RESUMEN
A novel hybrid membrane was developed on the basis of poly(m-phenylene isophthalamide) (PA) by introducing an original complex modifier into the polymer; this modifier consisted of equal amounts of heteroarm star macromolecules with a fullerene C60 core (HSM) and the ionic liquid [BMIM][Tf2N] (IL). The effect of the (HSM:IL) complex modifier on characteristics of the PA membrane was evaluated using physical, mechanical, thermal, and gas separation techniques. The structure of the PA/(HSM:IL) membrane was studied by scanning electron microscopy (SEM). Gas transport properties were determined by measuring He, O2, N2, and CO2 permeation through the membranes based on PA and its composites containing a 5 wt% modifier. The permeability coefficients of all gases through the hybrid membranes were lower than the corresponding parameters for the unmodified membrane, whereas the ideal selectivity in the separation of He/N2, CO2/N2, and O2/N2 gas pairs was higher for the hybrid membrane. The position of the PA/(HSM:IL) membrane on the Robeson's diagram for the O2/N2 gas pair is discussed.
RESUMEN
The absorption and release of poly(vinylpyrrolidone)-fullerene C60 complexes (PVP/C60) from a model microgel is studied. A dry microgel based on a chemically cross-linked sodium polyacrylate was swollen in the aqueous solutions of complexes which were afterwards released under shear stress. First, gel swelling degree in static conditions in the excess of PVP/C60 solutions was studied: the degree of swelling decreases with the increase in PVP/C60 concentration. While pure PVP is homogeneously distributed between the gel and the surrounding solution, a slight concentration of complexes outside the gel was recorded. It was attributed to PVP/C60 hydrophobicity leading to the decrease in the thermodynamic quality of fullerene-containing solution being gel solvent. The release of PVP/C60 solutions induced by shear was studied with counter-rotating rheo-optical technique and compared with PVP solution release under the same conditions. The amount of solution released depends on polymer concentration and shear strain. Contrary to pure PVP solutions in which rate of release decreases with the increase in polymer concentration, PVP/C60 complexes are released faster when fullerene concentration inside the gel is higher.