ABSTRACT
Inorganic zeolites have excellent molecular sieving properties, but they are difficult to process into macroscopic structures. In this work, we use metal-organic framework (MOF) glass as substrates to engineer the interface with inorganic zeolites, and then assemble the discrete crystalline zeolite powders into monolithic structures. The zeolites are well dispersed and stabilized within the MOF glass matrix, and the monolith has satisfactory mechanical stabilities for membrane applications. We demonstrate the effective separation performance of the membrane for 1,3-butadiene (C4H6) from other C4 hydrocarbons, which is a crucial and challenging separation in the chemical industry. The membrane achieves a high permeance of C4H6 (693.00±21.83â GPU) and a high selectivity over n-butene, n-butane, isobutene, and isobutane (9.72, 9.94, 10.31, and 11.94, respectively). This strategy opens up new possibilities for developing advanced membrane materials for difficult hydrocarbon separations.
ABSTRACT
Membranes with ultrahigh permeance and practical selectivity could greatly decrease the cost of difficult industrial gas separations, such as CH4/N2 separation. Advanced membranes made from porous materials, such as metal-organic frameworks, can achieve a good gas separation performance, although they are typically formed on support layers or mixed with polymeric matrices, placing limitations on gas permeance. Here an amorphous glass foam, agfZIF-62, wherein a, g and f denote amorphous, glass and foam, respectively, was synthesized by a polymer-thermal-decomposition-assisted melting strategy, starting from a crystalline zeolitic imidazolate framework, ZIF-62. The thermal decomposition of incorporated low-molecular-weight polyethyleneimine evolves CO2, NH3 and H2O gases, creating a large number and variety of pores. This greatly increases pore interconnectivity but maintains the crystalline ZIF-62 ultramicropores, allowing ultrahigh gas permeance and good selectivity. A self-supported circular agfZIF-62 with a thickness of 200-330 µm and area of 8.55 cm2 was used for membrane separation. The membranes perform well, showing a CH4 permeance of 30,000-50,000 gas permeance units, approximately two orders of magnitude higher than that of other reported membranes, with good CH4/N2 selectivity (4-6).
Subject(s)
Gases , Metal-Organic Frameworks , Molecular Weight , Polyethyleneimine , PolymersABSTRACT
Metal-organic framework (MOF) glass is an easy to process and self-supported amorphous material that is suitable for fabricating gas separation membranes. However, MOF glasses, such as ZIF-62 and ZIF-4 have low porosity, which makes it difficult to obtain membranes with high permeance. Here, a self-supported MOF crystal-glass composite (CGC) membrane was prepared by melt quenching a mixture of ZIF-62 as the membrane matrix and ZIF-8 as the filler. The conversion of ZIF-62 from crystal to glass and the simultaneous partial melting of ZIF-8 facilitated by the melt state of ZIF-62 make the CGC membrane monolithic, eliminating non-selective grain boundaries and improving selectivity. The thickness of CGC membrane can be adjusted to fabricate a membrane without the need of a support substrate. CGC membranes exhibit a C2 H6 permeance of 41 569â gas permeation units (GPU) and a C2 H6 /C2 H4 selectivity of 7.16. The CGC membrane has abundant pores from the glassy state of ZIF-62 and the crystalline ZIF-8, which enables high gas permeance. ZIF-8 has preferential adsorption for C2 H6 and promotes C2 H6 transport in the membrane, and thus the GCG membrane exhibits ultrahigh C2 H6 permeance and good C2 H6 /C2 H4 selectivity.