Graphene and two-dimensional transition metal carbides and/or nitrides (MXenes) are important materials for making flexible energy storage devices because of their electrical and mechanical properties. It remains a challenge to assemble nanoplatelets of these materials at room temperature into in-plane isotropic, free-standing sheets. Using nanoconfined water-induced basal-plane alignment and covalent and π-π interplatelet bridging, we fabricated Ti3C2Tx MXene-bridged graphene sheets at room temperature with isotropic in-plane tensile strength of 1.87 gigapascals and moduli of 98.7 gigapascals. The in-plane room temperature electrical conductivity reached 1423 siemens per centimeter, and volumetric specific capacity reached 828 coulombs per cubic centimeter. This nanoconfined water-induced alignment likely provides an important approach for making other aligned macroscopic assemblies of two-dimensional nanoplatelets.
RESUMEN
Calcite mesocrystals were proposed, and have been widely reported, to form in the presence of polymer additives via oriented assembly of nanoparticles. However, the formation mechanism and the role of polymer additives remain elusive. Here, inspired by the biomineralization process of sea urchin spine comprising magnesium calcite mesocrystals, we show that calcite mesocrystals could also be obtained via attachment of amorphous calcium carbonate (ACC) nanoparticles in the presence of inorganic zinc ions. Moreover, we demonstrate that zinc ions can induce the formation of temporarily stabilized amorphous nanoparticles of less than 20 nm at a significantly lower calcium carbonate concentration as compared to pure solution, which is energetically beneficial for the attachment and occlusion during calcite growth. The cation-mediated particle attachment crystallization significantly improves our understanding of mesocrystal formation mechanisms in biomineralization and offers new opportunities to bioprocess inspired inorganic ions regulated materials fabrication.