Effect of calcination on minimally processed recycled zirconia powder derived from milling waste.

OBJECTIVE: To assess the influence of calcination process on the properties of minimally processed recycled 3Y-TZP, and to compare it with its commercial counterpart. METHODS: Non-milled 3Y-TZP waste was collected, fragmented and ball-milled to a granulometric < 5 µm. Half of the recycled powder was calcined at 900 °C. Recycled 3Y-TZP disks were uniaxially pressed and sintered to create two recycled groups: 1) Calcined and 2) Non-calcined to be compared with a commercial CAD/CAM milled 3Y-TZP. The microstructure of experimental groups was assessed through density (n = 6), scanning electron microscopy (n = 3) and energy-dispersive X-ray spectroscopy (n = 3); and the crystalline content was evaluated through X-ray diffraction (XRD) (n = 3). Optical and mechanical properties were investigated through reflectance tests (n = 10), and Vickers hardness, fracture toughness (n = 5), and biaxial flexural strength tests (n = 16), respectively. Fractographic analysis was performed to identify fracture origin and crack propagation. Statistical analyses were performed through ANOVA followed by Tukey´s test, and by Weibull statistics. RESULTS: Particle size distribution of recycled powder revealed an average diameter of ∼1.60 µm. The relative density of all experimental groups was > 98.15 % and XRD analysis exhibited a predominance of tetragonal-phase in both recycled groups, which were similar to the crystallographic pattern of the control group. Cross-section micrographs presented flaws on the non-calcined group, and a more homogeneous microstructure for the calcined and commercial groups. Commercial samples showed lower contrast-ratio and higher translucency-parameter than the recycled groups, where non-calcined presented higher translucency-parameter and lower contrast-ratio than its calcined counterpart. The commercial group presented higher fracture toughness and characteristic strength than the recycled groups. Moreover, the calcined group exhibited higher hardness, characteristic strength, and probability of survival at higher loads than the non-calcined group. Fractographic analysis depicted the presence of microstructural flaws in the non-calcined group, which may have acted as stress-raisers and led to failures at lower flexural strengths values. SIGNIFICANCE: The calcination process improved the microstructure, optical, and mechanical properties of the recycled 3Y-TZP.

Atypical histological presentation of bone regeneration after insertion of cryoprotected allogeneic bone graft.

BACKGROUND: To evaluate bone regenerative capacity of cryoprotected corticocancellous allogeneic bone graft performed in type II and III post-extraction sockets for ridge preservation after twelve weeks in-vivo. MATERIAL AND METHODS: Twenty-seven type II or III bony-walled extraction sockets (mandible and maxilla) were selected for this study. Following atraumatic tooth-extraction a cryoprotected corticocancellous allogeneic bone graft material and a resorbable porcine-derived collagen membrane were used for ridge preservation. During re-entry surgery at approximately 12 weeks, bone core biopsies were obtained using a 3.2 mm trephine drill and samples were histologically processed and subjected to qualitative and quantitative histomorphometric analysis. Quantitative data was analyzed using a general linear mixed model with results presented as mean values with the corresponding 95% confidence interval values. RESULTS: Healing without incident and ridge preservation allowed for the placement of dental implants after 12 weeks in 25 out of the 27 treated socket sites. Analyses yielded an average of ~21.0±7% of old/native bone, ~17±5.5% of newly regenerated bone (total of ~38±12.8% for all bone), 0.23±0.14% of new bone presenting with nucleating sites within the matrix, ~52±5.12% of soft tissue, and 3.6±2.09% of damaged bone. The average regenerated bone was statistically analogous to that of old/native bone (p=0.355). Furthermore, an atypical histological pattern of bone regeneration was observed, with newly formed bone exhibiting "infiltration-like" behavior and with new bone nucleating sites observed within the demineralized bone matrix. CONCLUSIONS: Cryoprotected corticocancellous allogeneic bone-graft demonstrated osteoconductive, osteoinductive, and osteogenic properties, yielding unique healing patterns which does warrant further investigation.

The effect of nano hydroxyapatite coating implant surfaces on gene expression and osseointegration.

