A promising poly (e-caprolactone)/graphene-based scaffold as an antibacterial in regenerating bone tissue.

Scaffolds are 3D biomaterials that provide an environment for cell regeneration. In the context of bone remodeling, poly(e-caprolactone) (PCL) combined with graphene has been developed as the scaffold. It is imperative for scaffolds to possess antibacterial properties in order to properly reduce the risk of potential infections.Therefore, this study aims to analyze the antibacterial characteristics of PCL/graphene scaffolds against Staphylococcus aureus (S. aureus) and Porphyromonas gingivalis (P. gingivalis) in vitro. In this study, five different groups were used, including PCL (K-), Amoxicillin (K+), PCL/Graphene 0.5 wt%, PCL/graphene 1 wt% and PCL/Graphene 1.5 wt%. All experiments were performed in triplicates and were repeated three times, and the diffusion method by Kirby-Bauer test was used. The disc was incubated with S. aureus and P. gingivalis for 24 hours and then the diameter of the inhibition zone was measured. The results showed that the PCL/graphene scaffolds exhibited dose-dependent antibacterial activity against S. aureus and P. gingivalis. The inhibition zone diameter (IZD) against S. aureus of PCL/graphene 1 wt% was 9.53 ± 0.74 mm, and increased to 11.93 ± 0.92 mm at a concentration of 1.5 wt% of graphene. The PCL/graphene scaffold with 1.5 wt% exhibited a greater inhibitory effect, with an IZD of 12.56 ± 0.06 mm against P. gingivalis, while the inhibitory activity of the 1 wt% variant was relatively lower at 10.46 ± 0.24 mm. The negative control, PCL, and PCL/graphene 0.5 wt% exhibited no antibacterial activity sequentially (p = 1). Scaffolds of poly(e-caprolactone)/graphene exhibited an antibacterial activity at 1, and 1.5 wt% on S. aureus and P. gingivalis. The antibacterial properties of this scaffold make it a promising candidate for regenerating bone tissue.

Design and simulation of scaffolds with lattice microstructures for bioprinting bone tissue.

BACKGROUND: Tissue engineering seeks to improve, maintain, or replace the biological functions of damaged organs or tissues with biological substitutes such as the development of scaffolds. In the case of bone tissue, they must have excellent mechanical properties like native bone. OBJECTIVE: In this work, three geometric models were designed for scaffolds with different structure lattices and porosity that could be biomechanically suitable and support cell growth for trabecular bone replacement applications in tissue engineering and regenerative medicine to the proximal femur area. METHODS: Geometries were designed using computer-aided design (CAD) software and evaluated using finite element analysis in compression tests. Three loads were considered according to the daily activity: 1177 N for slow walking, 2060 N for fast walking, and 245.25 N for a person in a bipedal position. All these loads for an adult weight of 75 kg. For each of them, three biomaterials were assigned: two polymers (poly-glycolic acid (PGA) and poly-lactic acid (PLA)) and one mineral (hydroxyapatite (HA)). 54 tests were performed: 27 for each of the tests. RESULTS: The results showed Young's modulus (E) between 1 and 4 GPa. CONCLUSION: If the resultant E is in the range of 0.1 to 5 GPa, the biomaterial is considered an appropriate alternative for the trabecular bone which is the main component of the proximal bone. However, for the models applied in this study, the best option is the poly-lactic acid which will allow absorbing the acting loads.

Graphene-enhanced PCL electrospun nanofiber scaffolds for cardiac tissue engineering.

Cardiovascular diseases, particularly myocardial infarction, have significant healthcare challenges due to the limited regenerative capacity of injured heart tissue. Cardiac tissue engineering (CTE) offers a promising approach to repairing myocardial damage using biomaterials that mimic the heart's extracellular matrix. This study investigates the potential of graphene nanopowder (Gnp)-enhanced polycaprolactone (PCL) scaffolds fabricated via electrospinning to improve the properties necessary for effective cardiac repair. This work aimed to analyze scaffolds with varying graphene concentrations (0.5%, 1%, 1.5%, and 2% by weight) to determine their morphological, chemical, mechanical, and biocompatibility characteristics. The results presented that incorporating graphene improves PCL scaffolds' mechanical properties and cellular interactions. The optimal concentration of 1% graphene significantly enhanced mechanical properties and biocompatibility, promoting cell adhesion and proliferation. These findings suggest that Gnp-enhanced PCL scaffolds at this concentration can serve as a potent substrate for CTE providing insights into designing more effective biomaterials for myocardial restoration.

