) filler on primary enamel demineralization in 18 extracted human primary teeth. The pulp was removed, and each tooth was ultrasonically cleaned with distilled water. Six teeth were treated with 0.1-M lactic acid buffer solution (De group). In the second group (n = 6), a thin film of coating material was applied before demineralization (PRG group). A third group (Control group; n = 6) was maintained in artificial saliva. Using optical coherence tomography, we measured peak signal intensity (dB) and width at 1/e2 (µm) at predetermined locations on the enamel surface and calculated integrated values. All data were analyzed with ANOVA and the Tukey-Kramer test (α = 0.05). Although changes in integrated values differed between groups, there was a small but significant increase in the Control group and a small but significant decrease in the De group. In the PRG group, integrated values were significantly higher at 7 days after the start of the experiment and significantly increased thereafter. Our findings indicate that a coating material containing S-PRG fillers may prevent primary enamel demineralization.

Effect of light irradiation and primer application on polymerization of selfadhesive resin cements monitored by ultrasonic velocity.

In this study, we investigated the effect of light irradiation and primer/adhesive application on the polymerization reaction and elastic modulus (E) of self-adhesive resin cement (SAC) through ultrasonic velocity (V) measurements. The V values of longitudinal and shear waves were determined based on the transit time through the specimens and specimen thicknesses, and were used to calculate the E values. Analysis of variance and Tukey tests revealed that V increased rapidly, reaching a plateau at 2,700-2,900 m/s, when the SACs were light-irradiated. However, the increasing rate of V was retarded for the non-irradiated SACs. In addition, when the primer/adhesive was applied, higher E values were obtained after 24 h. Finally, the polymerization behavior of the SACs was affected by light irradiation and primer application, and the use of prime/adhesive might improve mechanical properties. In clinical situations, use of primer/adhesive is recommended for getting proper adhesion.