BACKGROUND: Hierarchical micro-nano structured topography along with surface chemistry modifications of dental implants have been suggested to positively contribute to the osseointegration process. However, the effect of such surface modifications on the molecular response as well as bone formation rate and quality are still unclear, especially in the early healing period. This study aimed to evaluate the effect of coating a double acid etched (DAE) implant surface with nano-sized (20 nm) hydroxyapatite (Nano) with respect to gene expression, histologic parameters, and nanomechanical properties when compared to DAE control at 1 and 2 weeks after implant placement in a rodent femur model. MATERIAL AND METHODS: Expression of bone-related genes was determined by qRT-PCR (Col-I, Runx-2, Osx, Opn, Ocn, Alp). Histomorphometric evaluation of bone-to-implant contact (BIC) and bone area fraction occupancy (BAFO) within implant threads was performed using photomicrographs after histologic processing. Mechanical properties, reduced elastic modulus and hardness, were determined through nanoindentation. RESULTS: At 1 week, the Nano group demonstrated significantly higher expression of Col-I and Ocn compared to the DAE group, indicating upregulation of osteoprogenitor and osteoblast differentiation genes. At 2 weeks, Nano surface further exhibited enhanced gene expression of Col-I and Osx in comparison to the DAE surface, suggesting an increased mineralization of the newly formed bone. Nanoindentation analysis revealed that the Nano group presented no significant difference on the ranks of reduced elastic modulus and hardness compared to DAE for both timepoints. Histomorphometric analysis yielded no significant difference in the percentage of BIC and BAFO between the Nano and DAE surfaces at 1 and 2 weeks. However, Nano implants did present a higher mean value, ~50%, of BIC compared to DAE, ~30%, after 2 weeks in vivo. CONCLUSIONS: While no significant differences were observed in the amount and mechanical properties of newly formed bone, Nano surface positively and significantly increased the expression osteogenic genes compared to DAE surface at early healing periods.

Impact of implant thread design on insertion torque and osseointegration: a preclinical model.

BACKGROUND: Successful osseointegration of endosteal dental implants has been attributed to implant design, including the macro-, micro- and nano- geometric properties. Based on current literature pertaining to implant design, the resultant cellular and bone healing response is unknown when the thread thickness of the implants is increased, resulting in an increased contact area in implants designed with healing chambers. The aim of this study was to evaluate the effect of two implant designs with different thread profiles on the osseointegration parameters and implant stability at 3- and 6-weeks in vivo using a well-established preclinical dog model. MATERIAL AND METHODS: A total of 48 type V Ti alloy implants were divided in two groups according to their thread design (D1= +0.1x/mm and D2= +0.15x/mm) and placed in an interpolated fashion into the radii of six beagles. Insertion torque was measured at time of placement, radii were extracted for histological processing following 3- and 6-week healing intervals. Histologic and histomorphometric analyses were performed in terms of bone to implant contact (%BIC) and bone area fraction occupancy within implant threads (%BAFO). Statistical analyses were performed through a linear mixed model with fixed factors of time and implant thread design. RESULTS: Surface roughness analysis demonstrated no significant differences in Sa and Sq between D1 and D2 implant designs, which confirmed that both implant designs were homogenous except for their respective thread profiles. For insertion torque, statistically significant lower values were recorded for D1 in comparison to D2 (59.6 ± 11.1 and 78.9 ± 10.1 N⋅cm, respectively). Furthermore, there were no significant differences with respect to histological analysis and histomorphometric parameters, between D1 and D2 at both time points. CONCLUSIONS: Both thread profiles presented equivalent potential to successfully osseointegrate in the osteotomies, with D2 yielding higher mechanical retention upon placement without detrimental bone resorption.

Bone regeneration at extraction sockets filled with leukocyte-platelet-rich fibrin: An experimental pre-clinical study.

BACKGROUND: We aimed to histomorphometrically evaluate the effects of Leucocyte-Platelet-Rich Fibrin (L-PRF), with and without the combination of a bone grafting material, for alveolar ridge preservation using an in vivo canine model. MATERIAL AND METHODS: Seven dogs (Female Beagles, ~18-month-old) were acquired for the study. L-PRF was prepared from each individual animal by drawing venous blood and spinning them through a centrifuge at 408 RCF-clot (IntrasSpin, Intra-Lock, Boca Raton, FL). L-PRF membranes were obtained from XPression fabrication kit (Biohorizons Implant Systems, Inc., AL, USA). A split mouth approach was adopted with the first molar mesial and distal socket defects treated in an interpolated fashion of the following study groups: 1) Empty socket (negative control); 2) OSS filled defect 3) L-PRF membrane; and 4) Mix of Bio-Oss® with L-PRF. After six weeks, samples were harvested, histologically processed, and evaluated for bone area fraction occupancy (BAFO), vertical/horizontal ridge dimensions (VRD and HRD, respectively), and area of coronal soft tissue infiltration. RESULTS: BAFO was statistically lower for the control group in comparison to all treatment groups. Defects treated with Bio-Oss® were not statistically different then defects treated solely with L-PRF. Collapsed across all groups, L-PRF exhibited higher degrees of BAFO than groups without L-PRF. Defects filled with Bio-Oss® and Bio-Oss® with L-PRF demonstrated greater maintenance of VRD relative to the control group. Collapsed across all groups, Bio-Oss® maintained the VRD and resulted in less area of coronal soft tissue infiltration compared to the empty defect. Soft tissue infiltration observed at the coronal area was not statistically different among defects filled with L-PRF, Bio-Oss®, and Bio-Oss® with L-PRF. CONCLUSIONS: Inclusion of L-PRF to particulate xenograft did not promote additional bone heading at 6 weeks in vivo. However, we noted that L-PRF alone promoted alveolar socket regeneration to levels comparable to particulate xenografts, suggesting its potential utilization for socket preservation.

