RESUMEN
The purpose of this study was to evaluate a resin based pit and fissure sealant containing 45S5 bioactive glass (BAG) by examining its ion release, pH variation, and apatite-forming properties. To prepare the experimental materials, 45S5 BAG, used as a filler, was incorporated into the light curable resin matrix at concentrations of 0 (control), 12.5, 37.5, and 50.0 wt.%. Ion release, pH variation, and apatite formation (Raman spectrometer and scanning electron microscopy-energy-dispersive X-ray spectrometry measurements) were performed. While no ions were released from the control group, the experimental groups containing 45S5 BAG showed an increased release of Ca and P ions with increasing amounts of 45S5 BAG (p < 0.05). The pH of the experimental group remained high and was significantly different from the control group (p < 0.05). Unlike the control group, it was confirmed that the apatite peak was formed in the 50.0 wt.% BAG group for 90 days, and the apatite layer consisting of Ca and P was deposited on the surface. Thus, a resin based pit and fissure sealant containing 45S5 BAG is a promising material for preventing secondary caries by releasing ions and forming apatite.
RESUMEN
Acrylic resins are widely used as the main components in removable orthodontic appliances. However, poor oral hygiene and maintenance of orthodontic appliances provide a suitable environment for the growth of pathogenic microorganisms. In this study, strontium-modified phosphate-based glass (Sr-PBG) was added to orthodontic acrylic resin at 0% (control), 3.75%, 7.5%, and 15% by weight to evaluate the surface and physicochemical properties of the novel material and its in vitro antifungal effect against Candida albicans (C. albicans). Surface microhardness and contact angle did not vary between the control and 3.75% Sr-PBG groups (p > 0.05), and the flexural strength was lower in the experimental groups than in the control group (p < 0.05), but no difference was found with Sr-PBG content (p > 0.05). All experimental groups showed an antifungal effect at 24 and 48 h compared to that in the control group (p < 0.05). This study demonstrated that 3.75% Sr-PBG exhibits antifungal effects against C. albicans along with suitable physicochemical properties, which may help to minimize the risk of adverse effects associated with harmful microbial living on removable orthodontic appliances and promote the use of various materials.
Asunto(s)
Resinas Acrílicas , Antifúngicos , Candida albicans , Vidrio , Ensayo de Materiales , Fosfatos , Estroncio , Propiedades de Superficie , Candida albicans/efectos de los fármacos , Resinas Acrílicas/química , Estroncio/farmacología , Estroncio/química , Antifúngicos/farmacología , Vidrio/química , Fosfatos/farmacología , Polimerizacion , Dureza , Resistencia Flexional , Humanos , Técnicas In VitroRESUMEN
INTRODUCTION AND AIMS: The gaps at the margins of restorative composite resin can increase as the carious process occurs underneath the materials, causing further demineralization along the tooth cavity wall. The aim of this study was to evaluate the effects of restorative resin composite containing hydrated calcium silicate (hCS) filler on enamel protection against demineralization by simulating microleakage between the test material and teeth in a cariogenic environment. METHODS: The experimental resin composites were composed of 70 wt.% filler, which was mixed with a glass filler and hCS in a weight ratio of 70.0% glass (hCS 0), 17.5% hCS + 52.5% glass (hCS 17.5), 35.0% hCS + 35.0% glass (hCS 35.0), and 52.5% hCS + 17.5% glass (hCS 52.5). A light-cured experimental resin composite disk was positioned over a polished bovine enamel disk, separated by a 30-µm gap, and immersed in artificial saliva with pH 4.0 for 15, 30, and 60 days. After the immersion period, the enamel disk was separated from the resin composite disk and evaluated using a microhardness tester, atomic force microscopy, and polarized light microscopy. The opposing sides of the enamel and resin composite disks were observed using scanning electron microscopy/energy dispersive X-ray spectrometry. RESULTS: The enamel surface showed a significant increase in microhardness, decreased roughness, and remineralization layer as the proportion of hCS increased (P < .05). In the scanning electron microscopy image, the enamel surface with hCS 35.0 and 52.5 after all experimental immersion periods, showed a pattern similar to that of a sound tooth. CONCLUSIONS: The results demonstrated that increasing the hCS filler level of restorative resin composites significantly decreased enamel demineralization. CLINICAL RELEVANCE: Hydrated calcium silicate laced restorative resin composites may be a promising dental biomaterial for protecting teeth against demineralization and preventing secondary caries around restorations.
