Semiconductor quantum dots (QDs) have been used in a variety of applications ranging from optoelectronics to biodiagnostic fields, primarily due to their size dependent fluorescent nature. CdSe nanocrystals (NCs) are generally synthesized via a hot injection method in an organic solvent. However, such NCs are insoluble in water and therefore preclude the direct usage toward biological systems. Thus, the preparation of more biocompatible water-soluble QDs with a high photoluminescent quantum yield (PLQY) is extremely important for imaging applications. Although previous literature has detailed on the synthesis of CdSe NCs in water, they suffer from poor size distribution and very low PLQY. The complex formation mechanism of CdSe NCs in an aqueous environment adversely affects the quality of NCs due to the presence of OH-, H+, and H2O moieties. Here in this article, we have presented the facile hydrothermal approach to obtain size tunable (2.9-5.1 nm), aqueous CdSe NCs with a narrow emission profile having â¼40 nm fwhm with 56% PLQY. Physicochemical properties of the synthesized water-soluble CdSe NCs were studied with the help of UV-vis, PL, XRD, FTIR, XPS, and HR-TEM analysis. Furthermore, the surface of the synthesized CdSe NCs was modified with d-glucosamine via EDC and NHS coupling to obtain a stable, biocompatible bioimaging probe. Furthermore, we demonstrated that their successful bioconjugation with glucosamine could facilitate effective internalization into the cellular matrix.
Metal nanoclusters (NCs) composed of the least number of atoms (a few to tens) have become very attractive for their emerging properties owing to their ultrasmall size. Preparing copper nanoclusters (Cu NCs) in an aqueous medium with high emission properties, strong colloidal stability, and low toxicity has been a long-standing challenge. Although Cu NCs are earth-abundant and inexpensive, they have been comparatively less explored due to their various limitations, such as ease of surface oxidation, poor colloidal stability, and high toxicity. To overcome these constraints, we established a facile synthetic route by optimizing the reaction parameters, especially altering the effective concentration of the reducing agent, to influence their optical characteristics. The improvement of the photoluminescence intensity and superior colloidal stability was modeled from a theoretical standpoint. Moreover, the as-synthesized Cu NCs showed a significant reduction of toxicity in both in vitro and in vivo models. The possibility of using such Cu NCs as a diagnostic probe toward C. elegans was explored. Also, the extension of our approach toward improving the photoluminescence intensity of the Cu NCs on other ligand systems was demonstrated.