Development of PHBV electrospun fibers containing a borate bioactive glass doped with Co, Cu, and Zn for wound dressings.

Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) nanofibers embedded with borate glasses of 45B5 composition doped with Co2+, Cu2+, and Zn2 +(46.1 B2O326.9-X CaO24.4 Na2O2.6 P2O5, X CoO/CuO/ZnO mol % (X = 0-5)) were produced by electrospinning for wound healing applications. Prior to their addition, the glasses exhibited two broad halos typical of a vitreous borate network, which were mainly composed of ring-type metaborate structural units. The particle distribution in the PHBV nanofibers embedded with 45B5 borate bioactive glasses is present in isolated and agglomerated states, being partially coated by a polymeric layer-except for the cobalt-doped glass, which resulted in a successful encapsulation with 100% embedding efficiency. The incorporation of the glasses reduced the PHBV crystallinity degree and its decomposition temperature, as well as its mechanical properties, including Young's modulus, tensile strength, and elongation at break. The neat PHBV fibers and those containing the cobalt-doped glasses demonstrated great cytocompatibility with human keratinocytes (HaCat), as suggested by the high cell viability after 7 days of exposure. Further studies are needed to fully understand the wound healing potential of these fibers, but our results significantly contribute to the area.

Aloe vera mucilage loaded gelatin electrospun fibers contained in polylactic acid coaxial system and polylactic acid and poly(e-caprolactone) tri-layer membranes for tissue engineering.

BACKGROUND: Polymeric electrospun mats have been used as scaffolds in tissue engineering for the development of novel materials due to its characteristics. The usage of synthetic materials has gone in decline due to environmental problems associated with their synthesis and waste disposal. Biomaterials such as biopolymers have been used recently due to good compatibility on biological applications and sustainability. OBJECTIVE: The purpose of this work is to obtain novel materials based on synthetic and natural polymers for applications on tissue engineering. METHODS: Aloe vera mucilage was obtained, chemically characterized, and used as an active compound contained in electrospun mats. Polymeric scaffolds were obtained in single, coaxial and tri-layer structures, characterized and evaluated in cell culture. RESULTS: Mucilage loaded electrospun fibers showed good compatibility due to formation of hydrogen bonds between polymers and biomolecules from its structure, evidenced by FTIR spectra and thermal properties. Cell viability test showed that most of the obtained mats result on viability higher than 75%, resulting in nontoxic materials, ready to be used on scaffolding applications. CONCLUSION: Mucilage containing fibers resulted on materials with potential use on scaffolding applications due to their mechanical performance and cell viability results.

Development of Bioactive Hybrid Poly(lactic acid)/Poly(methyl methacrylate) (PLA/PMMA) Electrospun Fibers Functionalized with Bioglass Nanoparticles for Bone Tissue Engineering Applications.

Hybrid scaffolds that are based on PLA and PLA/PMMA with 75/25, 50/50, and 25/75 weight ratios and functionalized with 10 wt.% of bioglass nanoparticles (n-BG) were developed using an electrospinning technique with a chloroform/dimethylformamide mixture in a 9:1 ratio for bone tissue engineering applications. Neat PLA and PLA/PMMA hybrid scaffolds were developed successfully through a (CF/DMF) solvent system, obtaining a random fiber deposition that generated a porous structure with pore interconnectivity. However, with the solvent system used, it was not possible to generate fibers in the case of the neat PMMA sample. With the increase in the amount of PMMA in PLA/PMMA ratios, the fiber diameter of hybrid scaffolds decreases, and the defects (beads) in the fiber structure increase; these beads are associated with a nanoparticle agglomeration, that could be related to a low interaction between n-BG and the polymer matrix. The Young's modulus of PLA/PMMA/n-BG decreases by 34 and 80%, indicating more flexible behavior compared to neat PLA. The PLA/PMMA/n-BG scaffolds showed a bioactive property related to the presence of hydroxyapatite crystals in the fiber surface after 28 days of immersion in a Simulated Body Fluids solution (SBF). In addition, the hydrolytic degradation process of PLA/PMMA/n-BG, analyzed after 35 days of immersion in a phosphate-buffered saline solution (PBS), was less than that of the pure PLA. The in vitro analysis using an HBOF-1.19 cell line indicated that the PLA/PMMA/n-BG scaffold showed good cell viability and was able to promote cell proliferation after 7 days. On the other hand, the in vivo biocompatibility evaluated via a subdermal model in BALC male mice corroborated the good behavior of the scaffolds in avoiding the generation of a cytotoxic effect and being able to enhance the healing process, suggesting that the materials are suitable for potential applications in tissue engineering.

