RESUMEN
Grain boundaries (GBs) modulate the macroscopic properties in polycrystalline materials because they have different atomic and electronic structures from the bulk. Despite the progress on the understanding of GB atomic structures, knowledge of the localized electronic band structures is still lacking. Here, we experimentally characterized the atomic structures and the band gaps of four typical GBs in α-Al2O3 by scanning transmission electron microscopy and valence electron energy-loss spectroscopy (EELS). It was found that the band gaps of the GBs are narrowed by 0.5-2.1 eV compared with that of 8.8 eV in the bulk. By combing core-loss EELS with first-principles calculations, we elucidated that the band gap reductions directly correlate with the decrease of the coordination numbers of Al and O ions at the GBs. These results provide in-depth understanding between the local atomic and electronic band structures for GBs and demonstrate a novel electronic-structure analysis for crystalline defects.
RESUMEN
Cutting-edge research on materials for lithium ion batteries regularly focuses on nanoscale and atomic-scale phenomena. Electron energy-loss spectroscopy (EELS) is one of the most powerful ways of characterizing composition and aspects of the electronic structure of battery materials, particularly lithium and the transition metal mixed oxides found in the electrodes. However, the characteristic EELS signal from battery materials is challenging to analyze when there is strong overlap of spectral features, poor signal-to-background ratios, or thicker and uneven sample areas. A potential alternative or complementary approach comes from utilizing the valence EELS features (<20 eV loss) of battery materials. For example, the valence EELS features in LiCoO2 maintain higher jump ratios than the Li-K edge, most notably when spectra are collected with minimal acquisition times or from thick sample regions. EELS maps of these valence features give comparable results to the Li-K edge EELS maps of LiCoO2. With some spectral processing, the valence EELS maps more accurately highlight the morphology and distribution of LiCoO2 than the Li-K edge maps, especially in thicker sample regions. This approach is beneficial for cases where sample thickness or beam sensitivity limit EELS analysis, and could be used to minimize electron dosage and sample damage or contamination.
RESUMEN
The spatial distribution of Li ions in a lithium iron phosphate (Li1-xFePO4) single crystal after chemical delithiation is quantitatively investigated using Fe M2,3-edge and valence electron energy loss (EEL) spectroscopy techniques. Li contents between those of end-member compositions LiFePO4 and FePO4 are found to correspond to reproducible changes in Fe M2,3-edge and valence EEL spectra across an interface between LiFePO4 and FePO4 regions. Quantitative analysis of these changes is used to estimate the local valence states of Fe ions, from which the Li concentration in the intermediate phase can be deduced. The faster recording time for valence EEL spectra than Fe M2,3-edge spectra makes measurement of the former a more efficient and reproducible means of estimating Li distributions.
RESUMEN
Using low beam energies in a (scanning) transmission electron microscope (S/TEM) has numerous advantages over higher beam energies. We discuss the performance of commonly available electron microscopes when being operated at reduced beam energies. Further on, we discuss the merits of low beam energies concerning the determination of the optical properties of Si as well as of buried quantum structures. For this purpose we have aligned a conventional S/TEM and the attached energy loss spectrometer for 13keV and 60keV, respectively. Finally we identify the key parameters for setting up a low voltage electron energy loss spectrometry (EELS) experiment.