BACKGROUND: Loeys-Dietz syndrome (LDS) is a type of connective tissue disease with systemic symptoms similar to Marfan syndrome. Ocular findings are rarely reported especially fundus and extraocular muscles. CASE PRESENTATION: A 6-month old boy with systemic skeletal development delay was found peripheral non-perfusion and neovascularization in the both eyes, and gaven intravitreal injection of ranibizumab and laser. Fundus examination revealed a mild straightening of the temporal vessel in the both eyes. A 22-month old girl with confirmed connective tissue disorder presented to our hospital for strabismus and showed congenital hypoplasia of extraocular muscles. She also had arteriovenous anastomosis in the retinal. The diagnosis of LDS was supported by the genetic DNA examination. CONCLUSION: His is the first report of LDS with congenital hypoplasia of extraocular muscles, meanwhile, ocular examination especially fundus should be paid attention to.

Enhanced Electrochemical Performance of Fast Ionic Conductor LiTi2(PO4)3-Coated LiNi1/3Co1/3Mn1/3O2 Cathode Material.

Layered LiNi1/3Co1/3Mn1/3O2 (NCM333) is successfully coated by fast ionic conductor LiTi2(PO4)3 (LTP) via a wet chemical method. The effects of LTP on the physicochemical properties and electrochemical performance are studied. The results reveal that a highly layered structure of NCM333 can be well maintained with less cation mixing after LTP coating. LTP of about 5 nm thickness is coated on the surface of NCM333. Such an LTP coating layer can effectively suppress the side reactions between NCM333 and electrolyte but will not hinder the lithium ion transmission. As a result, LTP-coated NCM333 owns an improved capability and cyclic performance, for example, NCM333/LTP delivers an initial capacity as high as 121.0 mA h g-1 with a capacity retention ratio of 82.3% after 200 cycles at 10 C, whereas NCM333 only has an initial capacity of 120.4 mA h g-1 with a very low capacity retention ratio of 66.4%. This method of using a fast ionic conductor like LTP as a coating material may provide a simple and effective strategy to modify those electrode materials with poor cyclic performance.