Effects of a local single dose administration of growth hormone on the osseointegration of titanium implants.

BACKGROUND: The aim of the present study was to evaluate the effect of different concentrations of growth hormone (GH) on endosteal implant's surface at the early stages of osseointegration. MATERIAL AND METHODS: Sixty tapered acid-etched titanium implants were divided into four groups: i) Collagen, used as a control group; and three experimental groups, where after collagen coating, GH was administered directly to the surface in varying concentrations: ii) 0.265 mg, iii) 0.53 mg, and iv) 1 mg. Implants were placed in an interpolated fashion in the anterior flange of C3, C4 or C5 of 15 sheep with minimum distance of 6 mm between implants. After 3-, 6- and 12-weeks of healing samples were harvested, histologically processed, qualitatively and quantitatively assessed for bone-to-implant contact (BIC) and bone area fraction occupancy (BAFO). RESULTS: Statistical analysis as a function of time in vivo and coating resulted in no significant differences for BIC and BAFO at any evaluation time point. Histological evaluation demonstrated similar osseointegration features for all groups with woven bone formation at 3 weeks and progressive replacement of woven for lamellar bone in close contact with the implant surface and within the implant's threads. CONCLUSIONS: A single local application of growth hormone to the surface of titanium implants did not yield improved implant osseointegration independent of healing time.

Microtomographic reconstruction of mandibular defects treated with xenografts and collagen-based membranes: A pre-clinical minipig model.

BACKGROUND: The goal of this study was to evaluate hard tissue response following guided bone regeneration using commercially available bovine bone grafts and collagen membranes; bilayer collagen membrane and porcine pericardium-based membrane, by means of a non-destructive three-dimensional (3D) computerized volumetric analysis following microtomography reconstruction. MATERIAL AND METHODS: Bone regenerative properties of various bovine bone graft materials were evaluated in the Göttingen minipig model. Two standardized intraosseous defects (15mm x 8mm x 8mm) were created bilaterally of the mandible of eighteen animals (n=72 defects). Groups were nested within the same subject and randomly distributed among the sites: (i) negative control (no graft and membrane), (ii) bovine bone graft/bilayer collagen membrane (BOB) (iii) Bio-Oss® bone graft/porcine pericardium-based membrane (BOJ) and (iv) cerabone® bone graft/porcine pericardium-based membrane (CJ). Samples were harvested at 4, 8, and 12-week time points (n=6 animal/time point). Segments were scanned using computerized microtomography (µCT) and three dimensionally reconstructed utilizing volumetric reconstruction software. Statistical analyses were performed using IBM SPSS with a significance level of 5%. RESULTS: From a temporal perspective, tridimensional evaluation revealed gradual bone ingrowth with the presence of particulate bone grafts bridging the defect walls, and mandibular architecture preservation over time. Volumetric analysis demonstrated no significant difference between all groups at 4 weeks (p>0.127). At 8 and 12 weeks there was a higher percentage of new bone formation for control and CJ groups when compared to BOB and BOJ groups (p<0.039). The natural bovine bone graft group showed more potential for graft resorption over time relative to bovine bone graft, significantly different between 4 and 8 weeks (p<0.003). CONCLUSIONS: Volumetric analysis yielded a favorable mandible shape with respect to time through the beneficial balance between graft resorption/bone regenerative capacity for the natural bovine bone graft.

Nanoscale physico-mechanical properties of an aging resistant ZTA composite.

