RESUMEN
Energy storage materials to modulate indoor microclimates are needed to improve energy efficiency and for human comfort. Of these, phase-change material (PCM) is considered a very useful material because of its excellent latent heat energy storage. For application, some synthetic porous materials for supporting PCM are usually not friendly enough for people and housing environments due to their non-degradation characteristics. Hence, to develop an eco-friendly porous material is needed in order to encapsulate PCM composites that are always expected in indoor applications. In this work, heat-treated bamboo bricks were delignified to provide a delignified bamboo (DB) matrix. A phase-change composite was then fabricated by impregnating DB with polyethylene glycol (PEG) polymer. Impregnation was carried out under wet conditions to ensure the regular arrangement of the DB structure so as to achieve dimensional stability. The final DB/PEG composite was investigated for dimensional stability, load rate, latent heat, and phase-change temperature. Results showed that the DB matrix could be easily impregnated with PEG polymer under wet conditions, and the DB/PEG composite was found to have high enthalpy and a large phase-change temperature interval. Moreover, the composite was found to be a good regulator of indoor temperature and a stable dimension with a snow-white appearance. In summary, this DB/PEG composite is an energy storage material with the potential to modulate ambient indoor temperature and reduce building energy consumption.
RESUMEN
Phase change materials (PCM) have the ability to store latent heat when they change phases, a property that gives clothing that incorporates PCM its cooling effect. This study investigated the effect of dry-heat loss (cooling) of a novel melt-spun PCM fibre on the basis of the area covered, mass, the latent heat of fusion and melting temperature, compared to a known PCM clothing product. PCM fibres with melting temperatures of 28.4 and 32.0°C and PCM packs with melting temperatures of 28.0 and 32.0°C were studied. The results showed that the PCM fibres had a larger initial peak cooling effect than that of the PCM packs. The duration of the cooling effect of PCM fibres was primarily dependent on the PCM mass and the latent heat of fusion capacity, and secondly on the covered area and melting temperature of the PCM. PRACTITIONER SUMMARY: This study investigates the cooling effect of PCM fibres on a thermal manikin. The PCM fibres had a high but short-lasting cooling effect. This study contributes to the knowledge of how the body's temperature regulation may be affected by the cooling properties of clothing that incorporates PCM.