RESUMEN
OBJECTIVES: This study aimed to evaluate the feasibility of monolithic zirconia laminate veneers (MZLV) compared to lithium disilicate laminate veneers (LDLV). MATERIALS AND METHODS: Sixty resin replicas, each prepared with depths of 0.5 mm, 0.7 mm, and 1 mm, were produced using a 3D printer from acrylic teeth. Laminate veneers of these thicknesses were milled from pre-sintered monolithic zirconia (3rd generation) and lithium disilicate blocks. The intaglio surface of MZLV was treated with air abrasion using 110 µm diameter silica-modified aluminium oxide particles and ceramic primer, while LDLV was etched with etchant gel and treated with the ceramic primer before cementation with resin cement. Vertical marginal discrepancy (VMD) was assessed using a stereomicroscope, and a load-to-failure test was conducted using a universal testing machine. Failure modes were evaluated macroscopically on fractured surfaces. Data were analysed statistically using Two-way ANOVA and Bonferroni correction (α = 0.05). RESULTS: LDLV samples exhibited significantly larger VMD compared to MZLV samples across all thicknesses, especially in cervical, palatal, and mean data. Within the LDLV group, load-to-fracture values for 0.7 mm and 1.0 mm thicknesses were similar, whereas for 0.5 mm thickness, it was significantly lower. In the MZLV group, load-to-fracture values were lower for 0.7 mm and 1.0 mm thicknesses compared to LDLV, but higher for 0.5 mm thickness. CONCLUSIONS: Material choice and restoration thickness significantly influence laminate veneer restorations' success. MZLV generally exhibits superior vertical marginal fit compared to LDLV, with varying load-to-failure values across different thicknesses. Clinical management of debonding in MZLV is simpler compared to restoration fracture in LDLV. CLINICAL RELEVANCE: Considering clinical factors, MZLV may be a preferable option to LDLV for this restoration with the thickness of 0.5 mm.
Asunto(s)
Adaptación Marginal Dental , Porcelana Dental , Coronas con Frente Estético , Circonio , Porcelana Dental/química , Circonio/química , Humanos , Ensayo de Materiales , Análisis del Estrés Dental , Fracaso de la Restauración Dental , Propiedades de Superficie , Materiales Dentales/química , Diseño de Prótesis DentalRESUMEN
Multilayer monolithic zirconia, which incorporates polychromatic layers that mimic natural tooth gradients, offers enhanced aesthetics and functionality while reducing debonding risks and improving fabrication efficiency. However, uncertainties remain regarding the fracture characteristics of multilayer monolithic zirconia crowns under occlusal loading, whether composed of uniform or combined yttria levels. The current study investigated how variations in yttria levels and thicknesses affected the optical properties and fracture loads of multilayer monolithic zirconia. Samples of multilayer monolithic zirconia in the Vita A1 shade were used, while employing 3Y (SZ) and 4Y + 5Y (AZ) yttria levels. The optical properties, including the color difference (ΔEWS) and translucency parameters (TP00), were measured using a digital colorimeter. The fracture loads were analyzed using a universal testing machine, and fractured surfaces were examined under a stereomicroscope. Statistical analyses assessed the impacts of the yttria levels and sample thicknesses on the optical properties. The ΔEWS values of SZ ranged 3.6 to 4.0, while for AZ, ΔEWS at 0.5 mm was 3.9 and <2.6 for other thicknesses. The TP00 values decreased with an increased thickness, with AZ generally exhibiting greater translucency than SZ. In the fracture load investigations, SZ (>1600 N) generally exceeded AZ (>1260 N), with fracture loads notably increasing with thickness, particularly for premolars (SZ > 3270 N, AZ > 2257 N). SZ predominantly exhibited partial and complete fractures, whereas AZ showed fewer non-fracture categorizations. Complete fractures began with dense, irregular cracks that extended outward to reveal smooth surfaces, while premolars subjected to higher loads exhibited concentric ripple-like structures. Partial fractures revealed radial textures indicative of areas of stress concentration. In summary, higher yttria levels were correlated with increased translucency, while variations in the fracture loads primarily stemmed from differences in the tooth position or thickness. Overall, multilayer monolithic zirconia incorporating combined yttria levels of 4Y + 5Y (AZ) offered high translucency, precise color matching, and substantial fracture resistance, rendering it highly suitable for aesthetic and functional dental applications.
