Composite Containing Calcium Phosphate Particles Functionalized with 10-MDP.

The phosphate ester monomer 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) is capable of bonding to hydroxyapatite and, for this reason, is a key component of several self-etch adhesives. In this study, dicalcium phosphate dihydrate particles (DCPD; CaHPO4.2H2O) were functionalized with 10-MDP and used to formulate an experimental composite with 50 vol% inorganic content (3:1 DCPD:silanated barium glass ratio) dispersed in a BisGMA/TEGDMA matrix. The tested hypothesis was that DCPD functionalization would improve the composite's mechanical performance without compromising Ca2+ release. Composites containing nonfunctionalized DCPD or only reinforcing glass (in both cases, with or without 10-MDP mixed in the resin phase) were used as controls. Materials were tested for degree of conversion (DC; by Fourier transform infrared spectroscopy), water sorption (WS) and solubility (SL; according to ISO 4049), biaxial flexural strength (BFS)/modulus (FM) after 24 h and 5 mo in water, and 28-d Ca2+ release in water (by plasma-coupled optical emission spectroscopy). Data were analyzed using analysis of variance/Tukey test (alpha: 5%). DCPD functionalization did not interfere with DC. The composite containing functionalized DCPD showed significantly lower WS and SL in comparison with the material formulated with nonfunctionalized particles. The presence of 10-MDP (as a functionalizing agent or dispersed in the resin phase) reduced the composite's initial BFS and FM. After 5 mo in water, the composite with functionalized DCPD and both glass-only composites were able to maintain their mechanical properties at levels statistically similar to what was observed after 24 h. Ca2+ release was significantly reduced in both formulations containing 10-MDP. In conclusion, DCPD functionalization with 10-MDP increased the composite's resistance to hydrolytic degradation, improving its mechanical stability after prolonged water storage. However, the impaired water transit at the particle-matrix interface led to a reduction in Ca2+ release.

Individual variation is the key to the development of a vaccine against Staphylococcus aureus: a comparative study between mice lineages.

Bacterial infections occur worldwide and are a major public health problem. Among pathogens, Staphylococcus aureus is the main causative agent of bacterial diseases in the world. This study aimed to evaluate which components of the immune system could act protectively against a S. aureus infection in intradermally immunized mice. C57BL/6 and A/j mice were immunized intradermally with S. aureus inactivated by heat and then challenged with viable strains in an air pouch model. At 6, 12, and 24 h after the challenge, euthanasia was performed, and the cellular profile of the inflammatory infiltrate, cytokines, and the bacterial load were evaluated in the air pouch lavages. Immunized mice demonstrated that the intradermal immunization with S. aureus promoted protection in C57BL/6 mice by reducing the bacterial, which was correlated with increased serum concentration of IgG antibodies (IgG1 and IgG2a) against S. aureus. The increase in IgG2a antibody levels was correlated with a decrease of bacterial load in intradermally immunized C57BL/6 mice, along with production of IL-17A at the inflammation site, as well as IgG1consumption. Similar results were not found in the A/j lineage. In conclusion, a vaccine against S. aureus should focus more on the individual characteristics of the host because it is a determinant factor for the success of the immunization.