Microwave-induced porosity and bioactivation of chitosan-PEGDA scaffolds: morphology, mechanical properties and osteogenic differentiation.

In this study, a new foaming method, based on physical foaming combined with microwave-induced curing, is proposed in combination with a surface bioactivation to develop scaffold for bone tissue regeneration. In the first step of the process, a stable physical foaming was induced using a surfactant (Pluronic) as blowing agent of a homogeneous blend of Chitosan and polyethylene glycol diacrylate (PEGDA700) solutions. In the second step, the porous structure of the foaming was chemically stabilized by radical polymerization induced by homogeneous heating of the sample in a microwave reactor. In this step, 2,2-azobis[2-(2-imidazolin-2yl)propane]dihydrochloride was used as thermoinitiator (TI). Chitosan and PEGDA were mixed in different blends to investigate the influence of the composition on the final properties of the material. The chemical properties of each sample were evaluated by infrared attenuated total reflectance analysis, before and after curing in order to maximize reaction yield and optimize kinetic parameters (i.e. time curing, microwave power). Absorption capacity, elastic modulus, porosity and morphology of the porous structure were measured for each sample. The stability of materials was evaluated in vitro by degradation test in phosphate-buffered saline. To improve the bioactivity and biological properties of chitosan scaffold, a biomineralization process was used. Biological characterization was carried out with the aim to prove the effect of biomineralization scaffold on human mesenchymal stem cells behaviour. Copyright © 2016 John Wiley & Sons, Ltd.

Cellulose-based porous scaffold for bone tissue engineering applications: Assessment of hMSC proliferation and differentiation.

Physical foaming combined with microwave-induced curing was used in this study to develop an innovative device for bone tissue regeneration. In the first step of the process, a stable physical foaming was induced using a surfactant (i.e. pluronic) as blowing agent of a homogeneous blend of Sodium salt of carboxymethylcellulose (CMCNa) and polyethylene glycol diacrylate (PEGDA700) solution. In the second step, the porous structure of the scaffold was chemically stabilized by radical polymerization induced by a homogeneous rapid heating of the sample in a microwave reactor. In this step 2,2-Azobis[2-(2-imidazolin-2 yl)propane]Dihydrochloride was used as thermoinitiator (TI). CMCNa and PEGDA were mixed with different blends to correlate the properties of final product with the composition. The chemical properties of each sample were evaluated by spectroscopy analysis ATR-IR (before and after curing) in order to maximize reaction yield, and optimize kinetic parameters (i.e. time curing, microwave power). The stability of the materials was evaluated in vitro by degradation test in Phosphate Buffered Saline. Biological analyses were performed to evaluate the effect of scaffold materials on cellular behavior in terms of proliferation and early osteogenic differentiation of human Mesenchymal Stem Cells. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 104A: 726-733, 2016.

Effects on growth and osteogenic differentiation of mesenchymal stem cells by the strontium-added sol-gel hydroxyapatite gel materials.

In the present study, strontium-modified hydroxyapatite gels (Sr-HA) at different concentrations were prepared using sol-gel approach and their effect on human-bone-marrow-derived mesenchymal stem cells, were evaluated. The effect of Strontium on physico-chemical and morphological properties of hydroxyapatite gel were evaluated. Morphological analyses (SEM and TEM) demonstrate that an increasing in the amount of Sr ions doped into HA made the agglomerated particles smaller. The substitution of large Sr2+ for small Ca2+ lead to denser atomic packing of the system causing retardation of crystals growth. The biological results demonstrated that hydroxyapatite gel containing from 0 to 20 mol% of Sr presented no cytotoxicity and promote the expression of osteogenesis related genes including an early marker for osteogenic differentiation ALP; a non-collagen protein OPN and a late marker for osteogenic differentiation OCN. Finally, the Sr-HA gels could have a great potential application as filler in bone repair and regeneration and used in especially in the osteoporotic disease.

Preparation and characterization of cellulose-based foams via microwave curing.

In this work, a mixture of a sodium salt of carboxymethylcellulose (CMCNa) and polyethylene glycol diacrylate (PEGDA700) was used for the preparation of a microporous structure by using the combination of two different procedures. First, physical foaming was induced using Pluronic as a blowing agent, followed by a chemical stabilization. This second step was carried out by means of an azobis(2-methylpropionamidine)dihydrochloride as the thermoinitiator (TI). This reaction was activated by heating the sample homogeneously using a microwave generator. Finally, the influence of different CMCNa and PEGDA700 ratios on the final properties of the foams was investigated. The viscosity, water absorption capacity, elastic modulus and porous structure were evaluated for each sample. In addition, preliminary biological characterization was carried out with the aim to prove the biocompatibility of the resulting material. The foam, including 20% of PEGDA700 in the mixture, demonstrated higher viscosity and stability before thermo-polymerization. In addition, increased water absorption capacity, mechanical resistance and a more uniform microporous structure were obtained for this sample. In particular, foam with 3% of CMCNa shows a hierarchical structure with open pores of different sizes. This morphology increased the properties of the foams. The full set of samples demonstrated an excellent biocompatibility profile with a good cell proliferation rate of more than 7 days.