Electrochemical and statistical study of Nickel ion assessment in daily children intake samples relying on magnesium aluminate spinel nanoparticles.

Lately, children's daily consumption of some products, such as cereals and candies, has been rising, which provides a compelling rationale for determining any metallic substances that may be present. Monitoring the concentration of certain metals, like nickel, in these products is necessary due to medical issues in humans when consumed regularly. So, in this work, a novel and highly selective carbon paste as a Ni(II) ion-selective sensor was prepared and investigated using ceramic magnesium aluminum spinel nanoparticles as the ionophore and tritolyl phosphate (TOCP) as a plasticizer. A modified co-precipitation method was used to synthesize the spinel nanoparticles. X-ray diffraction, scanning electron microscope with EDAX, transmission electron microscope, and BET surface area were used to determine the phase composition, microstructure, pores size, particle size, and surface area of the synthesized nanoparticles. The spinel nanoparticle was found to have a nano crystallite size with a cubic crystal system, a particle size ranging from 17.2 to 51.52 nm, mesoporous nature (average pore size = 8.72 nm), and a large surface area (61.75 m2/g). The composition ratio of graphite carbon as a base: TOCP as binder: spinal as ionophore was 67.3:30.0:2.7 (wt%) based on potentiometric detections over concentrations from 5.0 × 10-8 to 1.0 × 10-2 mol L-1 with LOD of 5.0 × 10-8 mol L-1. A measurement of 29.22 ± 0.12 mV decade-1 over pH 2.0-7.0 was made for the Nernstian slope. This sensor demonstrated good repeatability over nine weeks and a rapid response of 8 s. A good selectivity was shown for Ni(II) ions across many interferents, tri-, di-, and monovalent cations. The Ni(II) content in spiked real samples, including cocaine, sweets, coca, chocolate, carbonated drinks, cereals, and packages, were measured. The results obtained indicated no significant difference between the proposed potentiometric method and the officially reported ICP method according to the F- and t-test data. In addition to utilizing ANOVA statistical analysis, validation procedures have been implemented, and the results exceed the ICP-MS methodology.

Ball billing induced highly dispersed nano-MgO in biochar for glucose isomerization at low temperatures.

The isomerization of glucose is a crucial step for biomass valorization to downstream chemicals. Herein, highly dispersed MgO doped biochar (BM-0.5@450) was prepared from rice straw via a solvent-free ball milling pretreatment and pyrolysis under nitrogen conditions. The nano-MgO doped biochar demonstrated enhanced conversion of glucose in water at low temperatures. A 31 % yield of fructose was obtained from glucose over BM-0.5@450 at 50 °C with 80.0 % selectivity. At 60 °C for 140 min, BM-0.5@450 achieved a 32.5 % yield of fructose. Compared to catalyst synthesized from conventional impregnation method (IM@450), the BM-0.5@450 catalyst shows much higher fructose yields (32.5 % vs 25.9 %), which can be attributed to smaller crystallite size of MgO (11.32 nm vs 19.58 nm) and homogenous distribution. The mechanism study shows that the activated MgOH+·OH- group by water facilitated the deprotonation process leading to the formation of key intermediate enediol.

A sustainable and economical solution for CO2 capture with biobased carbon materials derived from palm kernel shells.

This study investigates the synthesize of activated carbon for carbon dioxide adsorption using palm kernel shell (PKS), a by-product of oil palm industry. The adsorbent synthesis involved a simple two-step carbonization method. Firstly, PKS was activated with potassium oxide (KOH), followed by functionalization with magnesium oxide (MgO). Surface analysis revealed that KOH activated PKS has resulted in a high specific surface area of 1086 m2/g compared to untreated PKS (435 m2/g). However, impregnation of MgO resulted in the reduction of surface area due to blockage of pores by MgO. Thermogravimetric analysis (TGA) demonstrated that PKS-based adsorbents exhibited minimal weight loss of less than 30% up to 500 °C, indicating their suitability for high-temperature applications. CO2 adsorption experiments revealed that PKS-AC-MgO has achieved a higher adsorption capacity of 155.35 mg/g compared to PKS-AC (149.63 mg/g) at 25 °C and 5 bars. The adsorption behaviour of PKS-AC-MgO was well fitted by both the Sips and Langmuir isotherms, suggesting a combination of both heterogeneous and homogeneous adsorption and indicating a chemical reaction between MgO and CO2. Thermodynamic analysis indicated a spontaneous and thermodynamically favourable process for CO2 capture by PKS-AC-MgO, with negative change in enthalpy (- 0.21 kJ/mol), positive change in entropy (2.44 kJ/mol), and negative change in Gibbs free energy (- 729.61 J/mol, - 790.79 J/mol, and - 851.98 J/mol) across tested temperature. Economic assessment revealed that the cost of PKS-AC-MgO is 21% lower than the current market price of commercial activated carbon, indicating its potential for industrial application. Environmental assessment shows a significant reduction in greenhouse gas emissions (381.9 tCO2) through the utilization of PKS-AC-MgO, underscoring its environmental benefits. In summary, the use of activated carbon produced from PKS and functionalised with MgO shows great potential for absorbing CO2. This aligns with the ideas of a circular economy and sustainable development.