RESUMEN
Background In light of the trend of using zirconia crowns, clinicians will likely face abutment included in removable partial dentures (RPD) designs with existing zirconia. However, the decision to replace the existing crown with a surveyed crown or modify the existing crown to accept the RPD is unclear. To the best of our knowledge, there is a lack of literature on the effect of preparing a rest seat on the existing monolithic zirconia crown in the patient's mouth on the fracture resistance of the crown. Therefore, in this study, we aimed to evaluate the fracture resistance of computer-aided design/computer-aided manufacturing (CAD/CAM) zirconia surveyed crowns with digitally designed rest seats and hand-modified rest seats. Methods Thirty CAD/CAM zirconia surveyed crowns were digitally designed and fabricated and divided into groups (n=10 per group) as follows: Group 1 comprised surveyed crowns with no occlusal rest seat; Group 2 comprised surveyed crowns with a digitally designed mesial rest seat; and Group 3 comprised surveyed crowns with a hand-modified mesial rest seat. Then, with all the crowns cemented to metal dies, the specimens were subjected to a fracture resistance test using a universal testing machine (Model 8501 Instron, Norwood, MA, USA). Results Surveyed crowns without any rest seat and those with digitally created and hand-modified rest seats displayed different fracture resistances: crowns with no rest seat offered the highest fracture resistance (5831 ± 895.15 N), followed by those with a digitally designed and milled rest seat (5280 ± 1673.33 N). Crowns with a hand-modified rest seat provided the lowest fracture resistance (4976 ± 322.5 N). Based on our results, surveyed crowns without a rest seat displayed higher fracture resistance than those with a rest seat. Conclusion The fracture resistance of crowns with a digitally designed and milled rest seat was statistically similar to that of control crowns with no rest seat, whereas hand-modified rest seats significantly reduced the fracture resistance of surveyed zirconia crowns.
RESUMEN
This study compared the effects of two surface preparation methods on two types of zirconia. Immediately prior to the placement of a monolithic zirconia crown, its morphology may be modified using a rotary cutting instrument for occlusal adjustments. The crown surface is scratched during the grinding process and, thus, requires polishing. Simplified zirconia crowns of 3Y and 5Y were fabricated and used as specimens. The surface roughness and gloss of the occlusal surfaces of specimens were measured and compared when a polishing compound was used after polishing points and when a silica-based coating was sintered. No significant differences were observed in surface roughness between 3Y and 5Y zirconia. The use of polishing compounds was effective because polishing points alone only resulted in a level of surface roughness that may cause wear on antagonist teeth. Although the silica-based coating improved surface properties, the polishing compound more effectively improved surface roughness.
RESUMEN
Introduction The main reason veneered zirconia restorations fail is due to porcelain veneer chipping. This chipping usually starts from wear marks on the chewing surface. As a result, small cracks under the contact area can grow into larger ones across the veneer layer. The veneer ceramic layer is more vulnerable to fractures because it has lower toughness and slightly lower stiffness compared to the base framework material. Thus, even when there's significant chipping, the main framework material usually stays protected with a thin layer of veneer ceramic on top. The aim of this in vitro study is to compare the edge strength of Monolithic Zirconia Crowns with that of Indirect Composite Layered Zirconia Crowns without aging. Materials and methods This research involved creating 12 hand-layered all-ceramic crowns and 12 indirect composite layered zirconia crowns. The sample size was determined using a G*Power calculation (Heinrich-Heine-Universität Düsseldorf, Düsseldorf, Germany). The zirconia frameworks (Upcera HT White; UPCERA Dental America Inc., Cerritos, CA, US) were milled and sintered following the manufacturer's instructions. For the all-ceramic group, veneering porcelain (e.max Ceram; Ivoclar Vivadent, Schaan, Liechtenstein) was hand-applied. In contrast, the indirect composite group utilized Ceramage (Shofu, Kyoto, Japan). An Instron 4501 universal testing machine (Instron Corp., Canton, MA, USA) was employed for the edge chipping tests, and a Vickers indenter (Shanghai Toyo Diamond Tools Co., LTD, Shanghai, China) was used to apply the load. The mean value for edge chipping was analyzed using an unpaired t-test with IBM SPSS Statistics for Windows, Version 26 (Released 2019; IBM Corp., Armonk, NY, USA). The normality of the data was confirmed, and statistical significance was set at 0.05. Results Monolithic Zirconia Crowns (Group 1) require significantly more force (mean: 405 N) to induce an edge chip compared to Indirect Composite Layered Zirconia Crowns (Group 2) (mean: 300 N). The 95% confidence interval (83.43261 N to 109.90072 N) confirms the statistical significance of this difference. Conclusion In conclusion, when evaluating restorative materials based on both esthetic and functional criteria, monolithic zirconia stands out due to its combination of strength, esthetic potential, biocompatibility, and versatility.
