ABSTRACT
OBJECTIVE: To evaluate the mechanical and biological properties of three-dimensionally (3D) printable resins filled with 2-methacryloyloxyethyl phosphorylcholine (MPC) and silicate-based composites and compare with those of a commercially available 3D-printable resin for definitive restorations. METHODS: A group of 3D-printable hybrid resins (HRs) filled with 6 wt% MPC and three different compositions of silicate-based composites (barium silicate to zirconium silicate ratios: 1.50:1 for HR1, 0.67:1 for HR2, and 0.25:1 for HR3) were prepared. The HR groups were compared with the commercially available unfilled 3D-printable resin (CR) marketed for definitive restorations in terms of flexural strength and modulus, fracture toughness, surface roughness, Vickers hardness, light transmittance (all, n = 15), cytotoxicity, and protein adsorption (both, n = 3). All data were analyzed by using non-parametric Kruskal-Wallis and Dunn's tests (α=0.05). RESULTS: The HR groups had significantly higher flexural strength, modulus, fracture toughness, and hardness values than the CR (P < 0.001). HR3 had the highest surface roughness and light transmittance among the groups (P ≤ 0.006). None of tested resins showed cytotoxicity. Both HR2 and HR3 showed significantly lower protein adsorption than the CR, with a difference of approximately 60% (P ≤ 0.026). CONCLUSION: Both HR2 and HR3 exhibited superior mechanical properties (flexural strength, flexural modulus, fracture toughness, and Vickers hardness), light transmittance, and protein-repellent activity than the CR, with no impact on cytotoxicity. CLINICAL SIGNIFICANCE: The MPC/silicate-based composite-filled resins may be a suitable alternative for definitive restorations, given their higher mechanical properties and promising biological properties to prevent microbial adhesion and subsequent biofilm formation, as well as their non-cytotoxic properties.
Subject(s)
Composite Resins , Hardness , Materials Testing , Methacrylates , Silicates , Surface Properties , Silicates/chemistry , Composite Resins/chemistry , Adsorption , Methacrylates/chemistry , Phosphorylcholine/analogs & derivatives , Phosphorylcholine/chemistry , Dental Materials/chemistry , Dental Restoration, Permanent/methods , Flexural Strength , Elastic Modulus , Animals , Polymers/chemistry , Humans , Zirconium/chemistryABSTRACT
OBJECTIVES: To investigate how postpolymerization time (PPT) and atmosphere (PPA) influence the surface properties, protein adsorption, and microbial adhesion of two types of additively manufactured (AM) resins used for definitive restorations. METHODS: Two different types of commercially available AM resins for definitive restorations (UR and CR) were used to create disk-shaped specimens. These specimens were divided into eight groups based on resin type (UR and CR), PPT (standard or extended), and PPA (air or nitrogen). After postpolymerization, the surface roughness (Ra and Sa) and surface free energy (SFE) of all specimens were measured. The study also evaluated protein adsorption, microbial attachment, and cytotoxicity. A non-parametric factorial analysis of variance with post-hoc analyses was conducted, using a significance level (α) of 0.05. RESULTS: The Ra and Sa values for CR were higher than those for UR, regardless of PPT or PPA (P < 0.05). For UR, SFE was higher with extended PPT compared to standard PPT. CR had higher SFE than UR under standard PPT. The interaction between PPT and PPA had a significant effect on protein adsorption (P < 0.05). When PPT was standard, nitrogen significantly increased protein adsorption compared to air. The interaction between resin type and PPA, and between resin type and PPT, significantly affected microbial adhesion (P < 0.05). The changes in PPT or PPA did not affect the cytotoxicity of either AM resin. CONCLUSION: Surface properties, protein adsorption, and microbial attachment were influenced by the interactions among PPT, PPA, and resin type. These factors can have implications for resin-based definitive restorations. CLINICAL SIGNIFICANCES: Clinicians should understand the impact of PPT and PPA on the surface properties of AM resins for definitive restorations, particularly regarding protein adsorption and microbial adhesion. Additionally, the type of AM resin (based on chemical composition) could affect its biological properties.