RESUMEN
Background: High-power short-duration (HPSD) ablation creates wide, shallow lesions using radiofrequency (RF) heating. It is uncertain if adjusting RF energy based on atrial wall thickness provides extra benefits. We studied the safety and effectiveness of tailored HPSD energy based on left atrial (LA) wall thickness (LAWT) for circumferential pulmonary vein isolation (CPVI) in patients with paroxysmal atrial fibrillation (PAF). Methods: We enrolled 212 patients (68.4% male, mean age: 59.5 ± 11.0 years) and randomly assigned them to two groups: LAWT-guided CPVI (WT, n = 108) and conventional CPVI (control, n = 104). Both groups used an open irrigated-tip deflectable catheter to apply 50 W for 10 s to the posterior LA, while controls used 60 W for 15 s on other LA regions. RF delivery time in WT was titrated (15 s at LAWT > 2.1 mm, 13 s at 1.4-2.1 mm, and 11 s at <1.4 mm) according to the computed tomogram-myocardial thickness color map. Results: After a mean follow-up of 13.4 ± 7.0 months, the WT and control groups showed no significant difference regarding clinical recurrence rate (13.9% vs. 5.8%, respectively; p = .061) and major complication rate (4.6% vs. 3.8%, respectively; p > .999). The total procedure time, cardioversion rate, and post-procedural AAD prescription rates did not significantly differ between the groups. Conclusions: The LAWT-guided energy titration strategy did not result in improved procedural safety and efficacy compared to the conventional 50-60 W-HPSD CPVI in patients with PAF.
RESUMEN
Various materials have been introduced for the three-dimensional (3D) printing of dentures. In this study, the color stability and surface and physicochemical properties of 3D-printed denture base resins with four types of nanofiller particles were evaluated. Al2O3, ZnO, CeZr, and SiO2 nanofillers were added to a 3D printable denture base-resin matrix and subjected to digital light processing. The specimens were immersed in Coke, coffee, black tea, or distilled water for 6 days. For the assessment of color differences, 6 samples were analyzed using a spectrophotometer. In a separate investigation, surface properties of 10 samples were examined, while a different set of 6 samples was used to analyze water sorption and solubility. All experimental groups exhibited higher color stability in Coke than the control group. However, the groups containing ZnO and CeZr had lower color stability in coffee and black tea than the control group. Moreover, they had agglomerated nanofillers and lower gloss than the control group. Compared with that of the control group, the contact angle of the CeZr group and microhardness of the ZnO group were not significantly different. Water sorption was higher in the Al2O3 group, whereas the solubility of the experimental and control groups was not statistically significant. The results demonstrated the significant effect of ZnO and CeZr nanofillers on the color stability of the dentures when exposed to discoloring beverages. These results will facilitate the development of fillers that enhance the resistance of 3D printed denture base resins to discoloration in the oral environment.
RESUMEN
BACKGROUND: White Portland cement is a calcium silicate material. It exhibits antibacterial properties and is biocompatible. In addition, calcium silicate-based materials are known to release calcium ions and form apatite. The purpose of this study was to develop a novel bioactive restorative resin composite with antibacterial and apatite forming properties to prevent tooth caries at the interface of teeth and restorative materials, by incorporation of hydrated calcium silicate (hCS) derived from white Portland cement. METHODS: To prepare the experimental composite resins, a 30 wt% light-curable resin matrix and 70 wt% filler, which was mixed with hCS and silanized glass powder were prepared in following concentrations: 0, 17.5, 35.0, and 52.5 wt% hCS filler. The depth of cure, flexural strength, water sorption, solubility, and antibacterial effect were tested. After immersion in artificial saliva solution for 15, 30, 60, and 90 days, ion concentration by ICP-MS and apatite formation using SEM-EDS, Raman spectroscopy and XRD from experimental specimens were analyzed. RESULTS: All experimental groups showed clinically acceptable depths of cure and flexural strength for the use as the restorative composite resin. Water sorption, solubility, released Ca and Si ions increased with the addition of hCS to the experimental composite resin. Experimental groups containing hCS showed greater antibacterial effects compared with the 0 wt% hCS filler group (p < 0.05). The 52.5 wt% hCS filler group produced precipitates mainly composed of Ca and P detected as hydroxyapatite after immersion in artificial saliva solution for 30, 60, and 90 days. CONCLUSIONS: This results show that composite resins containing hCS filler is effective in antibacterial effects. hCS has also apatite formation ability for reducing gap size of microleakage by accumulating hydroxyapatite precipitates at the restoration-tooth interface. Therefore, novel composite resin containing hCS is promising bioactive resin because of its clinically acceptable physiochemical properties, antibacterial properties, and self-sealing potential for prevention of microleakage for longer usage of restorations.