RESUMEN
Increasing demand for adult orthodontic treatment using clear aligners has highlighted challenges in bonding clear aligner attachments to various restorations. Specifically, the bond strength of clear aligner attachments to glazed monolithic zirconia has not been extensively studied. This study aims to compare the shear bond strength (SBS) and mode of failure (MOF) of conventional bonding methods versus Superbond C&B (4-META/MMA-TBB resin cement) for clear aligner attachments on glazed monolithic zirconia. Fifty sintered and glazed zirconia samples were divided into five groups and attached with clear aligner attachments: Si (silane), B (bonding agent), SiB (bonding agent and silane), SU (Superbond C&B), and SiSU (silane and Superbond C&B). SBS and MOF of these samples were analyzed. Results indicated a significant difference in bond strength among the groups. SiSU exhibited the highest bond strength, followed by SU, while B had the lowest bond strength. SEM analysis revealed that SiSU and SU predominantly exhibited mixed failure, indicating high bond strength without affecting the glazed layers of the zirconia. In contrast, B exhibited only adhesive failure at the interface, resulting in insufficient bond strength for effective orthodontic treatment. In conclusion, using 4-META/MMA-TBB resin cement provides high bond strength for clear aligner attachments on glazed zirconia with minimal material damage during debonding.
RESUMEN
BACKGROUND: The translucency of different zirconia generations at each time point after thermocycling aging is still lacking. METHODS: Four zirconia materials were used with a total of 60 samples produced from monolithic third generation (5Y) 5 mol% yttria-stabilized zirconia polycrystalline ceramic and fourth generation zirconia (4Y) 4 mol% yttria-stabilized zirconia polycrystalline ceramic, represented by [group1:[CM-5Y] Ceramill Zolid fx (3rd generation zirconia) (Amann Girrbach, Koblach, Austria), group 2:[CM-4Y] Ceramill Zolid HT + (4th generation zirconia) (Amann Girrbach, Koblach, Austria), group 3:[CC-5Y] Cercon XT/ML (Dentsply Sirona, Germany) (3rd generation), and group 4:[CC-4Y] Cercon HT/ML (Dentsply Sirona, Germany) (4th generation)]. The L*a*b* figures were measured by using a spectrophotometer at baseline and after 10,000, 30,000, and 50,000 cycles of thermocycling. At each interval, the translucency of the samples was estimated by using the translucency formula CIEDE2000. The Scheffe post-hoc compared differences among each of the four materials. The Repeated measures ANOVA tested the differences between the materials at each of the different thermocycling intervals (p < .001). Data analyses were evaluated at a significance level of p < .05 (CI 95%). RESULTS: Two-way ANOVA revealed that at baseline the third and fourth generation's zirconia showed statistically significant differences in translucency (P < .001). Translucency values at baseline and after thermocycling exhibited statistically significant changes (p = .003). At each of the time interval; CM-4Y had the highest translucency values followed by CM-5Y, CC-4Y and CC-5Y had the least translucency values. CONCLUSIONS: The third and fourth generations of zirconia displayed different translucencies. Thermocycling affected the translucency of both third and fourth generations of zirconia. At each of the time intervals group 2:[CM-4Y] had the highest TP followed by group1:[CM-5Y], while, group 3:[CC-5Y] and group 4:[CC-4Y] had the least TP.
Asunto(s)
Ensayo de Materiales , Circonio , Circonio/química , Factores de Tiempo , Itrio/química , Espectrofotometría , Materiales Dentales/química , Luz , Propiedades de Superficie , Color , Temperatura , Humanos , Porcelana Dental/químicaRESUMEN
OBJECTIVES: The present study aimed to evaluate the trueness and precision of monolithic zirconia crowns (MZCs) fabricated by 3D printing and milling techniques. METHODS: A premolar crown was designed after scanning a prepared typodont. Twenty MZCs were fabricated using milling and 3D-printing techniques (n = 10). All the specimens were scanned with an industrial scanner, and the scanned data were analyzed using 3D measurement software to evaluate the trueness and precision of each group. Root mean square (RMS) deviations were measured and statistically analyzed (One-way ANOVA, Tukey's, p ≤ 0.05). RESULTS: The trueness of the printed MZC group (140 ± 14 µm) showed a significantly higher RMS value compared to the milled MZCs (96 ± 27 µm,p < 0.001). At the same time, the precision of the milled MZCs (61 ± 17 µm) showed a significantly higher RMS value compared to that of the printed MZCs (31 ± 5 µm,p < 0.001). CONCLUSIONS: The Fabrication techniques had a significant impact on the accuracy of the MZCs. Milled MZCs showed the highest trueness, while printed MZCs showed the highest precision. All the results were within the clinically acceptable error values. CLINICAL SIGNIFICANCE: Although the trueness of the milled MZCs is higher, the manufacturing accuracy of the 3D-printed MZCs showed clinically acceptable results in terms of trueness and precision. However, additional clinical studies are recommended. Furthermore, the volumetric changes of the material should be considered.
