RESUMEN
For the first time, the possibility of obtaining B-site disordered, Ruddlesden-Popper type, high-entropy oxides has been proven, using as an example the LnSr(Co,Fe,Ga,Mn,Ni)O4 series (Ln = La, Pr, Nd, Sm, or Gd). The materials were synthesized using the Pechini method, followed by sintering at a temperature of 1200 °C. The XRD analysis indicated the single-phase, I4/mmm structure of the Pr-, Nd-, and Sm-based materials, with a minor content of secondary phase precipitates in La- and Gd-based materials. The SEM + EDX analysis confirms the homogeneity of the studied samples. Based on the oxygen non-stoichiometry measurements, the general formula of LnSr(Co,Fe,Ga,Mn,Ni)O4+δ, is established, with the content of oxygen interstitials being surprisingly similar across the series. The temperature dependence of the total conductivity is similar for all materials, with the highest conductivity value of 4.28 S/cm being reported for the Sm-based composition. The thermal expansion coefficient is, again, almost identical across the series, with the values varying between 14.6 and 15.2 × 10-6 K-1. The temperature stability of the selected materials is verified using the in situ high-temperature XRD. The results indicate a smaller impact of the lanthanide cation type on the properties than has typically been reported for conventional Ruddlesden-Popper type oxides, which may result from the high-entropy arrangement of the B-site cations.
RESUMEN
Phase composition, crystal structure, and selected physicochemical properties of the high entropy Ln(Co,Cr,Fe,Mn,Ni)O3-δ (Ln = La, Pr, Gd, Nd, Sm) perovskites, as well as the possibility of Sr doping in Ln1-xSrx(Co,Cr,Fe,Mn,Ni)O3-δ series, are reported is this work. With the use of the Pechini method, all undoped compositions are successfully synthesized. The samples exhibit distorted, orthorhombic or rhombohedral crystal structure, and a linear correlation is observed between the ionic radius of Ln and the value of the quasi-cubic perovskite lattice constant. The oxides show moderate thermal expansion, with a lack of visible contribution from the chemical expansion effect. Temperature-dependent values of the total electrical conductivity are reported, and the observed behavior appears distinctive from that of non-high entropy transition metal-based perovskites, beyond the expectations based on the rule-of-mixtures. In terms of formation of solid solutions in Sr-doped Ln1-xSrx(Co,Cr,Fe,Mn,Ni)O3-δ materials, the results indicate a strong influence of the Ln radius, and while for La-based series the Sr solubility limit is at the level of xmax = 0.3, for the smaller Pr it is equal to just 0.1. In the case of Nd-, Sm- and Gd-based materials, even for the xSr = 0.1, the formation of secondary phases is observed on the SEM + EDS images.