Additive manufacturing of bioactive and biodegradable poly (lactic acid)-tricalcium phosphate scaffolds modified with zinc oxide for guided bone tissue repair.

Bioactive and biodegradable scaffolds that mimic the natural extracellular matrix of bone serve as temporary structures to guide new bone tissue growth. In this study, 3D-printed scaffolds composed of poly (lactic acid) (PLA)-tricalcium phosphate (TCP) (90-10 wt.%) were modified with 1%, 5%, and 10 wt.% of ZnO to enhance bone tissue regeneration. A commercial chain extender named Joncryl was incorporated alongside ZnO to ensure the printability of the composites. Filaments were manufactured using a twin-screw extruder and subsequently used to print 3D scaffolds via fused filament fabrication (FFF). The scaffolds exhibited a homogeneous distribution of ZnO and TCP particles, a reproducible structure with 300 µm pores, and mechanical properties suitable for bone tissue engineering, with an elastic modulus around 100 MPa. The addition of ZnO resulted in enhanced surface roughness on the scaffolds, particularly for ZnO microparticles, achieving values up to 241 nm. This rougher topography was responsible for enhancing protein adsorption on the scaffolds, with an increase of up to 85% compared to the PLA-TCP matrix. Biological analyses demonstrated that the presence of ZnO promotes mesenchymal stem cell (MSC) proliferation and differentiation into osteoblasts. Alkaline phosphatase (ALP) activity, an important indicator of early osteogenic differentiation, increased up to 29%. The PLA-TCP composite containing 5% ZnO microparticles exhibited an optimized degradation rate and enhanced bioactivity, indicating its promising potential for bone repair applications.

Electrochemical detection of poly(3-hydroxybutyrate) production from Burkholderia glumae MA13 using a molecularly imprinted polymer-reduced graphene oxide modified electrode.

The development and application of an electrochemical sensor is reported for detection of poly(3-hydroxybutyrate) (P3HB) - a bioplastic derived from agro-industrial residues. To overcome the challenges of molecular imprinting of macromolecules such as P3HB, this study employed methanolysis reaction to break down the P3HB biopolymer chains into methyl 3-hydroxybutyrate (M3HB) monomers. Thereafter, M3HB were employed as the target molecules in the construction of molecularly imprinted sensors. The electrochemical device was then prepared by electropolymerizing a molecularly imprinted poly (indole-3-acetic acid) thin film on a glassy carbon electrode surface modified with reduced graphene oxide (GCE/rGO-MIP) in the presence of M3HB. Electrochemical impedance spectroscopy (EIS), cyclic voltammetry (CV), scanning electron microscopy with field emission gun (SEM-FEG), Raman spectroscopy, attenuated total reflection Fourier-transform infrared (ATR-FTIR) and X-ray Photoelectron Spectroscopy (XPS) were employed to characterize the electrode surface. Under ideal conditions, the MIP sensor exhibited a wide linear working range of 0.1 - 10 nM and a detection limit of 0.3 pM (n = 3). The sensor showed good repeatability, selectivity, and stability over time. For the sensor application, the bioproduction of P3HB was carried out in a bioreactor containing the Burkholderia glumae MA13 strain and sugarcane byproducts as a supplementary carbon source. The analyses were validated through recovery assays, yielding recovery values between 102 and 104%. These results indicate that this MIP sensor can present advantages in the monitoring of P3HB during the bioconversion process.

Lysine grafted poly(lactic acid): An intrinsically antimicrobial polymer.

