RESUMEN
Posttreatment of pristine metal-organic frameworks (MOFs) with suitable vapor may be an effective way to regulate their structures and properties but has been less explored. Herein, we report an interesting example in which a crystalline nonporous Eu(III)-MOF was transferred to a porous amorphous MOF (aMOF) via iodine vapor adsorption-desorption posttreatment, and the resulting aMOF showed improved turn-on sensing properties with respect to Ag+ ions. The crystalline Eu-MOF, namely, Eu-IPDA, was assembled from Eu(III) and 4,4'-{4-[4-(1H-imidazol-1-yl)phenyl]pyridine-2,6-diyl}dibenzoic acid (H2IPDA) and exhibited a two-dimensional (2D) coordination network based on one-dimensional secondary building blocks. The close packing of the 2D networks gives rise to a three-dimensional supramolecular framework without any significant pores. Interestingly, the nonporous Eu-IPDA could absorb iodine molecules when Eu-IPDA crystals were placed in iodine vapor at 85 °C, and the adsorption capacity was 1.90 g/g, which is comparable to those of many MOFs with large BET surfaces. The adsorption of iodine is attributed to the strong interactions among the iodine molecule, the carboxy group, and the N-containing group and leads to the amorphization of the framework. After immersion of the iodine-loaded Eu-IPDA in EtOH, approximately 89.7% of the iodine was removed, resulting in a porous amorphous MOF, denoted as a-Eu-IPDA. In addition, the remaining iodine in the a-Eu-IPDA framework causes strong luminescent quenching in the fluorescence emission region of the Eu(III) center when compared with that in Eu-IPDA. The luminescence intensity of a-Eu-IPDA in water suspensions was significantly enhanced when Ag+ ions were added, with a detection limit of 4.76 × 10-6 M, which is 1000 times that of pristine Eu-IPDA. It also showed strong anti-interference ability over many common competitive metal ions and has the potential to sense Ag+ in natural water bodies and traditional Chinese medicine preparations. A mechanistic study showed that the interactions between Ag+ and the absorbed iodine, the carboxylate group, and the N atoms all contribute to the sensing performance of a-Eu-IPDA.
RESUMEN
The research on amorphous metal-organic frameworks (aMOFs) is still in its infancy, and designing and constructing aMOFs with functional pores remains a challenge. Two aMOFs based on Co(II) and heterotopic triangular ligands with large conjugated aromatic planes, namely aMOF-1 and aMOF-2, were constructed and characterized by IR, XPS, EA, ICP, XANS and so on. aMOF-1 possesses mesopores, whereas aMOF-2 possesses micropores. The porosity, conjugated aromatic plane and uncoordinated N atoms in the framework allow these aMOFs to adsorb iodine and dyes. The iodine adsorption capacity of aMOF-1 is 3.3 g per g, which is higher than that of aMOF-2 (0.56 g per g), mainly due to the expansion or swelling of aMOF-1 after iodine adsorption. The uptake of cationic dyes by aMOF-2 showed more rapid kinetics and a higher removal rate than that by aMOF-1, mainly due to the difference in the porosity and surface charge. Although the surface charges of aMOF-1 and aMOF-2 are negative, both of them showed significantly faster adsorption kinetics toward anionic dyes, among which methyl orange (MO) and Congo red (CR) can be removed in 5 min. This occurs possibly because the quick adsorption of Na+ ions alters the surface charge of the framework and promotes dye uptake. The adsorption capacities of aMOF-1 for MO and CR reached 921 and 2417 mg g-1, respectively. The correlation data for aMOF-2 are 1042 and 1625 mg g-1, respectively. All adsorption capacities are among the highest compared to many cMOFs. Adsorption in mixed dye solution is found to be charge-dependent, kinetic-dependent, and synergetic in these systems. The porosity, surface charge regulation during adsorption, weak interactions and multiple adsorption processes contribute to the dye adsorption performance.