ABSTRACT
We designed a cascaded all-soft-glass fiber structure and simulate midinfrared 2-20 µm ultrawideband supercontinuum (SC) generation numerically. The cascaded fiber structure consists of a 1.5 m I n F 3 fiber, a 0.2 m chalcogenide photonic crystal fiber, and a 0.2 m tellurium-based chalcogenide photonic crystal fiber. Using a 2 µm pulse pumping this cascaded structure, the generated SC covering the wavelengths longer than 20 µm has been demonstrated theoretically. The 30 dB bandwidth reaches 20.87 µm from 1.44 to 22.31 µm. The effect of different pulse widths on SC generation is considered. With the increase of peak power and the decrease of pulse width, the energy of SC in the 15-20 µm waveband increases gradually. The mechanism of SC broadening process has also been analyzed. The SC generation of more than 20 µm in this cascade structure is caused by the self-phase modulation, soliton effects, four-wave mixing, and redshifted dispersive wave. This method demonstrates the possibility of generating ultrawide bandwidth SCs up to a 20 µm waveband by a commercial 2 µm pump source and all-fiber structure.
ABSTRACT
We demonstrated an efficient way to enhance and flatten the emission cross sections of Er3+ ions at the L-band in the silicate fiber amplifier by increasing Mg2+ (up to 22.5â mol%) with high field strength. High values of Er3+ concentration, lifetime, and L-band emission cross section were achieved in our silicate fibers. Particularly, the flatness at the L-band was achieved to be 0.8â dB, and a high gain coefficient at 1625â nm (4.7â dB/m) was demonstrated by pumping meter-scale Er-silicate fibers. The as-prepared Er-silicate fibers are attractive for the L-band fiber amplifier.