RESUMEN
The use of the "Holy Grail" lithium metal anode is pivotal to achieve superior energy density. However, the practice of a lithium metal anode faces practical challenges due to the thermodynamic instability of lithium metal and dendrite growth. Herein, an artificial stabilization of lithium metal was carried out via the thermal pyrolysis of the NH4F salt, which generates HF(g) and NH3(g). An exposure of lithium metal to the generated gas induces a spontaneous reaction that forms multiple solid electrolyte interface (SEI) components, such as LiF, Li3N, Li2NH, LiNH2, and LiH, from a single salt. The artificially multilayered protection on lithium metal (AF-Li) sustains stable lithium stripping/plating. It suppresses the Li dendrite under the Li||Li symmetric cell. The half-cell Li||Cu and Li||MCMB systems depicted the attributions of the protective layer. We demonstrate that the desirable protective layer in AF-Li exhibited remarkable capacity retention (CR) results. LiFePO4 (LFP) showed a CR of 90.6% at 0.5 mA cm-2 after 280 cycles, and LiNi0.5Mn0.3Co0.2O2 (NCM523) showed 58.7% at 3 mA cm-2 after 410 cycles. Formulating the multilayered protection, with the simultaneous formation of multiple SEI components in a facile and cost-effective approach from NH4F as a single salt, made the system competent.
RESUMEN
Despite the unique advantages of single-atom catalysts, molecular dual-active sites facilitate the C-C coupling reaction for C2 products toward the CO2 reduction reaction (CO2 RR). The Ni/Cu proximal dual-active site catalyst (Ni/Cu-PASC) is developed, which is a harmonic catalyst with dual-active sites, by simply mixing commercial Ni-phthalocyanine (Ni-Pc) and Cu-phthalocyanine (Cu-Pc) molecules physically. According to scanning transmission electron microscopy (STEM) and transmission electron microscopy (TEM) energy dispersive spectroscopy (EDS) data, Ni and Cu atoms are separated, creating dual-active sites for the CO2 RR. The Ni/Cu-PASC generates ethanol with an FE of 55%. Conversely, Ni-Pc and Cu-Pc have only detected single-carbon products like CO and HCOO- . In situ X-ray absorption spectroscopy (XAS) indicates that CO generation is caused by the stable Ni active site's balanced electronic state. The CO production from Ni-Pc consistently increased the CO concentration over Cu sites attributed to subsequent reduction reaction through a C-C coupling on nearby Cu. The CO bound (HCOO- ) peak, which can be found on Cu-Pc, vanishes on Ni/Cu-PASC, as shown by in situ fourier transformation infrared (FTIR). The characteristic intermediate of *CHO instead of HCOO- proves to be the prerequisite for multi-carbon products by electrochemical CO2 RR. The work demonstrates that the harmonic dual-active sites in Ni/Cu-PASC can be readily available by the cascading proximal active Ni- and Cu-Pc sites.
RESUMEN
Sulfide-based solid-state lithium-ion batteries (SSLIB) have attracted a lot of interest globally in the past few years for their high safety and high energy density over the traditional lithium-ion batteries. However, sulfide electrolytes (SEs) are moisture-sensitive which pose significant challenges in the material preparation and cell manufacturing. To the best of our knowledge, there is no tool available to probe the types and the strength of the basic sites in sulfide electrolytes, which is crucial for understanding the moisture stability of sulfide electrolytes. Herein, we propose a new spectral probe with the Lewis base indicator BBr3 to probe the strength of Lewis basic sites on various sulfide electrolytes by 11B solid-state NMR spectroscopy (11B-NMR). The active sulfur sites and the corresponding strength of the sulfide electrolytes are successfully evaluated by the proposed Lewis base probe. The probed strength of the active sulfur sites of a sulfide electrolyte is consistent with the results of DFT (density functional theory) calculation and correlated with the H2S generation rate when the electrolyte was exposed in moisture atmosphere. This work paves a new way to investigate the basicity and moisture stability of the sulfide electrolytes.
RESUMEN
Copper/nickel nanocatalysts with a unique morphology were prepared by thermal reduction of a perovskite LaNix Cu1-x O3 precursor (x=1, 0.9, and 0.7). During thermal reduction, copper was first reduced and reacted with lanthanum to form metastable Cu5 La and Cu13 La. When the thermal reduction temperature was increased, the perovskite decomposed to Ni and La2 O3 , CuLa alloys disappeared, and Cu deposits on Ni nanoparticles were generated, thereby forming Cu/Ni nanocatalysts with hierarchical structures. Nanosized nickel, decorated with copper and supported on La2 O3 , could be produced at 520-550 °C. The steam reforming of ethanol was used as a model reaction to demonstrate the catalytic capability of the materials formed. The hierarchical structure of the Cu/Ni/La2 O3 catalysts confers synergetic effects that greatly favor the dehydrogenation of ethanol and which break the C-C bond to produce a higher yield of hydrogen at a low reaction temperature, whereas La2 O3 provides the required stability during the reaction. The reaction at 290 °C achieved almost 100 % conversion with a hydrogen yield reaching 2.21 molH2 mol(-1) EtOH thus indicating that this special structural feature can achieve high activity for the SRE at low temperatures. The proposed synthesis of nanocatalysts appears to be a good way to generate oxide-supported hierarchically structured nanoparticles that can also be applied to other reactions catalyzed by a heterogeneous metal oxide system.