RÉSUMÉ
Gallium (Ga) is a low melting point post-transition metal that, under mild mechanical agitation, can form micron and submicron-sized particles with combined fluid-like and metallic properties. In this work, an inorganic network of Ga liquid metal particles was synthesised via spontaneous formation of manganese (Mn) oxide species on their liquid metallic surfaces forming an all-inorganic composite. The micron-sized Ga particles formed by sonication were connected together by Mn oxide nanostructures spontaneously established from the reduction of a Mn salt in aqueous solution slightly above the melting point of Ga. The formed Mn oxide nanostructures were found to coalesce from the surface of the Ga particles into a continuous inorganic network. The morphology of the composites could be altered by varying the Mn salt concentration and by performing post-treatment annealing. The composites presented a shell of various Mn oxide nanostructures including wrinkled sheets, rods and nanoneedles, around spherical liquid Ga particles, and a liquid metal core. The photoelectric and optical properties of the composites were thoroughly characterised, which revealed decreasing bandgaps and valence band edge characteristics as a function of increased Mn oxide coverage. The photoluminescence properties of the composites could be also engineered by increasing the Mn oxide coverage. The all-inorganic liquid Ga composite could be formed via a straightforward reduction reaction of a Mn-rich salt at the surface of liquid Ga particles with tunable surface properties for future optoelectronic applications.
RÉSUMÉ
In nature, snowflake ice crystals arrange themselves into diverse symmetrical six-sided structures. We show an analogy of this when zinc (Zn) dissolves and crystallizes in liquid gallium (Ga). The low-melting-temperature Ga is used as a "metallic solvent" to synthesize a range of flake-like Zn crystals. We extract these metallic crystals from the liquid metal solvent by reducing its surface tension using a combination of electrocapillary modulation and vacuum filtration. The liquid metal-grown crystals feature high morphological diversity and persistent symmetry. The concept is expanded to other single and binary metal solutes and Ga-based solvents, with the growth mechanisms elucidated through ab initio simulation of interfacial stability. This strategy offers general routes for creating highly crystalline, shape-controlled metallic or multimetallic fine structures from liquid metal solvents.
RÉSUMÉ
Liquid metals and alloys with high-aspect-ratio nanodimensional features are highly sought-after for emerging electronic applications. However, high surface tension, water-like fluidity, and the existence of self-limiting oxides confer specific peculiarities to their characteristics. Here, we introduce a high accuracy nanometric three-dimensional pulling and stretching method to fabricate liquid-metal-based nanotips from room- or near-room-temperature gallium-based alloys. The pulling rate and step size were controlled with a resolution of up to 10 nm and yielded different nanotip morphologies and lengths as a function of the base liquid metal alloy composition and the pulling parameters. The obtained nanotips presented high aspect ratios over lengths of a few microns and apexes between 10 and 100 nm. The liquid metal alloys were found confined within nanotips with about 10 nm apexes when vertically pulled at 100 nm/s. An amorphous gallium oxide skin was shown to cover the surface of the nanotips, while the liquid core was composed of the initial liquid metal alloys. The electrical contact established at the nanotips was characterized under dynamic conditions. The liquid metal nanotips showed an Ohmic resistance when a continuous liquid metal channel was formed, and a controllable semiconductor state corresponding to a heterojunction formed at the junction between the liquid metal phase and the gallium oxide semiconductor skin. The variable threshold voltages of the heterojunction were controlled via stretching of the nanotips with a 10 nm step resolution. The liquid metal nanotips were also used for establishing soft electronic junctions. This novel method of liquid metal nanotip fabrication with Ohmic and semiconducting behaviors will lead to exciting avenues for developing electronic and sensing devices.
RÉSUMÉ
Colloidal liquid metal alloys of gallium, with melting points below room temperature, are potential candidates for creating electrically conductive and flexible composites. However, inclusion of liquid metal micro- and nanodroplets into soft polymeric matrices requires a harsh auxiliary mechanical pressing to rupture the droplets to establish continuous pathways for high electrical conductivity. However, such a destructive strategy reduces the integrity of the composites. Here, this problem is solved by incorporating small loading of nonfunctionalized graphene flakes into the composites. The flakes introduce cavities that are filled with liquid metal after only relatively mild press-rolling (<0.1 MPa) to form electrically conductive continuous pathways within the polymeric matrix, while maintaining the integrity and flexibility of the composites. The composites are characterized to show that even very low graphene loadings (≈0.6 wt%) can achieve high electrical conductivity. The electrical conductance remains nearly constant, with changes less than 0.5%, even under a relatively high applied pressure of >30 kPa. The composites are used for forming flexible electrically-conductive tracks in electronic circuits with a self-healing property. The demonstrated application of co-fillers, together with liquid metal droplets, can be used for establishing electrically-conductive printable-composite tracks for future large-area flexible electronics.
RÉSUMÉ
Gallic acid, a natural phenolic compound, efficiently establishes surface complexes with liquid gallium leading to the formation of an aqueous gallium dispersion via sonication. The surface functionalised gallium particles thus obtained were easily impregnated into paper membranes that could be turned from insulating to conductive by pressure induced deformation of the embedded particles.