How Water Content Can Influence the Chemomechanical Properties and Physical Degradation under Aging of Experimental Adhesives.

Objective: To evaluate the physicochemical (sorption (SOR), solubility (SOL), and degree of conversion (DC)) and mechanical (flexural strength (FS), modulus of elasticity (ME), and compressive strength (CS)) properties of adhesives with different water contents (D2O). Materials and Methods: An adhesive was formulated: 55 wt% BisGMA, 45 wt% HEMA, 0.5 wt% camphorquinone, 0.5 wt% EDMAB, and 1.0 wt% DPIHP. D2O was added into the adhesives (0 wt%, 10 wt%, and 16 wt%). DC was monitored through the FTIR. FS, ME, CS, SOR, and SOL were tested. The adhesive samples were aged in deionized water, ethanol, and acetone. Data were submitted to ANOVA and Tukey's tests (5%). Results: For DC, the 0 wt% group showed a significant reduction (68.09 ± 0.14A) compared with the 10 wt% (87.07 ± 0.81B) and 16 wt% groups (89.87 ± 0.24B); 10 wt% showed the highest FS (MPa) mean values (141.6 ± 6.71B) compared with the 0 wt% (109.4 ± 20.5A) and 16 wt% (107.8 ± 15.8A). For the CS (MPa) and ME (GPa), the 16 wt% showed the lowest mean values (98.8 ± 18.0B and 2.2 ± 0.3B, respectively) compared with the 10 wt% and 0 wt%. For the SOR, 16 wt% of water showed the highest mean values and the ethanol showed the lowest mean values of SOL regardless of water content. Conclusion: The amount of water content and the types of aging solvents significantly affect the adhesive properties.

Universal adhesive: the effect of different simulated pulpal pressure fluids and bonding modes to dentin.

The aim of this study was to evaluate the effect of SPP with either fetal bovine serum (FBS) or deionized water (DW) on the bond strength (µTBS) of a Universal adhesive to dentin, in both etch-and-rinse (ER) and self-etch (SE) modes. The kinematic viscosity (cSt) of FBS and DW was measured at 25 °C ± 0.1 ºC. Seventy-two sound human molars were sectioned and randomly divided into three groups according to the SPP conditions: (1) Control (0 cm H2O), (2) SPP (15 cm H2O) with FBS, (3) SPP (15 cm H2O) with DW. Each group was subdivided (n = 10) based on the bonding modes: ER (37% phosphoric acid + ScothBond Universal Adhesive) or SE (ScothBond Universal Adhesive). Samples were then submitted to µTBS. Data were analyzed by Student's t test, two-way ANOVA and Tukey tests (p < 0.05). The cSt results showed that DW (23.59 ± 0.39) had significantly higher values than FBS (22.33 ± 0.06). With regard to SPP, the control group (36.1 MPa) had significantly higher values of µTBS when compared to the SPP using FBS (31.06 MPa) and SPP with DW (26.55 MPa). According to ANOVA, the bonding modes and the interaction of simulated pulpal pressure (SPP) did not statistically influence the results (p < 0.05). The presence of SPP reduced the bond strength of Universal adhesive to dentin. DW during SPP had significantly reduced bonding values when compared to FBS. Bonding strategies were not affected by SPP when evaluated in a short period of time (24 h).

Polyphenol-enriched extract of Arrabidaea chica used as a dentin pretreatment or incorporated into a total-etching adhesive system: Effects on bonding stability and physical characterization.

The aim of this paper was to evaluate the physical properties and the long-term bond strength of a 2.5% polyphenol-enriched extract of Arrabidaea chica (AC) incorporated into both the phosphoric acid and the primer of a three-step total-etch adhesive, or into an aqueous solution as a dentin pretreatment. Fifty dentin surfaces received the treatments (n = 10): CON (control) - application of the three-step adhesive system (Adper Scotchbond Multipurpose, 3M ESPE); WAT - distilled water used as a pretreatment after dentin etching and before application of the adhesive system; ACPA - AC incorporated into the phosphoric acid; ACW - dentin pre-treatment with AC incorporated into an aqueous solution after etching; ACP - AC incorporated into the primer. Microtensile bond strength tests were performed after 24 h, 6 and 12 months of storage. Slices from the resin-dentin interface were obtained for scanning electron microscopy analysis of the hybrid layer. Degree of conversion of AC incorporated into the primer was evaluated. The particle size, polydispersity index and zeta potential of all the solutions prepared by incorporating AC (phosphoric acid, primer and distilled water) were measured by dynamic light scattering, which brought about changes after incorporation. Degree of conversion of the primer was not affected after incorporating AC. ACP showed lower microtensile bond strength values than the other groups. Bond strength decreased after 6 months of storage, stabilizing at the 12-month evaluation. Therefore, use of AC incorporated into the primer led to lower bond strength values, since AC modified the physical properties (particle size, polydispersity index and zeta potential) of the primer, but did not change the degree of conversion. Application of AC as a dentin pretreatment did not affect bond strength or the micromorphological characteristics of the hybrid layer.

Diffusion of hydroxyl ion on external root surface using different irrigating solutions: An In vitro study.