OBJECTIVE: To characterize the effects of aging on the nanomechanical properties and 3D surface topographical parameters of an experimental Zirconia Toughened Alumina (ZTA) composite compared to its respective individual counterpart materials. METHODS: Disk-shaped specimens comprised of three material groups were processed: 1) ZTA 70/30 (70% alumina reinforced with 30% second-generation 3Y-TZP); 2) Zpex (Second-generation 3Y-TZP), and; 3) Al2O3 (High purity Alumina) (n = 10/material, 12 × 1 mm). After synthesis, ceramic powders were pressed, the green-body samples were sintered and polished. Nanoindentation testing was performed to record elastic modulus (E) and hardness (H). Interferometry was utilized to assess 3D surface roughness parameters (Sa, Sq), while X-ray diffraction (XRD) and scanning electron microscope (SEM) assessed the crystalline content and microstructure. All tests were performed before and after simulated aging (134°C, 2.2 bar, 20 h). Statistical analyses were performed using linear mixed-model and least square difference pos-hoc tests (α = 5%). RESULTS: XRD spectra indicated increase of monoclinic peaks for Zpex (~18%) relative to ZTA 70/30 (~2.5%) after aging. Additionally, aging did not affect the surface roughness parameters of ZTA 70/30 and Al2O3, although a significant increase in Sa was recorded for Zpex following aging (~90 nm) (p < 0.001). Al2O3 yielded the highest H and E values (H:21 GPa, E: 254 GPa), followed by ZTA 70/30 (H: 13 GPa, E: 214 GPa) and Zpex (H:11 GPa, E: 167 GPa), all significantly different (p < 0.03). CONCLUSION: ZTA 70/30 and Al2O3 presented high hydrothermal stability with respect to all evaluated variables, where artificial aging significantly increased the monoclinic content and surface roughness of Zpex.

Microstructural, mechanical, and optical characterization of an experimental aging-resistant zirconia-toughened alumina (ZTA) composite.

OBJECTIVE: To evaluate the effect of aging on the microstructural, mechanical, and optical properties of an experimental zirconia-toughened alumina composite with 80%Al2O3 and 20%ZrO2 (ZTA Zpex) compared to a translucent zirconia (Zpex) and Alumina. METHODS: Disc-shaped specimens were obtained by uniaxial and isostatic pressing the synthesized powders (n = 70/material). After sintering and polishing, half of the specimens underwent aging (20 h, 134 °C, 2.2 bar). Crystalline content and microstructure were evaluated using X-ray diffraction and scanning electron microscopy, respectively. Specimens underwent biaxial flexural strength testing to determine the characteristic stress, Weibull modulus, and reliability. Translucency parameter (TP) and Contrast ratio (CR) were calculated to characterize optical properties. RESULTS: ZTA Zpex demonstrated a compact surface with a uniform dispersion of zirconia particles within the alumina matrix, and typical alumina and zirconia crystalline content. ZTA Zpex and alumina exhibited higher CR and lower TP than Zpex. ZTA Zpex and Zpex showed significantly higher characteristic stress relative to alumina. While aging did not affect optical and mechanical properties of ZTA Zpex and alumina, Zpex demonstrated a significant increase in translucency, as well as a in characteristic stress. Alumina reliability was significantly lower than others at 300 MPa, ZTA Zpex and Zpex reliability decreased at 800 MPa, except for aged Zpex. SIGNIFICANCE: While aging did not affect the mechanical nor the optical properties of ZTA Zpex and alumina, it did alter both properties of Zpex. The results encourage further investigations to engineer ZTA as a framework material for long span fixed dental prostheses specially where darkened substrates, such as titanium implant abutments or endodontically treated teeth, demand masking.

Assessing osseointegration of metallic implants with boronized surface treatment.

BACKGROUND: Modification of endosteal implants through surface treatments have been investigated to improve osseointegration. Boronization has demonstrated favorable mechanical properties, but limited studies have assessed translational, in vivo outcomes. This study investigated the effect of implant surface boronization on bone healing. MATERIAL AND METHODS: Two implant surface roughness profiles (acid etched, machined) in CP titanium (type II) alloy implants were boronized by solid-state diffusion until 10-15µm boron coating was achieved. The surface-treated implants were placed bilaterally into 5 adult sheep ilia for three and six weeks. Four implant groups were tested: boronized machined (BM), boronized acid-etched (BAA), control machined (CM), and control acid-etched (CAA). Osseointegration was quantified by calculating bone to implant contact (BIC) and bone area fraction occupancy (BAFO). RESULTS: Both implant types treated with boronization had BIC values not statistically different from machined control implants at t=3 weeks, and significantly less than acid-etched control (p<0.02). BAFO values were not statistically different for all 3-week groups except machined control (significantly less at p <0.02). BAFO had a significant downward trend from 3 to 6 weeks in both boronized implant types (p<0.03) while both control implant types had significant increases in BIC and BAFO from 3 to 6 weeks. CONCLUSIONS: Non-decalcified histology depicted intramembranous-like healing/remodeling in bone for controls, but an absence of this dynamic process in bone for boronized implants. These findings are inconsistent with in vitro work describing bone regenerative properties of elemental Boron and suggests that effects of boron on in vivo bone healing warrant further investigation.