RESUMEN
This study aimed to evaluate the antibacterial, physicochemical, and mechanical properties of pit and fissure sealants containing different weight percentages of zinc oxide nanoparticles (ZnO NPs). The following amounts of ZnO NPs were added to a commercially available pit and fissure sealant (BeautiSealant, Shofu, Japan) to prepare the experimental materials: 0 wt.% (commercial control (CC)), 0.5 wt.% (ZnO 0.5), 1 wt.% (ZnO 1.0), 2 wt.% (ZnO 2.0), and 4 wt.% (ZnO 4.0). The antibacterial effect against S. mutans was confirmed by counting the colony-forming units (CFUs) and observing live/dead bacteria. In addition, ion release, depth of cure, water sorption and solubility, and flexural strength tests were conducted. When compared with the CC, the experimental groups containing ZnO NPs showed zinc ion emission and significantly different CFUs (p < 0.05) with fewer live bacteria. ZnO NP addition reduced the depth of cure and water solubility and increased water sorption in comparison with the CC (p < 0.05). However, all groups showed similar flexural strength (p > 0.05). The pit and fissure sealants containing ZnO NPs exhibited antibacterial activity against S. mutans with no negative effects on physicochemical and mechanical properties, and thus, these sealants can be ideal secondary caries prevention material.
RESUMEN
Poly (methyl methacrylate) (PMMA) is a commonly used denture material with poor antimicrobial effects. This study investigated the antimicrobial effects of PMMA-containing silver-phosphate glass. We fabricated a novel material comprising PMMA-containing silver-phosphate glass. Then, microhardness, flexural strength, and gloss unit were analyzed. Antimicrobial activity against Streptococcus mutans and Candida albicans was investigated. Colony-forming units were counted, and antimicrobial rates were measured. Biocompatibility tests were performed using a colorimetric MTT assay for evaluating cell metabolic activity. The microhardness, flexural strength, and gloss unit of the experimental groups (with silver-phosphate glass) were not significantly different from those of the control group (no silver-phosphate glass) (P > 0.05), which showed clinically valid values. With increasing proportions of silver-phosphate glass, the antimicrobial activity against the two microorganisms increased (P < 0.05). Furthermore, S. mutans showed more than 50% antimicrobial activity in 4%, 6%, and 8% experimental groups, C. albicans showed more than 50% antimicrobial activity in 6% and 8% groups, and a statistically significant difference in antimicrobial activity was observed compared to the control (P < 0.05). The cell viability of the experimental groups was not significantly different from that of the control group (P > 0.05). Both control and experimental groups showed approximately 100% cell viability. These results suggest that silver-phosphate glass is a promising antimicrobial material in dentistry.
RESUMEN
[This corrects the article DOI: 10.3389/fphys.2021.807545.].
