Correction: Fang et al. Study on Dispersion, Adsorption, and Hydration Effects of Polycarboxylate Superplasticizers with Different Side Chain Structures in Reference Cement and Belite Cement. Materials 2023, 16, 4168.

In the original publication [...].

Study on the Effect of Main Chain Molecular Structure on Adsorption, Dispersion, and Hydration of Polycarboxylate Superplasticizers.

Polycarboxylate ether (PCE) with different main chain structures was prepared by aqueous solution free radical polymerization using unsaturated acids containing sulfonic acid groups, acrylamide groups, and carboxyl groups and isoprenyl polyoxyethylene ether (IPEG). The molecular structure was characterized by infrared spectroscopy and gel chromatography, while adsorption, dispersion, and hydration properties were studied using a total organic carbon analyzer, rheometer, and isothermal microcalorimeter, respectively. The results show that the adsorption process of PCE on cement particles is spontaneous physical adsorption. The adsorption forces are mainly electrostatic interaction, and hydrogen bonding. The introduction of sulfonic acid groups and polycarboxylic acid groups reduces the initial adsorption amount of PCE but can accelerate the adsorption rate of PCE on cement and increase the adsorption amount at the adsorption equilibrium. The introduction of acrylamide groups in the PCE main chain is beneficial to the initial dispersion of PCE and can reduce the plastic viscosity of cement slurry. PCE can delay the hydration of cement. The introduction of acrylamide groups and dicarboxylic acid groups in the PCE main chain helps prolong the induction period of cement hydration, while the introduction of sulfonic acid groups is not conducive to its retarding effect.

Study on Dispersion, Adsorption, and Hydration Effects of Polycarboxylate Superplasticizers with Different Side Chain Structures in Reference Cement and Belite Cement.

To investigate the effects of Reference cement (RC) and Belite cement (LC) systems, different molecular structures of polycarboxylate ether (PCE) were prepared through the free radical polymerization reaction and designated as PC-1 and PC-2. The PCE was characterized and tested using a particle charge detector, gel permeation chromatography, a rotational rheometer, a total organic carbon analyzer, and scanning electron microscopy. The results showed that compared to PC-2, PC-1 exhibited higher charge density and better molecular structure extension, with smaller side-chain molecular weight and molecular volume. PC-1 demonstrated enhanced adsorption capacity in cement, improved initial dispersibility of cement slurry, and a reduction in slurry yield stress of more than 27.8%. LC, with its higher C2S content and smaller specific surface area compared to RC, could decrease the formation of flocculated structures, resulting in a reduction in slurry yield stress of over 57.5% and displaying favorable fluidity in cement slurry. PC-1 had a greater retarding effect on the hydration induction period of cement compared to PC-2. RC, which had a higher C3S content, could adsorb more PCE, leading to a greater retarding effect on the hydration induction period compared to LC. LC and PC-2, on the other hand, exhibited inhibition during the hydration acceleration period. The addition of PCE with different structures did not significantly affect the morphology of hydration products in the later stage, which was consistent with the trend of KD variation. This indicates that the analysis of hydration kinetics can better reflect the final hydration morphology.