RESUMEN
The objective of this work was to assess the efficacy of different proteolytic agents on the bond strength of pit and fissure sealants to bovine enamel. Eighty-four bovine enamel specimens were randomly assigned in groups according to the pit and fissure sealant applied (HelioSeal F or Dyad Flow). Then, the specimens were subdivided according to the proteolytic agent used (n = 7): Group 1, distilled water (control); Group 2, 10 wt.% Tergazyme®; Group 3, 10 wt.% ZYME®; Group 4, 10% papain gel; Group 5, 10% bromelain gel; and Group 6, 5.25 wt.% sodium hypochlorite. The cell viability of the proteolytic solutions was assessed through the MTT assay. The proteolytic agents were applied on the enamel surface prior to the acid-etching procedure; then, the pit and fissure sealants were placed. The micro-shear bond strength was evaluated after 24 h or 6 months of water storing at 37 °C. Representative SEM images were taken for each experimental group. The bond strength data were statistically analyzed by a three-way ANOVA test using a significance level of α = 0.05. Bromelain and papain proteolytic solutions did not exert any cytotoxic effect on the human dental pulp cells. After 24 h and 6 months of aging, for both pit and fissure sealants, sodium hypochlorite, papain, bromelain, and Tergazyme® achieved statistically significant higher bond strength values (p < 0.05). Irrespective of the deproteinizing agent used, Dyad Flow resulted in a better bond strength after 6 months of aging. The type 1 etching pattern was identified for sodium hypochlorite, papain, and bromelain. Tergazyme®, papain, and bromelain demonstrated efficacy in deproteinizing enamel surfaces prior to acid etching, leading to the improved bond strength of pit and fissure sealants. Clinically, this suggests that these proteolytic agents can be considered viable alternatives to traditional methods for enhancing sealant retention and longevity. Utilizing these agents in dental practice could potentially reduce sealant failures.
RESUMEN
OBJECTIVES: The aim of this systematic review was to critically analyze previously published studies of the effects of dentin surface pretreatment with deproteinizing agents on the bonding of self-etch (SE) adhesives to dentin. Additionally, a meta-analysis was conducted to quantify the effects of the above-mentioned surface pretreatment methods on the bonding of SE adhesives to dentin. MATERIALS AND METHODS: An electronic search was performed using the following databases: Scopus, PubMed and ScienceDirect. The online search was performed using the following keywords: 'dentin' or 'hypochlorous acid' or 'sodium hypochlorite' and 'self-etch adhesive.' The following categories were excluded during the assessment process: non-English articles, randomized clinical trials, case reports, animal studies, and review articles. The reviewed studies were subjected to meta-analysis to quantify the effect of the application time and concentration of sodium hypochlorite (NaOCl) and hypochlorous acid (HOCl) deproteinizing agents on bonding to dentin. RESULTS: Only 9 laboratory studies fit the inclusion criteria of this systematic review. The results of the meta-analysis revealed that the pooled average microtensile bond strength values to dentin pre-treated with deproteinizing agents (15.71 MPa) was significantly lower than those of the non-treated control group (20.94 MPa). CONCLUSIONS: In light of the currently available scientific evidence, dentin surface pretreatment with deproteinizing agents does not enhance the bonding of SE adhesives to dentin. The HOCl deproteinizing agent exhibited minimal adverse effects on bonding to dentin in comparison with NaOCl solutions.
RESUMEN
OBJECTIVES: The aim of this systematic review was to critically analyze previously published studies of the effects of dentin surface pretreatment with deproteinizing agents on the bonding of self-etch (SE) adhesives to dentin. Additionally, a meta-analysis was conducted to quantify the effects of the above-mentioned surface pretreatment methods on the bonding of SE adhesives to dentin. MATERIALS AND METHODS: An electronic search was performed using the following databases: Scopus, PubMed and ScienceDirect. The online search was performed using the following keywords: ‘dentin’ or ‘hypochlorous acid’ or ‘sodium hypochlorite’ and ‘self-etch adhesive.’ The following categories were excluded during the assessment process: non-English articles, randomized clinical trials, case reports, animal studies, and review articles. The reviewed studies were subjected to meta-analysis to quantify the effect of the application time and concentration of sodium hypochlorite (NaOCl) and hypochlorous acid (HOCl) deproteinizing agents on bonding to dentin. RESULTS: Only 9 laboratory studies fit the inclusion criteria of this systematic review. The results of the meta-analysis revealed that the pooled average microtensile bond strength values to dentin pre-treated with deproteinizing agents (15.71 MPa) was significantly lower than those of the non-treated control group (20.94 MPa). CONCLUSIONS: In light of the currently available scientific evidence, dentin surface pretreatment with deproteinizing agents does not enhance the bonding of SE adhesives to dentin. The HOCl deproteinizing agent exhibited minimal adverse effects on bonding to dentin in comparison with NaOCl solutions.