Osteogenic parameters surrounding trabecular tantalum metal implants in osteotomies prepared via osseodensification drilling.

BACKGROUND: Surgical fixation of implants into bone for the correction of bone deformities or defects is a traditional approach for skeletal stabilization. Important measures of efficacy of implants include implant stability and osseointegration-the direct interaction between living bone and an implant. Osseointegration depends on successful implant placement and subsequent bone remodeling. This study utilized osseodensification drilling (OD) in a low bone density model using trabecular metal (TM) implants. MATERIAL AND METHODS: Three osteotomy sites, Regular, OD-CW (clockwise), and OD-CCW (counterclockwise), were prepared in each ilium of three female sheep. Drilling was performed at 1100rpm with saline irrigation. Trabecular metal (TM) (Zimmer, Parsippany, NJ, USA) implants measuring 3.7mm in diameter x 10mm length were placed into respective osteotomies. A three-week period post-surgery was given to allow for healing to take place after which all three sheep were euthanized and the ilia were collected. Samples were prepared, qualitatively and quantitatively analyzed using histology micrographs and image analysis software (ImageJ, NIH, Bethesda, MD). Bone-to-implant contact (BIC) and bone area fraction occupancy (BAFO) were quantified to evaluate the osseointegration parameters. RESULTS: All implants exhibit successful bone formation in the peri-implant environment as well as within the open spaces of the trabecular network. Osseointegration within the TM (quantified by %BIC) as a function of drilling technique was more pronounced in OD samples(p>0.05). The %BAFO however shows a significant difference (p=0.036) between the CCW and R samples. Greater bone volume and frequency of bone chips are observed in OD samples. CONCLUSION: The utilization of OD as a design for improved fixation of hardware was supported by increased levels of stability, both primary and secondary. Histological data with OD provided notably different results from those of the regular drilling method.

Effect of implant placement depth on the peri-implant bone defect configurations in ligature-induced peri-implantitis: An experimental study in dogs.

BACKGROUND: The subcrestal placement of implant platform has been considered a key factor in the preservation of crestal bone, but the influence of implant placement depth on bone remodeling combined with peri-implantitis is not fully understood. The aim of this study was to assess the effect of the crestal or subcrestal placement of implants on peri-implant bone defects of ligature-induced peri-implantitis in dogs. MATERIAL AND METHODS: Eight weeks after tooth extraction in six beagle dogs, two different types of implants (A: OsseoSpeed(TM), Astra, Molndal, Sweden; B: Integra-CP(TM), Bicon, Boston, USA) were placed at either crestal or subcrestal (-1.5 mm) positions on one side of the mandible. Ligature-induced peri-implantitis was initiated four weeks after the installation of the healing abutment connections. After 12 weeks, tissue biopsies were processed for histological analyses. RESULTS: Supra-alveolar bone loss combined with a shallow infrabony defect was observed in crestal level implants while deep and wide infrabony defects were present in subcrestal level groups. Subcrestal groups showed significantly greater ridge loss, depths and widths of infrabony defects when compared to crestal groups (P <0.001). CONCLUSIONS: Within the limitations of the animal study, it can be stated that the implants at subcrestal position displayed greater infra-osseous defect than implants at crestal position under an experimental ligature-induced peri-implantitis.

Evaluation of bone response to various anorganic bovine bone xenografts: an experimental calvaria defect study.

This in vivo study investigated the in vivo performance of two newly developed synthetic bone substitutes and compared them to commercially available xenografts (Bio-Oss, Geistlich Pharma AG, Switzerland; OsteoGraf, Dentsply, USA). The materials were tested in a rabbit calvaria model, and the bone forming properties were observed at 4 and 8 weeks after implantation by means of histomorphometry and micro computed tomography (micro-CT). Defects without any graft material were used as negative controls. Micro-CT showed that all materials tested presented new bone formation that filled the defects at both time points, whereas the negative control presented less bone formation, with soft tissue infiltration into the defects. Comparable bone fill percentages were observed for histomorphometric and micro-CT results. Even though no statistically significant difference was found quantitatively between all of the bone graft substitute groups, a higher mean decrease in graft material filling the defects, along with higher remodelling activity, was evident for the experimental materials compared to the commercially available xenografts at 8 weeks. The results indicate that the experimental materials possess high degradability, along with osteoconduction comparable to commercially available xenografts.