ABSTRACT
The effect of sigma-phase precipitation on plastic anisotropy of the equiatomic CoCrFeMnNi high-entropy alloy was investigated. Annealing at 700 °C after cold-rolling leads to the formation of the Cr-rich σ phase with a fraction of 2.7%. It is experimentally found that the planar anisotropy (∆r = -0.16) of the CoCrFeMnNi alloy annealed at 700 °C is two times lower than that of the alloy annealed at 800 °C (∆r = -0.35). This observation was further supported by measuring the earing profile of cup specimens after the deep drawing process. The plastic strain ratio, normal anisotropy, and planar anisotropy were also predicted using the visco-plastic self-consistent model. The results indirectly indicated that the reduction of plastic anisotropy in alloy annealed at 700 °C can be attributed to the formation of the σ phase.
ABSTRACT
Metal alloys with enhanced mechanical properties are in considerable demand in various industries. Thus, this study focused on the development of nanosized precipitates in Fe71.25(CoCrMnNi)23.75Cu3Al2 maraging medium-entropy alloy (MEA). The Fe-based alloying design in the MEA samples initially formed a body-centered cubic (BCC) lath martensite structure. After a subsequent annealing process at 450 °C for varying durations (1, 3, 5, and 7 h), nanosized precipitates (B2 intermetallic) enriched with Cu and with a diameter of approximately 5 nm formed, significantly increasing the hardness of the alloy. The highest Vickers microhardness of 597 HV, along with compressive yield strength and ultimate compressive strength of 2079 MPa and 2843 MPa, respectively, was achieved for the Aged_7h sample. Therefore, the BCC lath martensite structure with B2 intermetallics leads to remarkable mechanical properties.
ABSTRACT
Iron making is the biggest single cause of global warming. The reduction of iron ores with carbon generates about 7% of the global carbon dioxide emissions to produce ≈1.85 billion tons of steel per year. This dramatic scenario fuels efforts to re-invent this sector by using renewable and carbon-free reductants and electricity. Here, the authors show how to make sustainable steel by reducing solid iron oxides with hydrogen released from ammonia. Ammonia is an annually 180 million ton traded chemical energy carrier, with established transcontinental logistics and low liquefaction costs. It can be synthesized with green hydrogen and release hydrogen again through the reduction reaction. This advantage connects it with green iron making, for replacing fossil reductants. the authors show that ammonia-based reduction of iron oxide proceeds through an autocatalytic reaction, is kinetically as effective as hydrogen-based direct reduction, yields the same metallization, and can be industrially realized with existing technologies. The produced iron/iron nitride mixture can be subsequently melted in an electric arc furnace (or co-charged into a converter) to adjust the chemical composition to the target steel grades. A novel approach is thus presented to deploying intermittent renewable energy, mediated by green ammonia, for a disruptive technology transition toward sustainable iron making.
ABSTRACT
Numerous studies have explored new materials for electrocatalysts, but it is difficult to discover materials that surpass the catalytic activity of current commercially available noble metal electrocatalysts. In contrast to conventional transition metal alloys, high-entropy alloys (HEAs) have immense potential to maximize their catalytic properties because of their high stability and compositional diversity as oxygen evolution reactions (OERs). This work presents medium-entropy alloys (MEAs) as OER electrocatalysts to simultaneously satisfy the requirement of high catalytic activity and long-term stability. The surface of MEA electrocatalyst is tailored to suit the OER via anodizing and cyclic voltammetry activation methods. Optimized electrical properties and hydrophilicity of the surface enable an extremely low overpotential of 187 mV for achieving the current density of 10 mA cm-2 alkaline media. Furthermore, a combined photovoltaic-electrochemical system with MEA electrocatalyst and a perovskite/Si tandem solar cell exhibits a solar-to-hydrogen conversion efficiency of 20.6% for an unassisted hydrogen generation system. These results present a new pathway for designing sustainable high efficiency water splitting cells.
ABSTRACT
Controlling the feature sizes of 3D bicontinuous nanoporous (3DNP) materials is essential for their advanced applications in catalysis, sensing, energy systems, etc., requiring high specific surface area. However, the intrinsic coarsening of nanoporous materials naturally reduces their surface energy leading to the deterioration of physical properties over time, even at ambient temperatures. A novel 3DNP material beating the universal relationship of thermal coarsening is reported via high-entropy alloy (HEA) design. In newly developed TiVNbMoTa 3DNP HEAs, the nanoporous structure is constructed by very fine nanoscale ligaments of a solid-solution phase due to enhanced phase stability by maximizing the configuration entropy and suppressed surface diffusion. The smallest size of 3DNP HEA synthesized at 873 K is about 10 nm, which is one order of magnitude smaller than that of conventional porous materials. More importantly, the yield strength of ligament in 3DNP HEA approaches its theoretical strength of G/2π of the corresponding HEA alloy even after thermal exposure. This finding signifies the key benefit of high-entropy design in nanoporous materials-exceptional stability of size-related physical properties. This high-entropy strategy should thus open new opportunities for developing ultrastable nanomaterials against its environment.
ABSTRACT
Synergetic strengthening induced by plastic strain incompatibility at the interface, and the resulting extra geometrically necessary dislocations (GNDs) generated during plastic deformation, were investigated to understand the origin of extra strength in heterogeneous structured (HS) materials. The mechanism of extra GND generation in twinning-induced plasticity (TWIP)-interstitial free (IF) steel layered sheet was quantitatively analyzed by conducting in situ neutron scattering tensile test. Load partitioning due to the different mechanical properties between the TWIP-steel core and IF-steel sheath at the TWIP/IF interface was observed during the in situ tensile testing. Because of the plastic strain incompatibility from load partitioning, extra GNDs are generated and saturate during tensile deformation. The extra GNDs can be correlated with the back-stress evolution of the HS materials, which contributes to the strength of layered materials. Because of the back-stress evolution caused by load partitioning, the strength of TWIP-IF layered steel is higher than the strength estimated by the rule-of-mixtures. This finding offers a mechanism by which extra GNDs are generated during load partitioning and shows how they contribute to the mechanical properties of HS materials.
ABSTRACT
Annealing of severely plastic deformed materials is expected to produce a good combination of strength and ductility, which has been widely demonstrated in conventional materials. In the present study, high-pressure torsion processed CoCrNi medium entropy alloy consisting of a single face-centered cubic (FCC) phase with a grain size of ~50 nm was subjected to different annealing conditions, and its effect on microstructure and mechanical behavior was investigated. The annealing of high-pressure torsion processed CoCrNi alloy exhibits partial recrystallization and near full recrystallization based on the annealing temperature and time. The samples annealed at 700 °C for 2 min exhibit very fine grain size, a high fraction of low angle grain boundaries, and high kernel average misorientation value, indicating partially recrystallized microstructure. The samples annealed for a longer duration (>2 min) exhibit relatively larger grain size, a low fraction of low angle grain boundaries, and low kernel average misorientation value, indicating nearly full recrystallized microstructure. The annealed samples with different microstructures significantly influence the uniform elongation, tensile strength, and work hardening rate. The sample annealed at 700 °C for 15 min exhibits a remarkable combination of tensile strength (~1090 MPa) and strain to failure (~41%).