Asunto(s)
Diseño Asistido por Computadora , Coronas , Diseño de Prótesis Dental , Impresión Tridimensional , Circonio , Circonio/química , Humanos , Diseño de Prótesis Dental/métodos , Materiales Dentales/química , Diente Premolar , Propiedades de Superficie , Ensayo de MaterialesRESUMEN
In order to effectively address challenges related to anterior teeth restoration and achieve natural-looking results, considerations such as shape, size, gingival contour, and color are crucial. Due to an increasing desire for visually appealing alternatives that are free of metal, materials such as dental zirconia have become popular because of their superior aesthetics and mechanical characteristics. This case report presents clinical insights into anterior teeth rehabilitation with the use of layered zirconia fixed dental prostheses. It delves into the experiences associated with zirconia dental restorations on both endodontically treated and vital abutments, aiming to discern how various factors influence treatment outcomes. Beginning with the design of the restoration, its intricacies significantly impact its fit, strength, and overall durability. Moreover, the composition of zirconia used plays a pivotal role, as different formulations offer varying degrees of mechanical properties, influencing factors such as resilience and wear resistance. The shade selection is also scrutinized, as it directly affects the restoration's aesthetic integration with surrounding natural teeth, contributing to a more harmonious smile. Furthermore, the layering technique employed, particularly when additional porcelain or ceramic layers are applied, is essential for both cosmetic enhancement and structural integrity. Lastly, considerations of occlusion are paramount, ensuring proper alignment and contact between teeth to prevent premature wear and discomfort. By exploring these facets in zirconia restorations across different abutment types, this inquiry seeks to illuminate best practices for achieving favorable treatment outcomes in dental restoration procedures. The choice of zirconia composition, framework design, and shade must be carefully tailored to suit the characteristics of each individual abutment. This emphasizes the significance of adopting a tailored approach to tackle the distinct challenges posed by every clinical scenario. The manuscript provides detailed observations from a clinical case involving the restoration of anterior teeth utilizing monolithic zirconia-fixed dental prostheses. Through a combination of root canal treatment and composite buildup, successful restoration was achieved, with meticulous attention paid to aesthetic considerations. The utilization of computer-aided designing/computer-aided manufacturing (CAD/CAM) technology in crafting zirconia restorations ensured precise fit and superior biocompatibility, contributing to the overall success of the treatment. The study underscores the importance of personalized treatment strategies in achieving optimal outcomes in anterior teeth restoration, emphasizing the need for careful consideration of various factors such as design, composition, and shade selection. Overall, the findings shed light on the potential of zirconia-based restorations in addressing the unique challenges associated with anterior teeth rehabilitation, offering valuable insights for dental practitioners striving to deliver aesthetically pleasing and functionally sound outcomes for their patients.
RESUMEN
OBJECTIVE: The purpose of this systematic review and meta-analysis was to evaluate the accuracy (trueness and precision), marginal and internal adaptation, and margin quality of zirconia crowns made by additive manufacturing compared to subtractive manufacturing technology. METHODS: The investigation adhered to the PRISMA-ScR guidelines for systematic reviews and was registered at the Prospero database (n°CRD42023452927). Four electronic databases, including PubMed, Scopus, Embase, and Web of Science and manual search was conducted to find relevant studies published until September 2023. In vitro studies that assessed the trueness and precision, marginal and internal adaptation, and margin quality of printed crowns compared to milled ones were included. Studies on crowns over implants, pontics, temporary restorations, laminates, or exclusively experimental materials were excluded. RESULTS: A total of 9 studies were included in the descriptive reporting and 7 for meta-analysis. The global meta-analysis of the trueness (P<0.74,I2=90 %) and the margin quality (P<0.61,I2=0 %) indicated no significant difference between the root mean square of printed and milled zirconia crowns. The subgroup analysis for the printing system showed a significant effect (P<0.01). The meta-analysis of the crown areas indicated no significant difference in most of the areas, except for the marginal (favoring milled crowns) and axial (favoring printed crowns) areas. For precision and adaptation, both methods showed a clinically acceptable level. CONCLUSIONS: Additive manufacturing technology produces crowns with trueness and margin quality comparable to subtractive manufacturing. Both techniques have demonstrated the ability to produce crowns with precision levels, internal discrepancy, and marginal fit within clinically acceptable limits. CLINICAL SIGNIFICANCE: 3D printing emerges as a promising and potentially applicable alternative method for manufacturing zirconia crowns, as it shows trueness and margin quality comparable to restorations produced by the subtractive method.
