RESUMEN
Fluorine-containing waste is one kind of hazardous waste characteristic by hard disposal and utilization, it is an attractive way to prepare for fluoride-based luminescent matrix. In this work, to realize the high value-added utilization of fluorine-containing waste and reduce cost of the raw materials for preparation near-infrared (NIR) glass-ceramic (GC) photocatalyst, the pure fluoride of luminescent matrix was replaced by introducing fluorine-containing waste. The waste contained NIR GC photocatalyst was synthesis by the method of facile in-situ etching of an upconversion GC with HCl, which possesses core-shell structure, where the GC micro-powder including optically active centers lanthanides doped CaF2 nanocrystals are displayed as the core, and the BiOCl is as the superficial coating. The upconversion emission performance of CaF2 based luminescent matrix in photocatalyst is not weakened with HCl etching. NIR GC photocatalyst has high methyl orange and enrofloxacin degradation rate of 86 % and 82 % over 180 min after NIR light irradiation, respectively. The UV-Vis-NIR photocatalytic activity was enhanced degradation rate (93 % in 15 min) of enrofloxacin compared with those of commercial P25 and BiOCl. In addition, the photocatalyst had stable photocatalytic activity and it also can be regenerated. The study provided references for high value-added utilization fluorine-containing waste.
RESUMEN
Negative thermal expansion (NTE) material as a compensator is very important for accurately controlling the thermal expansion of materials. Along with the magnitude of the coefficient of thermal expansion, the operating temperature window of the NTE materials is also a major concern. However, only a few of the NTE materials possess both a large operating temperature range and a large thermal expansion coefficient. To explore this type of new NTE material, the Mn0.965Co1.035Ge fine powders were prepared by mechanical ball milling (BM). These fine powders show a largely extended NTE operation temperature window simultaneously possessing a giant thermal expansion coefficient. For samples treated with different BM times, such as the BM-0.5h, BM-4h, and BM-12 h samples, the operating temperature window (Δ T) and linear thermal expansion coefficient (αL) are 167 K (222-389 K) and â¼ -63 ppm/K, 221 K (140-360 K) and â¼ -41.3 ppm/K, and 208 K (234-442 K) and â¼ -40 ppm/K, respectively, which are larger than most well-known NTE materials. More strikingly, all BM samples have a large constant linear NTE coefficient with an ultrawide temperature window covering room temperature. For these three samples, these values are â¼ -52 ppm/K (140 K), â¼ -58.3 ppm/K (110 K), and â¼ -65 ppm/K (80 K), respectively. The origin of the excellent NTE properties is discussed based on the thermomagnetic measurements and X-ray absorption spectroscopic results.
RESUMEN
Nanocrystalline yttria-stabilized zirconia (ZrO2-8 mol%Y2O3, 8YSZ) was synthesized by a homogeneous precipitation process using urea as the precipitation agent. Zirconia (ZrO2) transparent ceramics samples have been successfully fabricated by a microwave sintering process at low temperature. The technologies of low-temperature microwave sintering and the relationships of the microstructures and properties of the specified samples have been investigated in detail. We have found out that the low-temperature microwave sintering has its obvious advantages over the other methods in manufacturing zirconia transparent ceramics.