RESUMEN
BACKGROUND AND OBJECTIVES: We investigated whether extra-pulmonary vein (PV) ablation targeting a high maximal slope of the action potential duration restitution curve (Smax) improves the rhythm outcome of persistent atrial fibrillation (PeAF) ablation. METHODS: In this open-label, multi-center, randomized, and controlled trial, 178 PeAF patients were randomized with 1:1 ratio to computational modeling-guided virtual Smax ablation (V-Smax) or empirical ablation (E-ABL) groups. Smax maps were generated by computational modeling based on atrial substrate maps acquired during clinical procedures in sinus rhythm. Smax maps were generated during the clinical PV isolation (PVI). The V-Smax group underwent an additional extra-PV ablation after PVI targeting the virtual high Smax sites. RESULTS: After a mean follow-up period of 12.3±5.2 months, the clinical recurrence rates (25.6% vs. 23.9% in the V-Smax and the E-ABL group, p=0.880) or recurrence appearing as atrial tachycardia (11.1% vs. 5.7%, p=0.169) did not differ between the 2 groups. The post-ablation cardioversion rate was higher in the V-Smax group than E-ABL group (14.4% vs. 5.7%, p=0.027). Among antiarrhythmic drug-free patients (n=129), the AF freedom rate was 78.7% in the V-Smax group and 80.9% in the E-ABL group (p=0.776). The total procedure time was longer in the V-Smax group (p=0.008), but no significant difference was found in the major complication rates (p=0.497) between the groups. CONCLUSIONS: Unlike a dominant frequency ablation, the computational modeling-guided V-Smax ablation did not improve the rhythm outcome of the PeAF ablation and had a longer procedure time. TRIAL REGISTRATION: ClinicalTrials.gov Identifier: NCT02558699.
RESUMEN
OBJECTIVES: The objective of this study was to evaluate an orthodontic adhesive containing hydrated calcium silicate (hCS) in terms of its bond strength with the enamel surface and its acid-neutralization and apatite-forming abilities. METHODS: The experimental orthodontic adhesives were composed of 30 wt.% resin matrix and 70 wt.% filler, which itself was a mixture of silanized glass filler and hCS in weight ratios of 100% glass filler (hCS 0), 17.5% hCS (hCS 17.5), 35% hCS (hCS 35.0), and 52.5% hCS (hCS 52.5). The degree of conversion (DC) and shear bond strength (SBS) of bovine enamel surfaces were tested. pH measurements were performed immediately upon submersion of the specimens in a lactic acid solution. The surface precipitates that formed on specimens immersed in phosphate-buffered saline (PBS) were analyzed by scanning electron microscopy with energy dispersive spectroscopy (SEM-EDS) and Raman spectroscopy after 15, 30, and 90 days. RESULTS: The experimental groups exhibited no significant differences in DC and had clinically acceptable SBS values. The hCS-containing groups showed increasing pH values as more hCS was added. hCS 52.5 produced Ca- and P-containing surface precipitates after PBS immersion, and hydroxyapatite deposition was detected after 15, 30, and 90 days. CONCLUSIONS: These results suggest that orthodontic adhesives containing hCS are effective for acid neutralization. Furthermore, hCS has an apatite-forming ability for enamel remineralization. CLINICAL SIGNIFICANCE: The novel orthodontic adhesive containing hCS exhibits a potential clinical benefit against demineralization and enhanced remineralization of the enamel surface around or beneath the orthodontic brackets.
Asunto(s)
Recubrimiento Dental Adhesivo , Soportes Ortodóncicos , Animales , Apatitas , Compuestos de Calcio , Bovinos , Recubrimiento Dental Adhesivo/métodos , Cementos Dentales/química , Ensayo de Materiales , Cementos de Resina/química , Resistencia al Corte , Silicatos , Propiedades de SuperficieRESUMEN
OBJECTIVES: This study aimed to evaluate the effects of 30% hydrogen peroxide (HP) solution containing various contents of 45S5 bioactive glass (BAG) on whitening efficacy and enamel surface properties after simulating the clinical bleaching procedure. MATERIALS AND METHODS: A total of 60 bovine enamel specimens discolored with black tea were divided into five groups treated with distilled water (DW), HP, 0.01 wt.% BAG + HP, 1.0 wt.% BAG + HP, and 20.0 wt.% BAG + HP (n = 12). The pH change was observed for 20 min immediately after mixing the experimental solutions, which were applied for 20 min/week, at 37 °C over 21 days. Color, gloss, roughness, microhardness, and micromorphology measurements were conducted before and after bleaching treatment. RESULTS: All groups containing BAG experienced an increase in pH from 3.5 to 5.5 in less than 1 min, and the final pH increased as the BAG content increased. The ΔE of all experimental groups was significantly higher than that of the DW group (p < 0.05), but there were no significant differences between different BAG contents (p > 0.05). Gloss significantly decreased in all experimental groups compared to the DW group, and the increased BAG content had significantly affected the decrease in gloss (p < 0.05). There was no statistical difference in surface roughness (p > 0.05), but hardness increased significantly with BAG content after bleaching treatment (p < 0.05). CONCLUSIONS: HP containing 45S5 BAG showed efficacy in tooth whitening. Also, the pH value of the HP remained acidic near 3.5 for 20 min, while the HP containing the 45S5 BAG showed an increase in pH, which inhibited the demineralization of the enamel surface, and maintained the surface morphology. CLINICAL RELEVANCE: These novel materials are promising candidates to minimize enamel surface damage caused by HP during bleaching procedure in dental clinic.
