Surface Nanostructuring of a CuAlBe Shape Memory Alloy Produces a 10.3 ± 0.6 GPa Nanohardness Martensite Microstructure.

Severe plastic deformation (SPD) has led to the discovery of ever stronger materials, either by bulk modification or by surface deformation under sliding contact. These processes increase the strength of an alloy through the transformation of the deformation substructure into submicrometric grains or twins. Here, surface SPD was induced by plastic deformation under frictional contact with a spherical tool in a hot rolled CuAlBe-shape memory alloy. This created a microstructure consisting of a few course martensite variants and ultrafine intersecting bands of secondary martensite and/or austenite, increasing the nanohardness of hot-rolled material from 2.6 to 10.3 GPa. In as-cast material the increase was from 2.4 to 5 GPa. The friction coefficient and surface damage were significantly higher in the hot rolled condition. Metallographic evidence showed that hot rolling was not followed by recrystallisation. This means that a remaining dislocation substructure can lock the martensite and impedes back-transformation to austenite. In the as-cast material, a very fine but softer austenite microstructure was found. The observed difference in properties provides an opportunity to fine-tune the process either for optimal wear resistance or for maximum surface hardness. The modified hot-rolled material possesses the highest hardness obtained to date in nanostructured non-ferrous alloys.

Preparation, characterization, and evaluation of compressive strength of polypropylene fiber reinforced geopolymer mortars.

The study of the fiber-matrix interface represents a crucial topic to determine the mechanical performance of geopolymer-based materials reinforced with polypropylene fibers (PPF). This research proposes the use of natural zeolite in the preparation geopolymers mortars through alkaline activation with NaOH, Ca(OH)2 and Na2SiO3, and with river sand as a fine aggregate. PPF were incorporated into the geopolymer-based mortar matrix in different proportions like 0, 0.5, and 1 wt.%. The mortars were cured for 24 h at 60 °C and then aged for six days more at room temperature. All samples analyzed through compressive strength were also characterized by X-ray diffraction, thermal analysis, Infrared Spectroscopy, and scanning electron microscopy techniques. The results indicated that the best mix design among the ones used: NaOH (10 M), Na2SiO3/NaOH = 3, Ca(OH)2 = 1.5 wt.% and PPF = 0.5 wt.%. The optimum mix design showed a compressive strength of 4.63 MPa on average. Besides, the fibers enhanced the compressive strength of those samples which the PP fibers probably have better dispersion inside the matrix of the geopolymer mortar.

Effect of extrapallial protein of Mytilus californianus on the process of in vitro biomineralization of chitosan scaffolds.

Biomineralization is the process by which diverse organisms have the capacity to create heterogeneous accumulations, derived from organic and inorganic compounds that induce the process of mineral formation. An example of this can be seen an extrapallial protein (EP) of Mytilus californianus, which is responsible for carrying out the biomineralization process. In order to determine their ability to perform the biomineralization process, EP protein was absorbed and mixed in chitosan scaffolds which were tested in simulated physiological fluid. The materials were analyzed by FTIR spectroscopy, field emission scanning electron microscopy-energy-dispersive electron X-ray spectroscopy andX-ray diffraction. Results confirmed that the EP protein stimulates the rapid growth of biological apatite on the chitosan scaffolds. The mixing method favored more the apatite growth as well as the formation of second nucleation sites than the immersion method.