Asunto(s)
Coronas , Adaptación Marginal Dental , Diseño de Prótesis Dental , Impresión Tridimensional , Circonio , Circonio/química , Humanos , Diseño de Prótesis Dental/métodos , Diseño Asistido por Computadora , Materiales Dentales/químicaRESUMEN
To investigate how patterns generated by femtosecond (fs) laser and femtosecond laser power affect the surface roughness (Ra) and biaxial flexural strength (BFS) of monolithic zirconia. Eighty disk-shaped zirconia specimens were divided into eight subgroups (n = 10): Control (C), airborne-particle abrasion (APA), 400 mW fs laser (spiral [SP(400)], square [SQ(400)], circular [CI(400)]), and 700 mW fs laser ([SP(700)], [SQ(700)], [CI(700)]). Ra values were calculated by using a surface profilometer. One additional specimen per group was analyzed with scanning electron microscopy and x-ray diffractometry. BFS values were obtained by using the piston-on-3-ball test. One-way ANOVA and either Tukey's HSD (BFS) or Tamhane's T2 (Ra) tests were used to evaluate data (α = 0.05). Regardless of the pattern and power, fs laser groups had higher Ra than C and APA, while SP groups had lower Ra than CI and SQ groups (p ≤ 0.004). For each pattern, Ra increased with higher laser power (p < 0.001), while the laser power did not affect the BFS (p ≥ 0.793). CI and SQ groups had lower BFS than the other groups (p ≤ 0.040), whereas SP groups had similar BFS to C and APA (p ≥ 0.430). Fs laser microstructuring with spiral surface pattern increased the Ra without jeopardizing the BFS of zirconia. Thus, this treatment might be an option to roughen tested zirconia.
Asunto(s)
Rayos Láser , Ensayo de Materiales , Propiedades de Superficie , Circonio , Circonio/química , Resistencia Flexional , Microscopía Electrónica de RastreoRESUMEN
PURPOSE: The aim of the current study was to evaluate the effect of simulated gastric acid on the color and translucency of different indirect restorative materials. MATERIALS AND METHODS: A total of 36 disc-shaped samples were cut by using an isomet saw and divided into four equal groups (n = 9) according to the material type: Group Z: translucent zirconia (Ceramill® Zolid ht.+ preshade, Amann Girrbach, Koblach, Austria); Group E: lithium disilicate (IPS e.max CAD, Ivoclar Vivadent AG, Schaan, Liechtenstein); Group C: resin nanoceramic (Cerasmart, GC, Tokyo, Japan); Group P: polyether ether ketone (PEEK) (Bettin Zirconia Dentale Italy) veneered with indirect high impact polymer composite (HIPC) (breCAM HIPC, Bredent GmbH & Co. KG, Germany). The samples were immersed in simulated gastric acid (HCl, pH 1.2) for 96 hours at 37 °C in an incubator. The color change (ΔE00) and translucency (RTP00) were measured every 9.6 hours (one-year clinical simulation) of immersion in simulated gastric acid. RESULTS: For color change (∆E00) and translucency (RTP00) among the tested materials, there was a highly statistically significant difference (P < 0.001) after every year of follow-up. The color change in both Z and G groups was the lowest after 1 year of acid immersion, followed by that in group H, and the highest change in color was recorded in group P. CONCLUSION: High translucent zirconia is recommended in patients who are concerned about esthetic, especially with acidic oral environment.
Asunto(s)
Cerámica , Materiales Dentales , Humanos , Ensayo de Materiales , Circonio , Propiedades de Superficie , Color , Diseño Asistido por ComputadoraRESUMEN
Background/purpose: Translucent monolithic zirconia restorations have recently introduced. The purpose of this study was to evaluate the clinical behavior and the survival rate of the posterior third-generation monolithic zirconia crowns (MZCs) during three years of clinical service. Materials and methods: Twenty-four patients who needed thirty crowns were enrolled in this study. Digital impressions were made, and the crowns were milled and cemented with a resin cement. The crowns outcomes were assessed using the California Dental Association's (CDA) criteria. Gingival index (GI), plaque index (PI), and periodontal probing depth (PPD) for MZCs and contralateral natural teeth (control) were assessed. Margin index (MI) for MZCs was also assessed. Data analysis was conducted using the Wilcoxon signed-rank and the Friedman tests. Results: The 3-year survival rate was 100%. All MZCs were rated as satisfactory throughout the follow-up period, and no biological or mechanical complications were observed. No differences were recorded when GI, PI and PPD at 3-year of follow-up were compared to baseline. No differences were recorded between crowned and control teeth. The MI remained stable throughout the study period. Conclusion: The third-generation monolithic zirconia appears to be a good treatment option for the rehabilitation of posterior single teeth.