Subject(s)
Bacterial Adhesion , Biofilms , Composite Resins , Materials Testing , Polymerization , Surface Properties , Biofilms/drug effects , Bacterial Adhesion/drug effects , Time Factors , Composite Resins/chemistry , Dental Materials/chemistry , Adsorption , Dental Restoration, Permanent , Humans , Methacrylates/chemistry , Atmosphere , Nitrogen/chemistry , Streptococcus mutans/drug effects , Polyurethanes/chemistryABSTRACT
STATEMENT OF PROBLEM: Studies on the effect of barium silicate on the material properties of additively manufactured (AM) resins containing 2-methacryloyloxyethyl phosphorylcholine (MPC) for dental applications are lacking. PURPOSE: The purpose of this in vitro study was to evaluate the mechanical properties, transmittance, and protein adsorption of MPC-containing AM resin incorporated with different barium silicate contents and to compare these findings with those of a commercially available unfilled AM resin marketed for definitive restorations. MATERIAL AND METHODS: Resins incorporating 6 wt% MPC and 4 different concentrations of barium silicate (10 wt%, MB10; 20 wt%, MB20; 30 wt%, MB30; and 40 wt%, MB40) were prepared. An MPC-containing resin with no filler was also prepared (0 wt%, MBN). Surface roughness (n=15), Vickers hardness (n=15), flexural strength and modulus (n=15), fracture toughness (n=15), transmittance (n=15), and protein adsorption (n=3) of the filled resin specimens were measured and compared with those of commercially available unfilled resin specimens. All data were analyzed using the Kruskal-Wallis and Dunn tests (α=.05). RESULTS: All experimental resins had higher surface roughness than the unfilled resin (P≤.048). MB40 had higher hardness, flexural strength, flexural modulus, and fracture toughness than most other groups (P≤.047). MB10 had higher transmittance than most other groups (P≤.012). All experimental resins had lower protein adsorption than the unfilled resin, regardless of the barium silicate content (P≤.023). CONCLUSIONS: The experimental resin containing 6 wt% MPC and 40 wt% barium silicate showed better mechanical properties and lower protein adsorption than the resin with no MPC or ceramic fillers. Transmittance decreased with the increase of barium silicate in the resins.
Subject(s)
Materials Testing , Silicates , Surface Properties , Silicates/chemistry , Adsorption , Polymers/chemistry , Barium Compounds/chemistry , Methacrylates/chemistry , Phosphorylcholine/chemistry , Phosphorylcholine/analogs & derivatives , Proteins/chemistry , In Vitro Techniques , Flexural Strength , Hardness , Dental Materials/chemistryABSTRACT
OBJECTIVES: This study aimed to investigate the antimicrobial properties of three dimensionally-printed dental polymers (3DPs) incorporated with microencapsulated phytochemicals (MPs) and to assess their surface characteristics and cytotoxicity. METHODS: MPs derived from phytoncide oil and their specific chemical components were introduced into suspensions of three microbial species: Streptococcus gordonii, Streptococcus oralis, and Candida albicans. Optical density was measured to determine the microbial growth in the presence of MPs for testing their antimicrobial activity. MPs at 5% (w/w) were mixed with dental polymers and dispersants to 3DP discs. These microbial species were then seeded onto the discs and incubated for 24 h. The antibacterial and antifungal activities of MP-containing 3DPs were evaluated by counting the colony-forming units (n = 3). The biofilm formation on the 3DP was assessed by crystal violet staining assay (n = 3). Microbial viability was determined using a live-dead staining and CLSM observation (n = 3). Surface roughness and water contact angle were assessed (n = 10). Cytotoxicity of MP-containing 3DPs for human gingival fibroblast was evaluated by MTT assay. RESULTS: MPs, particularly (-)-α-pinene, suppressed the growth of all tested microbial species. MP-containing 3DPs significantly reduced the colony count (P ≤ 0.001) and biofilm formation (P ≤ 0.009), of all tested microbial species. Both surface roughness (P < 0.001) and water contact angle (P < 0.001) increased. The cytotoxicity remained unchanged after incorporating MPs to the 3DPs (P = 0.310). CONCLUSIONS: MPs effectively controlled the microbial growth on 3DPs as evidenced by the colony count, biofilm formation, and cell viability. Although MPs modified the surface characteristics, they did not influence the cytotoxicity of 3DPs. CLINICAL SIGNIFICANCE: Integration of MPs into 3DPs could produce dental prostheses or appliances with antimicrobial properties. This approach not only provides a proactive solution to reduce the risk of oral biofilm-related infection but also ensures the safety and biocompatibility of the material, thereby improving dental care.