Characterization of the boron profile and coordination in altered glass layers by EEL spectroscopy.

Electron energy-loss spectroscopy was used to characterize the boron profile and its coordination (BIII and BIV), along the complex alteration layer of glass samples altered for 511 days at 50 °C in solution containing FeCl2, MgCl2 and/or CaCl2. To reach this goal, the impact of both TEM operating conditions and sample preparation on the determination of the boron coordination was first studied using mineralogical and pristine glasses reference samples. Then, the boron concentration profiles were characterized in the glass alteration layer. These profiles were found to be S-shaped with a thickness around forty nanometers. The proportion of BIII was found to decrease with the boron total concentration (from the pristine glass to the gel layer), which suggests a higher bonding strength for BIV bonds than that of BIII bonds under the alteration conditions. These findings are of tremendous interest to advance further in the understanding of glass alteration mechanisms.

Evaluation and application of a new scintillator-based heat-resistant back-scattered electron detector during heat treatment in the scanning electron microscope.

A new high-temperature detector dedicated to the collection of backscattered electrons is used in combination with heating stages up to 1050°C, in high-vacuum and low-vacuum modes in order to evaluate its possibilities through signal-to-noise ration measurements and different applications. Four examples of material transformations occurring at high temperature are herein reported: grain growth during annealing of a rolled platinum foil, recrystallisation of a multiphased alloy, oxidation of a Ni-based alloy and complex phase transformations occurring during the annealing of an Al-Si coated boron steel. The detector could be potentially adapted to any type of SEM and it offers good opportunities to perform high-temperature experiments in various atmospheres.