A PSCLC Pattern Prepared Based on Handedness Inversion for Anti-counterfeiting.

Handedness inversion has been widely studied in supramolecular chemistry and material sciences. Herein, a photoisomerizable chiral dopant was synthesized, which could induce the formation of a cholesteric phase with right-handedness. The Bragg reflection band of the cholesteric liquid crystal (CLC) mixture shifted to the long wavelength with extending 365 nm UV light irradiation time. Based on this photochromic property, a colourful polymer-stabilized CLC (PSCLC) film was prepared using a grayscale mask. A handedness reversible CLC mixture was prepared using a mixture of this chiral dopant and S5011. With extending the UV light irradiation time, the handedness of the CLC mixture changed from right- to left-handedness. A patterned PSCLC film was prepared using this CLC mixture. Complementary images were observed under right- and left-handedness circularly polarized lights. The results shown here not only give us a better understanding the competition between photopolymerization and photoisomerization, but also lay the foundations for decoration and anti-counterfeiting.

Light Intensity-Selective Photopolymerization and Photoisomerization for Creating Colorful Polymer-Stabilized Cholesteric Liquid Crystal Patterns.

Polymer-stabilized cholesteric liquid crystal (PSCLC) films have been widely studied for their application as sensors, polarizers, and reflective windows. However, the preparation of programmable and colorful patterns based on the structural color is still challenging. Herein, the photochromic CLC mixtures were prepared by adding a photoisomerizable chiral additive (CA) and a photoinitiator in the nematic liquid crystal LC242. Under UV irradiation with weak intensity, photoisomerization of the CA was carried out and photopolymerization was suppressed by oxygen inhibition. With extending the irradiation time, the helical pitch of the CLC film increased and the selective Bragg reflection band tended to redshift. Under strong UV irradiation, oxygen inhibition was overcome and photopolymerization dominates the reaction. Therefore, the colorful-patterned PSCLC films were able to be prepared using masks. The results shown here not only give us a better understanding of the effect of oxygen inhibition but also lay the foundations for practical applications such as decoration and optical devices.