Asunto(s)
Blanqueadores Dentales , Blanqueamiento de Dientes , Animales , Bovinos , Esmalte Dental , Dureza , Peróxido de Hidrógeno/química , Propiedades de Superficie , Blanqueamiento de Dientes/métodos , Blanqueadores Dentales/química , Blanqueadores Dentales/farmacologíaRESUMEN
Biocompatibility is important for the 3D printing of resins used in medical devices and can be affected by photoinitiators, one of the key additives used in the 3D printing process. The choice of ingredients must be considered, as the toxicity varies depending on the photoinitiator, and unreacted photoinitiator may leach out of the polymerized resin. In this study, the use of ethyl (2,4,6-trimethylbenzoyl) phenylphosphinate (TPO-L) as a photoinitiator for the 3D printing of resin was considered for application in medical device production, where the cytotoxicity, colour stability, dimensional accuracy, degree of conversion, and mechanical/physical properties were evaluated. Along with TPO-L, two conventional photoinitiators, phenylbis (2,4,6-trimethylbenzoyl) phosphine oxide (BAPO) and diphenyl (2,4,6-trimethylbenzoyl) phosphine oxide (TPO), were considered. A total of 0.1 mol% of each photoinitiator was mixed with the resin matrix to prepare a resin mixture for 3D printing. The specimens were printed using a direct light processing (DLP) type 3D printer. The 3D-printed specimens were postprocessed and evaluated for cytotoxicity, colour stability, dimensional accuracy, degree of conversion, and mechanical properties in accordance with international standards and the methods described in previous studies. The TPO-L photoinitiator showed excellent biocompatibility and colour stability and possessed with an acceptable dimensional accuracy for use in the 3D printing of resins. Therefore, the TPO-L photoinitiator can be sufficiently used as a photoinitiator for dental 3D-printed resin.
RESUMEN
Renal cell carcinoma (RCC) is the most common form of kidney cancer, with a high recurrence rate and metastasis capacity. Circular RNAs (circRNAs) have been suggested to act as the critical regulator in several diseases. This study is designed to investigate the role of circCSNK1G3 on RCC progression. We observed a highly expression of circCSNK1G3 in RCC tissues compared with normal tissues. The aberrantly circCSNK1G3 promoted the tumour growth and metastasis in RCC. In the subsequent mechanism investigation, we discovered that the tumour-promoting effects of circCSNK1G3 were, at least partly, achieved by up-regulating miR-181b. Increased miR-181b inhibits several tumour suppressor gene, including CYLD, LATS2, NDRG2 and TIMP3. Furthermore, the decreased TIMP3 leads to the enhanced epithelial to mesenchymal transition (EMT) process, thus promoting the cancer metastasis. In conclusion, we identified the oncogenic role of circCSNK1G3 in RCC progression and demonstrated the regulatory role of circCSNK1G3 induced miR-181b expression, which leads to TIMP3-mediated EMT process, thus resulting in tumour growth and metastasis in RCC. This study reveals the promise of circCSNK1G3 to be developed as a potential diagnostic and prognostic biomarker in the clinic. And the roles of circCSNK1G3 in cancer research deserve further investigation.
