Photocatalytic H2 production and degradation of aqueous 2-chlorophenol over B/N-graphene-coated Cu0/TiO2: A DFT, experimental and mechanistic investigation.

Energy and environmental challenges are global concerns that scientists are interested in alleviating. It is on this premise that we prepared boron/nitrogen graphene-coated Cu0/TiO2 (B/N-graphene-coated Cu/TiO2) photocatalyst of varying B:N ratios with dual functionality of H2 production and 2-Chlorophenol (2-CP) degradation. In-situ coating of Cu0 with B/N-graphene is achieved via solvothermal synthesis and calcination under an inert atmosphere. All B/N-graphene-coated Cu/TiO2 exhibit higher photonic efficiencies (5.68%-7.06% at 300 < λ < 400 nm) towards H2 production than bare TiO2 (0.25% at 300 < λ < 400 nm). Varying the B:N ratio in graphene influences the efficiency of H2 generation. A B:N ratio of 0.08 yields the most active composite exhibiting a photonic efficiency of 7.06% towards H2 evolution and a degradation rate of 4.07 × 10-2 min-1 towards 2-chlorophenol (2-CP). Density functional theory (DFT) investigations determine that B-doping (p-type) enhances graphene stability on Cu0 while N-doping (n-type) increases the reduction potential of Cu0 relative to H+ reduction potential. X-ray photoelectron spectroscopy reveals that increasing the B:N ratio increases p-type BC2O while decreasing n-type pyridinic-N in graphene thus altering the interlayer electron density. Isotopic labelling experiments determine water reduction as the main mechanism by which H2 is produced over B/N-graphene-coated Cu/TiO2. The reactive species involved in the degradation of 2-CP are holes (h+), hydroxyl radical (OH•), and O2•-, of which superoxide (O2•-) plays the major role. This work displays B/N -graphene-coated Cu/TiO2 as a potential photocatalyst for large-scale H2 production and 2-CP degradation.

Nitrogen/Carbon-Coated Zero-Valent Copper as Highly Efficient Co-catalysts for TiO2 Applied in Photocatalytic and Photoelectrocatalytic Hydrogen Production.

Zero-valent copper (Cu0) is a promising co-catalyst in semiconductor-based photocatalysis as it is inexpensive and exhibits electronic properties similar to those of Ag and Au. However, its practical application in photocatalytic hydrogen production is limited by its susceptibility to oxidation, forming less active Cu species. Herein, we have carried out in situ encapsulation of Cu0 nanoparticles with N-graphitic carbon layers (14.4% N) to stabilize Cu0 nanoparticles (N/C-coated Cu) and improve the electronic communication with a TiO2 photocatalyst. A facile solvothermal procedure is used to coat the Cu0 nanoparticles at 200 °C, while graphitization is achieved by calcination at 550 °C under an inert atmosphere. The resultant N/C-coated Cu/TiO2 composites outperform the uncoated Cu counterparts, exhibiting a 27-fold enhancement of the hydrogen evolution rate compared to TiO2 and achieving a rate of 19.03 mmol g-1 h-1 under UV-vis irradiation. Likewise, the N/C-coated Cu co-catalyst exhibits a less negative onset potential of -0.05 V toward hydrogen evolution compared to uncoated Cu (ca. -0.30 V). This superior activity is attributed to coating Cu0 with N/C, which enhances the stability, electronic communication with TiO2, conductivity, and interfacial charge transfer processes. The reported synthetic approach is simple and scalable, yielding an efficient and affordable Cu0 co-catalyst for TiO2.