RESUMEN
OBJECTIVES: Multilayer monolithic zirconia (M-Zr) crowns can be engineered to achieve gradational translucency and color intensity. However, this modification may compromise the mechanical strength, raising concerns regarding the ability of M-Zr crowns to withstand occlusal stresses. The effects of M-Zr crown thickness on translucency and ability to endure occlusal forces were investigated at different tooth positions (incisors, premolars, and molars). The objective was to determine the minimal thickness of M-Zr crowns used in tooth preparation to meet aesthetic and functional demands. METHODS: M-Zr samples (Vita A1) with four thicknesses (0.5, 1.0, 1.5, and 2.0 mm) were prepared and subjected to translucency testing using a digital colorimeter by 3-third and 9-square division methods. Crown-shaped M-Zr samples with three thicknesses (1.0, 1.5, and 2.0 mm) and three tooth positions (incisor, premolar, and molar) were digitally designed, and 2.0 mm metal abutments were fabricated. The samples were bonded to the abutments; their fracture characteristics were evaluated using a universal testing machine, and their fracture surfaces examined using an optical microscope. Statistical analyses included the Shapiro-Wilk test, Pearson correlation, and one-way and two-way ANOVA with a post hoc Tukey HSD test (α = 0.05). RESULTS: Color analysis results revealed a significant negative correlation between thickness and translucency (r < -0.96, P < 0.01), with the highest values in the incisal region. Cross-sectional profiles confirmed the uniform thickness and morphology of the digitally designed M-Zr crowns. The results of fracture strength analysis showed position-dependent variability, a strong positive correlation with thickness (r > 0.96, P < 0.01), and fracture strengths consistently exceeding 1200 N across all tooth positions. Fracture patterns indicated that thinner crowns at the incisors and molars were more prone to cracking, whereas those at the premolars demonstrated significantly higher strength (4872.51 N, P < 0.05), only with crack or even no fracture occurring at 2.0 mm. CONCLUSIONS: Thickness significantly influenced both the translucency and fracture strength of M-Zr, with the tooth position playing an additional role, albeit to a lesser extent. Although thinner crowns exhibited lower strength at each tooth position, even at a thickness of 1.0 mm, fracture strength exceeding 1200 N was maintained, surpassing the typical occlusal forces. Thus, it can be asserted that M-Zr crowns with a minimum thickness of 1.0 mm can meet both aesthetic and functional requirements.
Asunto(s)
Diente Premolar , Coronas , Materiales Dentales , Diseño de Prótesis Dental , Ensayo de Materiales , Circonio , Circonio/química , Humanos , Materiales Dentales/química , Propiedades de Superficie , Diente Molar , Análisis del Estrés Dental , Fracaso de la Restauración Dental , Color , Pilares Dentales , Fuerza de la Mordida , Incisivo , Porcelana Dental/química , Estrés MecánicoRESUMEN
BACKGROUND: Recent forms of translucent zirconia material have been developed, offering a wide range of options and varieties for enhancing aesthetics, making it a preferred choice in the field of prosthetic dentistry. However, there is insufficient understanding regarding the recent types of zirconia materials and their optical behavior. Understanding the variables that influence the translucency of zirconia and identifying strategies to enhance its esthetics are crucial. PURPOSE: The current systemic review highlights a comprehensive understanding of different zirconia generations in relation to their optical characteristics and evaluates material-related variables affecting their translucency. METHODS: The present review studied in-vitro studies that evaluated the optical characteristics of different yttria content of yttria stabilized materials. The topics explored were: (1) the different zirconia material generations and their optical behavior; (2) material-related factors that affect their translucency. The research was restricted to online publication in the English language from July 1, 2010, to July 31, 2023, using PubMed, Scopus, and Science Direct resources. The search key terms and their combinations were "zirconia," "translucent zirconia," "cubic zirconia," "highly translucent zirconia," "yttria partially stabilized zirconia," "monolithic zirconia," "translucency," "optical properties," and "light transmission." RESULTS: The data obtained from fifty-three studies addressed the optical characteristics of various zirconia generations. They reported that changing yttria content had a significant impact on translucency. Different kinds of zirconia ceramics of the same generation have varying translucencies. Achieving optimum aesthetics with monolithic zirconia is challenging due to factors related to material aspects such as the presence of additives, point defects, microstructure, thickness, phase distribution, and sintering conditions. CONCLUSIONS: Newly developed monolithic dental zirconia ceramics have improved aesthetics and translucency. However, additional research is necessary to evaluate their performance and long-term durability. TRIAL REGISTRATION: This systematic review was registered in PROSPERO, under number CRD42023474482.