Nosocomial infections or healthcare-associated infections, normally develops after the healthcare treatment in the hospital. Most of them are caused by infected medical devices. Plastics are the most common materials for manufacturing these devices because of their good processability, sterilization efficacy, ease of handling and harmlessness, however, it usually do not display antimicrobial properties. Here, in order to infer antimicrobial activity to poly(lactic acid), it was modified by maleation, followed by l-lysine grafting to its structure. The chemical modifications were confirmed by FTIR and 1H NMR analysis, indicating the success of the reactions. The antimicrobial activity was tested using Escherichia coli and Staphylococcus aureus and the results showed that the sample was capable of inhibiting about 99 % of the S. aureus growth by contact. The samples cytotoxicity was also tested using the L929 mouse cells and the results indicated no cytotoxic effect. These results indicated the sample antimicrobial potential, without affect the normal eukaryotic cells. In addition, the processability of the modified PLA (PLA-g-Lys) was improved without compromising its mechanical properties, as shown by thermal analysis and tensile tests. Thus, this novel PLA derivative can be seen as a promising material for future applications in the manufacturing of biomedical devices.

Electrospun scaffolds based on a PCL/starch blend reinforced with CaO nanoparticles for bone tissue engineering.

Electrospun nanocomposite scaffolds with improved bioactive and biological properties were fabricated from a blend of polycaprolactone (PCL) and starch, and then combined with 5 wt% of calcium oxide (CaO) nanoparticles sourced from eggshells. SEM analyses showed scaffolds with fibrillar morphology and a three-dimensional structure. The hydrophilicity of scaffolds was improved with starch and CaO nanoparticles, which was evidenced by enhanced water absorption (3500 %) for 7 days. In addition, PCL/Starch/CaO scaffolds exhibited major degradation, with a mass loss of approximately 60 % compared to PCL/Starch and PCL/CaO. The PCL/Starch/CaO scaffolds decreased in crystallinity as intermolecular interactions between the nanoparticles retarded the mobility of the polymeric chains, leading to a significant increase in Young's modulus (ca. 60 %) and a decrease in tensile strength and elongation at break, compared to neat PCL. SEM-EDS, FT-IR, and XRD analyses indicated that PCL/Starch/CaO scaffolds presented a higher biomineralization capacity due to the ability to form hydroxyapatite (HA) in their surface after 28 days. The PCL/Starch/CaO scaffolds showed attractive biological performance, allowing cell adhesion and viability of M3T3-E1 preosteoblastic cells. In vivo analysis using a subdermal dorsal model in Wistar rats showed superior biocompatibility and improved resorption process compared to a pure PCL matrix. This biological analysis suggested that the PCL/Starch/CaO electrospun mats are suitable scaffolds for guiding the regeneration of bone tissue.

Poly-3-hydroxybutyrate-silver nanoparticles membranes as advanced antibiofilm strategies for combatting peri-implantitis.

Dental implant success is threatened by peri-implantitis, an inflammation leading to implant failure. Conventional treatments struggle with the intricate microbial and host factors involved. Antibacterial membranes, acting as barriers and delivering antimicrobials, may offer a promising solution. Thus, this study highlights the potential of developing antibacterial membranes of poly-3-hydroxybutyrate and silver nanoparticles (Ag Nps) to address peri-implantitis challenges, discussing design and efficacy against potential pathogens. Electrospun membranes composed of PHB microfibers and Ag Nps were synthesized in a blend of DMF/chloroform at three different concentrations. Various studies were conducted on the characterization and antimicrobial activity of the membranes. The synthesized Ag Nps ranged from 4 to 8 nm in size. Furthermore, Young's modulus decreased, reducing from 13.308 MPa in PHB membranes without Ag Nps to 0.983 MPa in PHB membranes containing higher concentrations of Ag Nps. This demonstrates that adding Ag Nps results in a less stiff membrane. An increase in elongation at break was noted with the rise in Ag Nps concentration, from 23.597 % in PHB membranes to 60.136 % in PHB membranes loaded with Ag Nps. The antibiotic and antibiofilm activity of the membranes were evaluated against Pseudomonas aeruginosa, Staphylococcus aureus, Streptococcus mutans, and Candida albicans. The results indicated that all PHB membranes containing Ag Nps exhibited potent antibacterial activity by inhibiting the growth of biofilms and planktonic bacteria. However, inhibition of C. albicans occurred only with the PHB-Ag Nps C membrane. These findings emphasize the versatility and potential of Ag Nps-incorporated membranes as a multifunctional approach for preventing and addressing microbial infections associated with peri-implantitis. The combination of antibacterial and antibiofilm properties in these membranes holds promise for improving the management and treatment of peri-implantitis-related complications.

