RÉSUMÉ
In this work, organic aerogels from spent ground coffee and apple pomace were prepared and characterized for the first time. Apple aerogel was found to be much lighter than that from coffee (0.19 vs. 0.016 g/cm3, whereas the specific surface areas are comparable (229 vs. 208 m2/g). Being intrinsically hydrophilic, these aerogels were silanized, both in liquid and gas phase, to increase stability in aqueous media. The latter modification method allowed chemical grafting of the silane to the aerogel surface (evidenced by FTIR and TGA) and resulted in certain hydrophobicity, as was evidenced via contact angle measurements: both aerogels possess a contact angle of ca. 100° after the gas hydrophobization, while for the pristine aerogels it was 50°. Furthermore, it was observed that the gas-phase silanization process is more applicable to apple aerogels.
RÉSUMÉ
Superhydrophobic coating technology is regarded as an attractive possibility for the protection of materials in a sea environment. DC techniques are a useful tool to characterize metals' behavior in seawater in the presence/absence of coatings and/or corrosion inhibitors. In this work, investigations concerning Al-5%Mg alloy with and without a sprayed superhydrophobic coating were carried out with potentiodynamic scans in photobiologically active and not active seawater (3 weeks of immersion). In not photobiologically active seawater, the presence of the superhydrophobic coating did not prevent pitting corrosion. With time, the coating underwent local exfoliations, but intact areas still preserved superhydrophobicity. In photobiologically active seawater, on samples without the superhydrophobic coating (controls) pitting was inhibited, probably due to the adsorption of organic compounds produced by the photobiological activity. After 3 weeks of immersion, the surface of the coating became hydrophilic due to diatom coverage. As suggested by intermediate observations, the surface below the diatom layer is suspected of having lost its superhydrophobicity due to early stages of biofouling processes (organic molecule adsorption and diatom attachment/gliding). Polarization curves also revealed that the metal below the coating underwent corrosion inhibiting phenomena as observed in controls, likely due to the permeation of organic molecules through the coating. Hence, the initial biofouling stages (days) occurring in photobiologically active seawater can both accelerate the loss of superhydrophobicity of coatings and promote corrosion inhibition on the underlying metal. Finally, time durability of superhydrophobic surfaces in real seawater still remains the main challenge for applications, where the early stages of immersion are demonstrated to be of crucial importance.