Asunto(s)
Cerámica , Lenguaje , Itrio , Circonio , ProstodonciaRESUMEN
PURPOSE: To evaluate the metameric disparities among monolithic zirconia materials with differing yttrium compositions across various lighting conditions. MATERIALS AND METHODS: Thirty-six square-shaped zirconia samples measuring 10 × 10 × 0.5 mm were prepared from monolithic zirconia materials with three different yttrium contents. A 0.2 mm thick layer of polymerized dual-polymerizable self-adhesive resin cement was created using a silicone mold with the same dimensions as the prepared zirconia specimens. To evaluate metamerism, color measurements were conducted using a spectrophotometer device on a neutral gray background in a color measurement cabinet that offers four different illumination environments. All samples underwent aging by subjecting them to 10000 thermal cycles using a thermal cycle tester. Following thermal aging, color measurements were taken once more, and the data were recorded using the CIE L*, a*, b* color system. Two-way ANOVA and Post-hoc Bonferroni tests were employed to analyze the data. RESULTS: It was observed that there was no statistical difference among the color measurements made in different illumination environments of the monolithic zirconia ceramics used to evaluate metamerism (P > .05). This observation remained consistent both before and after thermal aging. After thermal aging, the color of monolithic zirconia materials exhibited a tendency towards red and yellow hues, accompanied by a decrease in brightness levels. CONCLUSION: It can be stated that different illumination conditions did not affect the metamerism of monolithic zirconia materials, but there was a color change in monolithic zirconia materials after a thermal aging period equivalent to one year.
RESUMEN
OBJECTIVES: To evaluate how various tooth preparation designs impact the adaptation-both at the margins and internally-and the retentive strength of computer-aided design and computer-aided manufacturing (CAD/CAM) produced endocrowns. MATERIALS AND METHODS: 60 extracted human mandibular first molars were endodontically treated and assigned into three groups (n = 20) according to the tooth preparation design: Group N: butt joint design, Group F and F1 received 1- and 2-mm circumferential ferrule preparation, respectively. Endocrowns were milled using either lithium disilicate glass-ceramic (IPS emax ceramic) or monolithic zirconia. The internal and marginal adaptation of the endocrowns were evaluated using the replica technique. After cementation, the endocrowns of all test groups were dislodged axially at 0.5 mm/min using a universal testing machine. A 2-way ANOVA and the independent samples t-test (α = .05) were performed to statistically analyze the data. RESULTS: The effect of changing the design of the tooth preparation (butt joint, ferrule) on the marginal and internal gap was shown to be statistically significant (p < .05); the lower gap values were recorded at the axial followed by cervical, marginal, and pulpal floor walls in both ceramic groups regardless of the teeth preparation design. The ANOVA test revealed similar average removal forces and stresses for the two types of tested ceramic materials. CONCLUSION: IPS emax ceramic adapted better than monolithic zirconia ceramic, regardless of the preparation design. Ferrule preparation design is more retentive than butt joint preparation, regardless of the type of ceramic material used.