A miniaturized additive-manufactured carbon black/PLA electrochemical sensor for pharmaceuticals detection.

Additive manufacturing is a technique that allows the construction of prototypes and has evolved a lot in the last 20 years, innovating industrial fabrication processes in several areas. In chemistry, additive manufacturing has been used in several functionalities, such as microfluidic analytical devices, energy storage devices, and electrochemical sensors. Theophylline and paracetamol are important pharmaceutical drugs where overdosing can cause adverse effects, such as tachycardia, seizures, and even renal failure. Therefore, this paper aims at the development of miniaturized electrochemical sensors using 3D printing and polylactic acid-based conductive carbon black commercial filament for theophylline and paracetamol detection. Electrochemical characterizations of the proposed sensor were performed to prove the functionality of the device. Morphological characterizations were carried out, in which chemical treatment could change the surface structure, causing the improvement of the analytical signal. Thus, the detection of theophylline at a linear range of 5.00-150 µmol L-1 with a limit of detection of 1.2 µmol L-1 was attained, and the detection of paracetamol at a linear range of 1.00-200 µmol L-1 with a limit of detection of 0.370 µmol L-1 was obtained, demonstrating the proposed sensor effectively detected pharmaceutical drugs.

Meniscal repair with additive manufacture of bioresorbable polymer: From physicochemical characterization to implantation of 3D printed poly (L-co-D, L lactide-co-trimethylene carbonate) with autologous stem cells in rabbits.

Three-dimensional (3D) structures are actually the state-of-the-art technique to create porous scaffolds for tissue engineering. Since regeneration in cartilage tissue is limited due to intrinsic cellular properties this study aims to develop and characterize three-dimensional porous scaffolds of poly (L-co-D, L lactide-co-trimethylene carbonate), PLDLA-TMC, obtained by 3D fiber deposition technique. The PLDLA-TMC terpolymer scaffolds (70:30), were obtained and characterized by scanning electron microscopy, gel permeation chromatography, differential scanning calorimetry, thermal gravimetric analysis, compression mechanical testing and study on in vitro degradation, which showed its amorphous characteristics, cylindrical geometry, and interconnected pores. The in vitro degradation study showed significant loss of mechanical properties compatible with a decrease in molar mass, accompanied by changes in morphology. The histocompatibility association of mesenchymal stem cells from rabbit's bone marrow, and PLDLA-TMC scaffolds, were evaluated in the meniscus regeneration, proving the potential of cell culture at in vivo tissue regeneration. Nine New Zealand rabbits underwent total medial meniscectomy, yielding three treatments: implantation of the seeded PLDLA-TMC scaffold, implantation of the unseeded PLDLA-TMC and negative control (defect without any implant). After 24 weeks, the results revealed the presence of fibrocartilage in the animals treated with polymer. However, the regeneration obtained with the seeded PLDLA-TMC scaffolds with mesenchymal stem cells had become intimal to mature fibrocartilaginous tissue of normal meniscus both macroscopically and histologically. This study demonstrated the effectiveness of the PLDLA-TMC scaffold in meniscus regeneration and the potential of mesenchymal stem cells in tissue engineering, without the use of growth factors. It is concluded that bioresorbable polymers represent a promising alternative for tissue regeneration.

Development and characterization of ceramic-polymeric hybrid scaffolds for bone regeneration: incorporating of bioactive glass BG-58S into PDLLA matrix.

In recent years, there has been a notable surge of interest in hybrid materials within the biomedical field, particularly for applications in bone repair and regeneration. Ceramic-polymeric hybrid scaffolds have shown promising outcomes. This study aimed to synthesize bioactive glass (BG-58S) for integration into a bioresorbable polymeric matrix based on PDLLA, aiming to create a bioactive scaffold featuring stable pH levels. The synthesis involved a thermally induced phase separation process followed by lyophilization to ensure an appropriate porous structure. BG-58S characterization revealed vitreous, bioactive, and mesoporous structural properties. The scaffolds were analyzed for morphology, interconnectivity, chemical groups, porosity and pore size distribution, zeta potential, pH, in vitro degradation, as well as cell viability tests, total protein content and mineralization nodule production. The PDLLA scaffold displayed a homogeneous morphology with interconnected macropores, while the hybrid scaffold exhibited a heterogeneous morphology with smaller diameter pores due to BG-58S filling. The hybrid scaffold also demonstrated a pH buffering effect on the polymer surface. In addition to structural characteristics, degradation tests indicated that by incorporating BG-58S modified the acidic degradation of the polymer, allowing for increased total protein production and the formation of mineralization nodules, indicating a positive influence on cell culture.

