RESUMEN
Current induced spin-orbit torques driven by the conventional spin Hall effect are widely used to manipulate the magnetization. This approach, however, is nondeterministic and inefficient for the switching of magnets with perpendicular magnetic anisotropy that are demanded by the high-density magnetic storage and memory devices. Here, we demonstrate that this limitation can be overcome by exploiting a magnetic spin Hall effect in noncollinear antiferromagnets, such as Mn3Sn. The magnetic group symmetry of Mn3Sn allows generation of the out-of-plane spin current carrying spin polarization collinear to its direction induced by an in-plane charge current. This spin current drives an out-of-plane anti-damping torque providing the deterministic switching of the perpendicular magnetization of an adjacent Ni/Co multilayer. Due to being odd with respect to time reversal symmetry, the observed magnetic spin Hall effect and the resulting spin-orbit torque can be reversed with reversal of the antiferromagnetic order. Contrary to the conventional spin-orbit torque devices, the demonstrated magnetization switching does not need an external magnetic field and requires much lower current density which is useful for low-power spintronics.
RESUMEN
Due to its inherent superior perpendicular magnetocrystalline anisotropy, the FePt in L10 phase enables magnetic storage and memory devices with ultrahigh capacity. However, reversing the FePt magnetic state, and therefore encoding information, has proven to be extremely difficult. Here, it is demonstrated that an electric current can exert a large spin torque on an L10 FePt magnet, ultimately leading to reversible magnetization switching. The spin torque monotonically increases with increasing FePt thickness, exhibiting a bulk characteristic. Meanwhile, the spin torque effective fields and switching efficiency increase as the FePt approaches higher chemical ordering with stronger spin-orbit coupling. The symmetry breaking that generates spin torque within L10 FePt is shown to arise from an inherent structural gradient along the film normal direction. By artificially reversing the structural gradient, an opposite spin torque effect in L10 FePt is demonstrated. At last, the role of the disorder gradient in generating a substantial torque in a single ferromagnet is supported by theoretical calculations. These results will push forward the frontier of material systems for generating spin torques and will have a transformative impact on magnetic storage and spin memory devices with simple architecture, ultrahigh density, and readily application.