Asunto(s)
Carcinoma de Células Renales , Quinasa de la Caseína I/genética , Neoplasias Renales , MicroARNs , Carcinoma de Células Renales/genética , Carcinoma de Células Renales/patología , Línea Celular Tumoral , Movimiento Celular/genética , Proliferación Celular/genética , Transición Epitelial-Mesenquimal/genética , Femenino , Regulación Neoplásica de la Expresión Génica , Humanos , Neoplasias Renales/genética , Neoplasias Renales/patología , Masculino , MicroARNs/genética , MicroARNs/metabolismo , Proteínas Serina-Treonina Quinasas , Inhibidor Tisular de Metaloproteinasa-3/genética , Inhibidor Tisular de Metaloproteinasa-3/metabolismo , Proteínas Supresoras de Tumor/genéticaRESUMEN
The aim of this study was to evaluate the antimicrobial, stain and protein removal efficacy of denture or orthodontic appliance cleansers using in vitro test methods. Experimental cleansers were applied for experimental time in each evaluation method. To evaluate the microorganism removal efficacy, C. albicans and S. mutans removal rate was calculated from the specimen surface. Stain and protein removal rate was calculated using the spectrophotometer. Experimental cleansers significantly affected the microorganism removal rate for both C. albicans and S. mutans, as well as the stain and protein removal rates, at each experimental time (p<0.05). As the application time increased, the stain and protein removal rates of all experimental cleansers significantly increased (p<0.05). The present study provided in vitro evaluation methods to assess the efficacy of denture or orthodontic appliance cleansers. Also, manufacturers and researchers can predict clinical outcomes and ensure proper hygiene management of dentures or orthodontic appliances.
Asunto(s)
Candida albicans , Limpiadores de Dentadura , Limpiadores de Dentadura/farmacología , Dentaduras , Aparatos Ortodóncicos , EspectrofotometríaRESUMEN
OBJECTIVES: The objectives of this study were to develop a novel bleaching material containing hydrated calcium silicate (hCS) particles and investigate the effects of hCS on the bleaching efficacy, microhardness, and surface morphology of bovine enamel. MATERIALS AND METHODS: To prepare the hCS particles, white Portland cement was mixed with distilled water and ground into a fine powder. The particles in various proportions were then mixed with 35% hydrogen peroxide solution (HP), while HP without hCS was used as a control (HP), and teeth whitening gel was used as a commercial control (CC). Following the thrice application of experimental and control solutions on the discolored bovine enamel surface for 15 min, color change (n = 10), microhardness (n = 10), and micromorphology (n = 2) of the enamel surface were analyzed. RESULTS: The Δ E* of the enamel surface treated with the experimental solution containing hCS was significantly higher than that of the CC, but there were no significant differences between the different hCS contents. The experimental solution containing hCS reduced the percentage of microhardness loss on the enamel surface, and the percentage of microhardness loss significantly decreased as the content of hCS increased (p < 0.05). The erosion pattern was only observed on enamel surfaces treated with HP and CC. CONCLUSIONS: This study suggests that HP containing hCS is effective in bleaching efficacy. In addition, hCS could also minimize the microhardness loss of tooth structure caused by HP and maintain enamel surface morphology. CLINICAL RELEVANCE: This novel bleaching material is promising for inhibiting demineralization and promoting the remineralization of teeth during bleaching treatment in dental clinics.
Asunto(s)
Blanqueadores Dentales , Blanqueamiento de Dientes , Animales , Compuestos de Calcio , Bovinos , Esmalte Dental , Dureza , Peróxido de Hidrógeno/farmacología , Silicatos , Blanqueadores Dentales/farmacologíaRESUMEN
Background: Clinical recurrence after atrial fibrillation catheter ablation (AFCA) still remains high in patients with persistent AF (PeAF). We investigated whether an extra-pulmonary vein (PV) ablation targeting the dominant frequency (DF) extracted from electroanatomical map-integrated AF computational modeling improves the AFCA rhythm outcome in patients with PeAF. Methods: In this open-label, randomized, multi-center, controlled trial, 170 patients with PeAF were randomized at a 1:1 ratio to the computational modeling-guided virtual DF (V-DF) ablation and empirical PV isolation (E-PVI) groups. We generated a virtual dominant frequency (DF) map based on the atrial substrate map obtained during the clinical AF ablation procedure using computational modeling. This simulation was possible within the time of the PVI procedure. V-DF group underwent extra-PV V-DF ablation in addition to PVI, but DF information was not notified to the operators from the core lab in the E-PVI group. Results: After a mean follow-up period of 16.3 ± 5.3 months, the clinical recurrence rate was significantly lower in the V-DF than with E-PVI group (P = 0.018, log-rank). Recurrences appearing as atrial tachycardias (P = 0.145) and the cardioversion rates (P = 0.362) did not significantly differ between the groups. At the final follow-up, sinus rhythm was maintained without any AADs in 74.7% in the V-DF group and 48.2% in the E-PVI group (P < 0.001). No significant difference was found in the major complication rates (P = 0.489) or total procedure time (P = 0.513) between the groups. The V-DF ablation was independently associated with a reduced AF recurrence after AFCA [hazard ratio: 0.51 (95% confidence interval: 0.30-0.88); P = 0.016]. Conclusions: The computational modeling-guided V-DF ablation improved the rhythm outcome of AFCA in patients with PeAF. Clinical Trial Registration: Clinical Research Information Service, CRIS identifier: KCT0003613.