Chlorinated-based bioceramics incorporated in polycaprolactone membranes.

The development of bioactive membranes with bone repair properties is great interest in the field of tissue engineering. In this study, we aimed to fabricate and characterize a composite membrane composed of sol-gel synthesized bioceramics and electrospun polycaprolactone (PCL) fibers for bone tissue regeneration applications. The bioceramics were prepared using the sol-gel method with nitrate (N) and chloride (CL) as precursors. PCL and bioceramic solutions were electrospun to obtain ultrafine fiber mats. Raman spectroscopy, x-ray diffraction (XRD), Fourier Transform Infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and scanning electron microscopy (SEM) were used to characterize the materials. The results showed that both chlorinated and non-chlorinated bioceramics contained NBOs (non-bridge bonds) and crystallized the α-wollastonite phase, with the chlorinated version doing so at lower temperatures. In vitro tests were performed to evaluate cytotoxicity, cell adhesion, and mineralized matrix formation on the membranes. The composite membranes showed improved cell viability and promoted mineralization nodules formation. This study presents a promising approach for the development of bioactive membranes for bone tissue engineering, with potential applications in bone regeneration therapies.

Biodegradable PBAT/PLA blend films incorporated with turmeric and cinnamomum powder: A potential alternative for active food packaging.

Active packaging made from biodegradable polymers and natural additives appears as an ecological alternative. In addition to having antioxidant activity and enhancing food preservation, it allows mitigating the negative impacts caused by improper disposal. This study pursued to produce biodegradable films based on a polymer blend PBAT/PLA (Ecovio®) using the flat extrusion method. The films were prepared with the incorporation of 5 wt% of powdered turmeric or cinnamon as natural additives. The films obtained, and those reprocessed twice, were characterized in terms of colorimetric, UV light transmittance, water contact angle, water vapor permeability, morphology, mechanical properties, and antioxidant activity. Cinnamon reduced the UV light transmittance and made a surface more hydrophobic. Reprocessing led to greater elongation and maximum load, associated with increased dispersion and distribution, as evidenced in the morphological analysis. The films developed have significant potential for applications in active food packaging, with emphasis on cinnamon-additivated films.

B cell-targeted polylactic acid nanoparticles as platform for encapsulating jakinibs: potential therapeutic strategy for systemic lupus erythematosus.

Background: B cells are pivotal in systemic lupus erythematosus and autoimmune disease pathogenesis. Materials & methods: To address this, Nile Red-labeled polylactic acid nanoparticles (NR-PLA NPs) loaded with the JAK inhibitor baricitinib (BARI), specifically targeting JAK1 and JAK2 in B cells, were developed. Results: Physicochemical characterization confirmed NP stability over 30 days. NR-PLA NPs were selectively bound and internalized by CD19+ B cells, sparing other leukocytes. In contrast to NR-PLA NPs, BARI-NR-PLA NPs significantly dampened B-cell activation, proliferation and plasma cell differentiation in healthy controls. They also inhibited key cytokine production. These effects often surpassed those of equimolar-free BARI. Conclusion: This study underscores the potential of PLA NPs to regulate autoreactive B cells, offering a novel therapeutic avenue for autoimmune diseases.

In this study, a new approach to treating autoimmune diseases, particularly systemic lupus erythematosus, was investigated by focusing on a type of immune cell called B cells. Special nanoparticles (NPs) labeled with Nile Red (NR) and made from polylactic acid (PLA) were created. These NPs were loaded with a drug called baricitinib (BARI), which targets specific proteins (JAK1 and JAK2) in B cells. This was done to determine if these NPs could help control the behavior of B cells, which are important in autoimmune diseases. First, these NPs remained stable for a long time (30 days). The NR-labeled PLA NPs (NR-PLA NPs) were also good at attaching to and entering a specific type of B cell called CD19⁺ B cells while leaving other types of immune cells alone. The use of NR-PLA NPs loaded with BARI produced exciting results. These NPs were better at reducing the activity, growth and transformation of B cells into plasma cells compared with the drug BARI by itself. They also stopped the production of certain immune system signals called cytokines, which are usually overactive in autoimmune diseases. This work suggests that PLA NPs could be a promising way to control overactive B cells that contribute to autoimmune diseases like systemic lupus erythematosus. This could open a new and exciting path for developing treatments for these conditions.

