RÉSUMÉ
In order to investigate the effect of boron element on liquefied wood carbon fibers and their composites, boric acid and boron carbide were utilized to modify liquefied wood resin through copolymerization and blending methods respectively. Then boric acid-modified liquefied wood carbon fiber (BA-WCF) and boron carbide-modified liquefied wood carbon fiber (BC-WCF) were produced via melt spinning, curing, and carbonization treatments. As expected, this modification approach effectively prevents the formation of skin-core structures and accelerates the evolution of a graphite microcrystalline structure, thereby enhancing the mechanical properties of the carbon fibers. Particularly, the tensile strength and elongation at break of BA-WCF increased to 331.57 MPa and 7.57 % respectively, representing increments of 117 % and 86 % compared to the conventional fibers. Furthermore, the as-fabricated carbon fiber/resin composites (CFPRs), composing of BA-WCF or BC-WCF as fillers and liquefied wood resin as matrix, exhibited excellent interlaminar shear strength, outstanding abrasion resistance, and well thermal conductivity, as well as electrical performance, significantly outperforming the conventional carbon fiber/phenolic resin composites. The friction rate of BC-WP/BA-WCF/CF was 2.37 %, while its thermal conductivity could reach 1.927 W/(m·K). These promising attributes lay the groundwork for the development of high-performance carbon fiber-based materials, fostering their widespread utilization across various industries.
Sujet(s)
Fibre de carbone , Conductivité thermique , Bois , Fibre de carbone/composition chimique , Bois/composition chimique , Catalyse , Résistance à la traction , Composés du bore/composition chimique , Acides boriquesRÉSUMÉ
In order to solve the environmental damage caused by the discharge of dyes as industrial wastewater, the development of efficient and sustainable adsorbents is the key, while most of the previous studies on bamboo parenchyma cells have focused on their microstructural, functional and mechanical properties, and few of the properties in adsorption have been investigated. To evaluate the role of the unique microstructure of bamboo parenchyma cells on adsorption after carbonization and activation, PC-based activated carbon (PPAC) was fabricated by the phosphoric acid activation method and tested for adsorption using methylene blue (MB). The effect of mesoporous structure on MB adsorption was investigated in detail using PPAC-30C impregnated with phosphoric acid at a concentration of 30%. The results showed that the adsorption performance was influenced by single-factor experiments (e.g., pH, activated carbon dosing). The adsorption isotherms and kinetics could conform to the Langmuir model (R2 = 0.983-0.994) and pseudo-second-order kinetic model (R2 = 0.822-0.991) respectively, and the maximum MB adsorption capacity of adsorbent was 576 mg g-1. The adsorption mechanism of MB on PPAC-30C includes physical adsorption, electrostatic attraction, hydrogen bonding, and the π-π conjugation effect, which was dominated by physical adsorption. The results of this study show that PPAC has good application prospects for cationic dye removal.