RESUMEN
Introduction: Whereas, high-power short-duration (HPSD) radiofrequency (RF) ablation is generally used in atrial fibrillation (AF) catheter ablation (CA), its efficacy, safety, and influence on autonomic function have not been well established in a large population. This study compared HPSD-AFCA and conventional power (ConvP)-AFCA in propensity score matched-population. Methods: In 3,045 consecutive patients who underwent AFCA, this study included 1,260 patients (73.9% male, 59 ± 10 years old, 58.2% paroxysmal type) after propensity score matching: 315 in 50~60W HPSD group vs. 945 in the ConvP group. This study investigated the procedural factors, complication rate, rhythm status, and 3-month heart rate variability (HRV) between the two groups and subgroups. Results: Procedure time was considerably short in the HPSD group (135 min in HPSD vs. 181 min in ConvP, p < 0.001) compared to ConvP group, but there was no significant difference in the complication rate (2.9% in HPSD vs. 3.7% in ConvP, p = 0.477) and the 3-month HRV between the two groups. At the one-year follow-up, there was no significant difference in rhythm outcomes between the two groups (Overall, Log-rank p = 0.885; anti-arrhythmic drug free, Log-rank p = 0.673). These efficacy and safety outcomes were consistently similar irrespective of the AF type or ablation lesion set. The Cox regression analysis showed that the left atrium volume index estimated by computed tomography (HR 1.01 [1.00-1.02]), p = 0.003) and extra-pulmonary vein triggers (HR 1.59 [1.03-2.44], p = 0.036) were independently associated with one-year clinical recurrence, whereas the HPSD ablation was not (HR 1.03 [0.73-1.44], p = 0.887). Conclusion: HPSD-AFCA notably reduced the procedure time with similar rhythm outcomes, complication rate, and influence on autonomic function as ConvP-AFCA, irrespective of the AF type or ablation lesion set.
RESUMEN
[Figure: see text].
Asunto(s)
Fibrilación Atrial/cirugía , Ablación por Catéter/métodos , Criocirugía/métodos , Sistema de Conducción Cardíaco/fisiopatología , Venas Pulmonares/cirugía , Fibrilación Atrial/diagnóstico , Fibrilación Atrial/fisiopatología , Ecocardiografía/métodos , Femenino , Humanos , Imagenología Tridimensional , Masculino , Persona de Mediana Edad , Tomografía Computarizada Multidetector/métodos , Estudios Prospectivos , Recurrencia , Factores de Tiempo , Resultado del TratamientoRESUMEN
The aim of this study is to investigate the resistance of various fluoride-releasing restorative materials against the demineralization and remineralization of enamel surfaces, including those that have been recently introduced to the market. Three different fluoride-releasing restorative materials were considered: glass ionomer (FI), resin-modified glass ionomer (RL), and an alkasite restorative material (CN). The acid neutralization ability was investigated using pH measurement, and the concentrations of released fluoride and calcium ions were measured. Finally, the demineralization resistance and remineralization effects of enamel were observed using a microhardness tester and SEM. CN showed an initial substantial increase in pH followed by a steady increase, with values higher than those of the other groups (p < 0.05). All three groups released fluoride ions, and the CN group released more calcium ions than the other groups (p < 0.05). In the acid resistance test, from the microhardness and SEM images, the CN group showed effective resistance to demineralization. In the remineralization test, the microhardness results showed that the FI and CN groups recovered the microhardness from the values of the demineralized enamel surface (p < 0.05). This was confirmed by the SEM images from remineralization tests; the CN group showed a recovered demineralized surface when immersed in artificial saliva for 7 days. In conclusion, alkasite restorative material can be an effective material when used in cariogenic environments.