Evaluation of contact angle and mechanical properties of resin monomers filled with graphene oxide nanofibers.

This in vitro study synthesized hybrid nanofibers embedded in graphene oxide (GO) and incorporated them into experimental resin composite monomers to evaluate their physical-mechanical properties. Inorganic-organic hybrid nanofibers were produced with precursor solutions of 1% wt. GO-filled Poly (d,l-lactide, PLA) fibers and scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS) characterized the morphology and chemical composition of the spun fibers. Resin composite monomers were developed and a total of 5% nanofibers were incorporated into the experimental materials. Three groups were developed: G1 (control resin monomers), G2 (resin monomers/PLA nanofibers), and G3 (resin monomers/inorganic-organic hybrid nanofibers). Contact angle (n=3), flexural strength (n=22), elastic modulus (n=22), and Knoop hardness (n=6) were evaluated. The mean of the three indentations was obtained for each sample. The normality of data was assessed by QQ Plot with simulated envelopes and analyzed by Welch's method (p<0.05). Overall, SEM images showed the regular shape of nanofibers but were non-aligned. Compositional analysis from EDS (n=6) revealed the presence of carbon and oxygen (present in GO composition) and Si from the functionalization process. The results of contact angle (°) and hardness (Kg/mm2) for each group were as follow, respectively: G1 (59.65±2.90; 37.48±1.86a), G2 (67.99±3.93; 50.56±1.03b) and G3 (62.52±7.40; 67.83±1.01c). The group G3 showed the highest Knoop hardness values (67.83 kg/mm2), and the flexural strength of all groups was adversely affected. The experimental resin composite composed of hybrid nanofibers with GO presented increased hardness values and hydrophilic behavior.

Additive manufacturing of poly (lactic acid)/hydroxyapatite/carbon nanotubes biocomposites for fibroblast cell proliferation.

Bone tissue is one of the most important in the human body. In this study, scaffolds of poly (lactic acid) PLA reinforced with hydroxyapatite (HA) and carbon nanotubes (CNT) were manufactured, evaluating their mechanical and biological properties. HA was synthesized by wet method and characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM). The scaffolds were produced using additive manufacturing and characterized by optical microscopy, SEM, thermogravimetric analysis (TGA), Raman spectroscopy and biological tests. The SEM results showed that the PLA surface was affected by the incorporation of CNT. TG showed that the incorporation of HA into the polymer matrix compromised the thermal stability of PLA. On the other hand, the incorporation of CNT to the polymer and the impregnation with HA on the surface by thermal effect increased the stability of PLA/CNT scaffolds. Raman spectra indicated that HA impregnation on the surface did not modify the polymer or the ceramic. In the compression tests, PLA and PLA/CNT scaffolds displayed the best compressive strength. In the biological tests, more than 85% of the cells remained viable after 48 h of incubation with all tested scaffolds and groups with CNT in the composition disclosing the best results.

Phosphorylated Polyesters Inspired by Phospholipids: Synthesis, Characterization, and Potential Applications.

We report the synthesis of phosphorylated polyesters by the phosphorylation of hydroxylated polyesters synthesized by the lipase-catalyzed polycondensation of glycerol and aliphatic dicarboxylic acids and their characterization. The use of phosphoryl chloride as a phosphorylating agent and triethylamine as a catalyst in mild reaction conditions resulted in polyesters with repetitive units structurally similar to phospholipids, molar mass of around 14-38 kDa, and a degree of phosphorylation of 36 ± 11 mol %. These polyesters are composed mainly of 10 different repetitive units as determined by 1D and 2D NMR. Their properties change from more hydrophilic and amorphous for phosphorylated poly(glycerol adipate) to more hydrophobic and semicrystalline for phosphorylated poly(glycerol dodecanedioate). Preliminary investigations have shown the potential of these polyesters to self-assemble in aqueous media forming nanoparticles, which can be loaded with hydrophobic molecules and released into an organic phase, acting as a phase transfer agent, and used as a pH-responsive emulsifier.