AIMS: The aim of this study was to evaluate the diffusion of hydroxyl ion to the external root surface using different irrigating solutions and intracanal medication with calcium hydroxide. MATERIALS AND METHODS: Sixty bovine tooth roots were randomly divided into six experimental groups (n = 10), according to the irrigating substance used during biomechanical preparation: 12% glycolic propolis extract (PROP); 20% glycolic ginger extract (GENG); 2% sodium hypochlorite with surfactant (NaOClS); 2% chlorhexidine gel (CLX); 2.5% sodium hypochlorite (NaOCl); and physiological saline solution. After filling the root canals with calcium hydroxide paste, pH measurements were taken directly at the external cavities over time intervals of up to 30 days. STATISTICAL ANALYSIS USED: Data were submitted to two-way ANOVA and Tukey's test (P < 0.05). RESULTS: The pH of the external root surface was increased when the surfactant associated with NaOCl was used. However, the pH values were very close for the different groups. Hydroxyl ion diffusion up to the external root surface did not exceed the pH value of 8.5, and in the hollow passage of the canal, the pH was higher than 12. CONCLUSIONS: Hydroxyl ion diffusion of calcium hydroxide paste through the dentinal tubules up to the external root surface allows minimal alkalinization of this surface, and it is greater when using NaOCl with surfactant during biomechanical preparation.

Effect of ethylenediaminetetraacetic acid and hyaluronic acid on the viability and cytokine expression of periodontal ligament fibroblasts.

BACKGROUND/AIMS: Dental root cell proliferation following tooth avulsion has not been well researched. Understanding the effects of dry time and dentin treatment influences on cell proliferation is essential to provide evidence-based guidelines for tooth replantation. The study evaluated the viability of periodontal ligament fibroblasts (PLF) in contact with roots, submitted to surface treatments with ethylenediaminetetraacetic acid (EDTA) and hyaluronic acid (HA) at different times, including to quantify inflammatory cytokines interleukin (IL)-6, IL-8, IL-1ß and TNF-α expressed by PLF. The adhesion of fibroblasts to treated root surfaces was also evaluated. MATERIAL AND METHODS: One hundred and eight cementum discs from bovine teeth were randomly divided into groups according to time periods of being dry (n = 12) as follows: (i) fresh discs that were not kept dry, (WD); (ii) dry for 1 hour (1 hd); and (iii) dry for 24 hours (24 hd). The discs were subdivided into 3 subgroups (n = 12) according to surface treatments: (iv) no treatment, (v) treatment with EDTA, (vi) treatment with HA. The discs were placed in 96-well plates, and PLF were seeded and kept in contact with the discs for 48 hours. Cell viability on the surface of the discs was assessed by XTT, and PLF adhesion was evaluated using scanning electron microscopy (SEM). Quantification of cytokines was performed using enzyme-linked immunosorbent assay (ELISA). Data were submitted to ANOVA and Tukey's test (α = .05). RESULTS: Surface treatment had a statistically significant effect on the cell viability in groups WD (P = .03), 1 hd (P = .01) and 24 hd (P = .048). PLF in contact with dried root surfaces expressed more cytokines without treatment with IL-6 decreasing the expression when treated with HA for 24 hours. SEM also showed adhesion of PLF to the surface of all discs at all time periods. CONCLUSION: EDTA + HA is an alternative treatment for cases of avulsed teeth as it promoted adhesion and increased viability of PLF.

Resin-dentin bond stability and physical characterization of a two-step self-etching adhesive system associated with TiF4.

OBJECTIVES: To evaluate the bond strength to superficial (SD) and deep (DD) dentin after the use of 2.5% (T2.5%) or 4% (T4%) titanium tetrafluoride (TiF4) in aqueous solution as a dentin pretreatment, or when incorporated into the primer (T2.5%P and T4%P) of an adhesive system (Clearfil SE Bond/CL). Degree of conversion (DC), particle size (PS), polydispersity index (PI) and zeta potential (ZP) of the solutions were evaluated. METHODS: Fifty molars were sectioned longitudinally to obtain two slices of each tooth, which were demarcated into SD and DD. Treatments were applied (n=10): CL; T2.5%; T4%; T2.5%P; T4%P. After 24h or 180days storage, microshear bond strength tests were performed. The DC values of T2.5%P and T4%P were evaluated by FTIR. PS, PI and ZP were measured using dynamic light scattering. RESULTS: Analysis of mixed models showed significant effect of concentration of TiF4 * solution * storage time (p=0.0075). There were higher bond strength values in SD than in DD (p=0.0105) for all treatments in both times. The failure mode showed adhesive failures in the majority of groups, irrespective of depth and time (p=0.3746). The bond strength values were not affected by treatments. Lower average particle size was observed for T2.5%P and T4%P at baseline. T2.5% and T4% showed a trend towards agglomeration. SIGNIFICANCE: Higher bond strength values were achieved at SD for all treatments and times. The failure modes observed were adhesive. TiF4 incorporation did not affect DC. T2.5%P and T4%P presented excellent stability over time.

Staining Beverages and Cigarette Smoke on Composite Resin and Human Tooth Fluorescence by Direct Spectrometry.

INTRODUCTION: This study evaluated the fluorescence intensity (FI) of different brands of composite resins (CRs) and compare those values with the FI of human tooth, under the action of cigarette smoke (CI), coffee (CA), and soft drink (CO), measured by direct spectrometry. MATERIALS AND METHODS: A total of 30 specimens of each brand (Filtek Z350, Esthet-X, Amelogen, Durafill) were made. Others 30 tooth specimens (3 mm/diameter) were obtained from human molars using a trephine bur. The specimens were randomly divided into three groups (n = 10), according to substances: CI, CA, CO. The FI was directly measured using an optic fiber associated with a spectrometer and was measured at baseline and after staining. Data were submitted to Kruskal-Wallis, Dunnett, and Dunn tests. RESULTS: Staining influenced FI mean values among CRs and between those with human tooth. Z showed the closest FI mean values of tooth after staining. CONCLUSION: Staining beverages and cigarette smoke negatively influenced on FI of CR and human tooth. CLINICAL SIGNIFICANCE: The study shows darkening treatments influenced on the fluorescent property of the dental tissues and restorative materials according to the direct spectrometry analysis.