A new multiphase calcium phosphate graft material improves bone healing-An in vitro and in vivo analysis.

This study aims to evaluate the potential of a novel biomaterial synthesized from amorphous calcium phosphate (ACP), octacalcium phosphate (OCP), and hydroxyapatite (HA) to repair critical-sized defects (CSD) in rabbit calvaria. In vitro analyses of cell viability, cell proliferation, formation of mineral nodules, and cell differentiation using qPCR were performed for comparing experimental calcium phosphate (ECP), deproteinized bovine bone (DBB), and beta-tricalcium phosphate (ß-TCP). Bilateral CSDs were created in 45 rabbit calvaria. Six groups were evaluated: ECP, ECP + fibrin sealant (ECP + S), coagulum, autogenous bone, DBB, and ß-TCP. Euthanasia was performed at 2, 4, and 8 weeks, followed by micro-computed tomography and histological and immunohistochemical analyses. Results from in vitro analyses revealed similar biocompatibility for all tested materials and a tendency for higher gene expression of some bone markers in the ECP group than in ß-TCP and DBB groups at 7 days. In contrast to that in DBB and ß-TCP groups, ECP displayed growing bone volume over total volume percentage (BV/TV%) with time in vivo. Histological analysis revealed a greater number of giant cells and reduced size of grafted particles in ECP during all periods of analysis. RUNX-2 expression was statistically lower in ECP than DBB at 2 and 4 weeks. Despite no statistical significance, ECP presented the highest absolute values for ALP-expression at 2, 4, and 8 weeks compared with other groups. Together, our findings indicate that a combination of the ACP, OCP, and HA phases into ECP is beneficial and promising for bone regeneration.

Sol-gel based calcium phosphates coatings deposited on binary Ti-Mo alloys modified by laser beam irradiation for biomaterial/clinical applications.

Ti-15Mo alloy samples were irradiated by pulsed Yb: YAG laser beam under air and atmospheric pressure. Calcium phosphate coatings were deposited on the irradiated surfaces by the sol-gel method. The sol was prepared from the precursors Ca (NO3)2.4H2 O and H3 PO4. The modified surfaces were submitted to heat treatment conditions at 350 and 600 °C. The results showed that the two conditions established have a sufficient energy to promote ablation on the laser beam irradiated surfaces. Likewise, it has been demonstrated the processes of fusion and fast solidification from the laser beam irradiation, under ambient atmosphere, inducing the formation of stoichiometric TiO2 and non-stoichiometric titanium oxides, including Ti3O5, TiO, Ti3O and Ti6O with different oxide percentages depending on the fluency used. Besides that, laser modification has allowed a clean and reproducible process, providing no traces of contamination, an important feature for clinical applications. The physico-chemical and morphological properties indicated the formation of a mixture of phases: calcium pyrophosphate, hydroxyapatite and ß-TCP for the procedure (PA: calcination temperature), whereas HA (hydroxyapatite) and ß-TCP (tricalcium phosphate) were obtained by the procedure (PB: calcination temperature). Therefore, it was possible to obtain a Ti-15Mo alloy surface consisted on calcium phosphate ceramics of biological interest using the procedure (PB). Thus, the laser beam irradiation associated to bioactive coatings of calcium phosphates of biological interest have shown to be promising and economically feasible for use in dental and orthopedic implants.