ABSTRACT
Sodium-sulfur (Na-S) batteries are attracting intensive attention due to the merits like high energy and low cost, while the poor stability of sulfur cathode limits the further development. Here, we report a chemical and spatial dual-confinement approach to improve the stability of Na-S batteries. It refers to covalently bond sulfur to carbon at forms of C-S/N-C=S bonds with high strength for locking sulfur. Meanwhile, sulfur is examined to be S1-S2 small species produced by thermally cutting S8 large molecules followed by sealing in the confined pores of carbon materials. Hence, the sulfur cathode achieves a good stability of maintaining a high-capacity retention of 97.64% after 1000 cycles. Experimental and theoretical results show that Na+ is hosted via a coordination structure (N···Na···S) without breaking the C-S bond, thus impeding the formation and dissolution of sodium polysulfide to ensure a good cycling stability. This work provides a promising method for addressing the S-triggered stability problem of Na-S batteries and other S-based batteries.
ABSTRACT
Gas drainage is an important method to prevent and control gas disasters. Sealing materials have an important impact on the gas drainage effect. To improve the extraction rate, the configuration and related characteristics of sealing materials were studied in this study. It was found that the fluidity increased gradually with the increase of the dosage of the suspension concentrate (SC). The water-cement ratio was directly proportional to the setting time of the slurry. Also, the mixing amount of the special cement was inversely proportional to the setting time of the slurry. The influence of the amount of foaming agent, special cement, and suspending agent on the expansion rate of the slurry was positive, and the influence gradually weakened. When the water-cement ratio of cement-based materials was 0.6, the special cement content percentage was 6, the suspension agent content percentage was 3, the plasticizer content percentage was 0.7, the early strength agent content percentage was 1.2, and the foaming agent content percentage was 0.2, the sealing effect was the best. The research results suggest that the porosity and pore length of the cement-based material are smaller than those of polyurethane, and its sealing property was better. This could further increase the sealing effect of the gas borehole, thereby facilitating gas extraction.