Asunto(s)
Coronas , Diseño de Prótesis Dental , Circonio , Humanos , Diseño de Prótesis Dental/métodos , Ensayo de Materiales , Cerámica , Preparación del Diente , Diseño Asistido por ComputadoraRESUMEN
OBJECTIVES: The aim of this study was to compare failure load and initial damage in monolithic, partially veneered, and completely veneered (translucent) zirconia cantilevered fixed partial dentures (CFPDs), as well as completely veneered metal-ceramic CFPDs under different support and loading configurations. MATERIALS AND METHODS: Eight test groups with anatomically congruent CFPDs (n = 8/group) were fabricated, differing in CFPD material/support structure/loading direction (load applied via steel ball (Ø 6 mm) 3 mm from the distal end of the pontic for axial loading with a 2-point contact on the inner cusp ridges of the buccal and oral cusps and 1.3 mm below the oral cusp tip for 30° oblique loading): (1) monolithic zirconia/CoCr abutment teeth/axial, (2) monolithic zirconia/CoCr abutment teeth/oblique, (3) partially veneered zirconia/CoCr abutment teeth/axial, (4) partially veneered zirconia/CoCr abutment teeth/oblique, (5) completely veneered zirconia/CoCr abutment teeth/axial, (6) completely veneered CoCr/CoCr abutment teeth/axial (control group), (7) partially veneered zirconia/implants/axial, and (8) partially veneered zirconia/natural teeth/axial. Restorations were artificially aged before failure testing. Statistical analysis was conducted using one-way ANOVA and Tukey post hoc tests. RESULTS: Mean failure loads ranged from 392 N (group 8) to 1181 N (group 1). Axially loaded monolithic zirconia CFPDs (group 1) and controls (group 6) showed significantly higher failure loads. Oblique loading significantly reduced failure loads for monolithic zirconia CFPDs (group 2). Initial damage was observed in all groups except monolithic zirconia groups, and fractography revealed design flaws (sharp edges at the occlusal boundary of the veneering window) in partially veneered zirconia CFPDs. CONCLUSIONS: Monolithic zirconia CFPDs might be a viable alternative to completely veneered CoCr CFPDs in terms of fracture load. However, oblique loading of monolithic zirconia CFPDs should be avoided in clinical scenarios. Design improvements are required for partially veneered zirconia CFPDs to enhance their load-bearing capacity. CLINICAL RELEVANCE: Monolithic zirconia may represent a viable all-ceramic alternative to the established metal-ceramic option for CFPD fabrication. However, in daily clinical practice, careful occlusal adjustment and regular monitoring should ensure that oblique loading of the cantilever is avoided.
Asunto(s)
Cerámica , Fracaso de la Restauración Dental , Circonio , Dentadura Parcial Fija , Porcelana Dental , Ensayo de Materiales , Análisis del Estrés Dental , CoronasRESUMEN
The aim was to compare the effect of different endodontic surgical treatments on the stress distributions in dentin of a simulated first mandibular molar tooth using the finite element analysis method. Three surgical endodontic procedures (apical resection, root amputation, and hemisection) were simulated in a first mandibular molar. Biodentine or mineral-trioxide-aggregate was used to repair the surgery site in apical resection and root amputation models; the remaining root canal spaces were filled with gutta-percha. Access cavities were restored using resin composite. In hemisection model, root canal was filled with gutta-percha, and coronal restoration was finished with a monolithic zirconia crown. A sound tooth model was created as a control model. An oblique force of 300 N angled at 45° to the occlusal plane was simulated. Maximum von Mises stresses were evaluated in dentin near the surgery regions and the entire tooth. Apical resection/Biodentine and apical resection/mineral-trioxide-aggregate models generated maximum von Mises stresses of 39.001 MPa and 39.106 MPa, respectively. The recorded maximum von Mises stresses in root amputation models were 66.491 MPa for root amputation/Biodentine and 73.063 MPa for root amputation/mineral-trioxide-aggregate models. The highest maximum von Mises stress value among all models was observed in the hemisection model, measuring 138.87 MPa. Hemisection induced the highest von Mises stresses in dentin, followed by root amputation and apical resection. In apical resection, Biodentine and mineral-trioxide-aggregate did not show a significant difference in stress distribution. Biodentine in root amputation may lead to lower stresses compared to mineral-trioxide-aggregate.
Asunto(s)
Compuestos de Calcio , Análisis del Estrés Dental , Dentina , Análisis de Elementos Finitos , Diente Molar , Óxidos , Silicatos , Humanos , Diente Molar/cirugía , Compuestos de Aluminio , Materiales de Obturación del Conducto Radicular , Mandíbula/cirugía , Gutapercha , Circonio , Raíz del Diente/cirugía , Combinación de MedicamentosRESUMEN
OBJECTIVE: This article highlights a CAD/CAM complete-mouth rehabilitation in an 82-year-old patient by means of a complete maxillary prosthesis and mandibular implant- and tooth-supported fixed restorations made from multilayered zirconia. CLINICAL CONSIDERATIONS: Comprehensive complete-mouth rehabilitations in elderly patients with adaptation of the occlusal vertical dimension (OVD) often present particular challenges. This applies especially when exacting functional and esthetic requirements are to be met and the treatment should not cause the patient too much effort, still ensuring the highest level of quality and efficiency and a low intervention rate. CONCLUSION: The digital approach used for the present patient allowed for an efficient treatment procedure, facilitated virtual evaluations using a face-scan, and enhanced the predictability of the prosthodontic outcome. The approach enabled some steps required in the conventional protocol to be omitted, resulting in a straightforward clinical treatment with minimal strain on the patient. CLINICAL SIGNIFICANCE: Because of the comprehensive recording of extraoral and intraoral data, for example with a facial scanner, it was possible to transfer a digital replica of the patient to the dental laboratory technician. With this protocol, many steps can be performed in the absence of the real patient.