Synergetic Dual-Additive Electrolyte Enables Highly Stable Performance in Sodium Metal Batteries.

Sodium (Na)-metal batteries (SMBs) are considered one of the most promising candidates for the large-scale energy storage market owing to their high theoretical capacity (1,166 mAh g-1) and the abundance of Na raw material. However, the limited stability of electrolytes still hindered the application of SMBs. Herein, sulfolane (Sul) and vinylene carbonate (VC) are identified as effective dual additives that can largely stabilize propylene carbonate (PC)-based electrolytes, prevent dendrite growth, and extend the cycle life of SMBs. The cycling stability of the Na/NaNi0.68Mn0.22Co0.1O2 (NaNMC) cell with this dual-additive electrolyte is remarkably enhanced, with a capacity retention of 94% and a Coulombic efficiency (CE) of 99.9% over 600 cycles at a 5 C (750 mA g-1) rate. The superior cycling performance of the cells can be attributed to the homogenous, dense, and thin hybrid solid electrolyte interphase consisting of F- and S-containing species on the surface of both the Na metal anode and the NaNMC cathode by adding dual additives. Such unique interphases can effectively facilitate Na-ion transport kinetics and avoid electrolyte depletion during repeated cycling at a very high rate of 5 C. This electrolyte design is believed to result in further improvements in the performance of SMBs.

Deep Eutectic Solvent Based on Lithium Bis[(trifluoromethyl)sulfonyl] Imide (LiTFSI) and 2,2,2-Trifluoroacetamide (TFA) as a Promising Electrolyte for a High Voltage Lithium-Ion Battery with a LiMn2O4 Cathode.

To design safe and electrochemically stable electrolytes for lithium-ion batteries, this study describes the synthesis and the utilization of new deep eutectic solvents (DESs) based on the mixture of 2,2,2-trifluoroacetamide (TFA) with a lithium salt (LiTFSI, lithium bis[(trifluoromethane)sulfonyl]imide). These prepared DESs were characterized in terms of thermal properties, ionic conductivity, viscosity, and electrochemical properties. Based on the appearance of the product and DSC measurements, it appears that this system is liquid at room temperature for LiTFSI mole fraction ranging from 0.25 to 0.5. At χLiTFSI = 0.25, DESs exhibited favorable electrolyte properties, such as thermal stability (up to 148 °C), relatively low viscosity (42.2 mPa.s at 30 °C), high ionic conductivity (1.5 mS.cm-1 at 30 °C), and quite large electrochemical stability window up to 4.9-5.3 V. With these interesting properties, selected DES was diluted with slight amount of ethylene carbonate (EC). Different amounts of EC (x = 0-30 %wt) were used to form hybrid electrolytes for battery testing with high voltage LiMn2O4 cathode and Li anode. The addition of the EC solvent into DES expectedly aims at enhancing the battery cycling performance at room temperature due to reducing the viscosity. Preliminary results tests clearly show that LiTFSI-based DES can be successfully introduced as an electrolyte in the lithium-ion batteries cell with a LiMn2O4 cathode material. Among all of the studied electrolytes, DES (LiTFSI: TFA = 4:1 + 10 %wt EC) is the most promising. The EC-based system exhibited a good specific capacity of 102 mAh.g-1 at C/10 with the theoretical capacity of 148 mAh.g-1 and a good cycling behavior maintaining at 84% after 50 cycles.