Composite bone graft of CaO-MgO-SiO2 glass-ceramics and CaSO4 ceramics for boosting bone formation rate.

This study develops a composite bone graft of CaO-MgO-SiO2 glass-ceramic and CaSO4 [abbreviated as (CMS)3-x(CS)x] via the sponge replication technique with weight fractions of x = 0, 1, 1.5, 2, and 3. The (CMS)1.5(CS)1.5 composite displays a superior degradability and, a suitable compressive strength of ∼3 MPa, and excellent cell proliferation and differentiation. The in vivo rat femur test in the hybrid-pore (CMS)1.5(CS)1.5 composite granules achieves a higher rate of bone formation, which is ∼2.7 times better than that of the commercial HAP/ß-TCP at 12 weeks. Improved expressions of osteocyte and mature osteocyte marker genes, namely (Spp1, Dmp1, and Fgf23), were observed in the (CMS)1.5(CS)1.5 group, indicating a faster differentiation into mature bone tissue. The ions release of (CMS)1.5(CS)1.5 through the ERK1/2 signaling pathway promotes osteogenic differentiation. The high bone generation rate can be attributed to faster active ions release and modified surface topography. This work highlights an excellent bone graft candidate for clinical applications in orthopedic surgery.

The role of magnesium oxide foliar sprays in enhancing mint (Mentha crispa L.) tolerance to cadmium stress.

This study investigates using magnesium foliar spray to enhance mint plants' growth and physiological performance under cadmium toxicity. It examines the effects of foliar application of magnesium oxide (40 mg L-1), in both nano and bulk forms, on mint plants exposed to cadmium stress (60 mg kg-1 soil). Cadmium stress reduced root growth and activity, plant biomass (32%), leaf hydration (19%), chlorophyll levels (27%), magnesium content (51%), and essential oil yield (35%), while increasing oxidative and osmotic stress in leaf tissues. Foliar application of magnesium increased root growth (32%), plant biomass, essential oil production (17%), leaf area (24%), chlorophyll content (10%), soluble sugar synthesis (33%), and antioxidant enzyme activity, and reduced lipid peroxidation and osmotic stress. Although the nano form of magnesium enhanced magnesium absorption, its impact on growth and physiological performance was not significantly different from the bulk form. Therefore, foliar application of both forms improves plants' ability to withstand cadmium toxicity. However, the study is limited by its focus on a single plant species and specific environmental conditions, which may affect the generalizability of the results. The long-term sustainability of such treatments could provide a more comprehensive understanding of magnesium's role in mitigating heavy metal stress in plants.

Synergetic impact of MgO on PMMA-ZrO2 hybrid composites: Evaluation of structural, morphological and improved mechanical behavior for dental applications.

This work aims to demonstrate the effect of ZrO2 and MgO inclusion into the Poly(methyl methacrylate) (PMMA). To fabricate novel hybrid composites via heat cure method, various composites (PZM2, PZM4 and PZM6) were synthesized in the system [(95-x) PMMA + 5 ZrO2 + x MgO] (x = 2, 4, and 6) respectively. Density of the prepared composites were determined and varying between 1.035-1.152 g/cm3. X-ray Diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM) followed by EDAX and mechanical testing were performed to evaluate the fabricated composite properties. Moreover, to explore the structure of the fabricated composites the 13 C CP-MAS SSNMR and 1 H-13 C Phase-Modulated Lee Goldberg (PMLG) HETCOR Spectrum were recorded which clarify chemical shifting and motional dynamics of the composites. Mechanical tests were performed by UTM and the obtained parameters such as compressive strength, Young's modulus, fracture toughness, brittleness coefficient, flexural strength and flexural modulus are found to be in the range of 91-100 MPa, 0.48-0.51 GPa, 9.122-9.705 MPa.m1/2, 0.66-0.815, 51.03-42.78 MPa and 499-663 MPa respectively. Some more mechanical parameters such as proportional limit, elastic limit, failure strength, modulus of resilience and modulus of toughness were also calculated. Furthermore, tribological properties were also determined and the coefficient of friction (COF) was decreased by 17.4 % and 38 % for composite PZM6 at 20 N and 40 N as compared to the composite PZM2 and the lowest wear volume of 1.55 mm3 was observed for PZM2, whereas the maximum volume loss of 5.64 mm3 is observed for composite PZM6. To check out the biocompatibility, cytotoxicity and genotoxicity of the fabricated composites the Trypan-blue assay was also performed for PZM2 and PZM6 composites. Dissection on the gut of larvae was also performed on the both composites followed by DAPI and DCFH-DA staining. Therefore, these synthesized samples can be used for the fabrication of denture materials.

Green hydrothermal synthesis and characterization of Ag2O-supported MgO/rGO nanocomposites by using Phoenix leaf extract: a promising approach for enhanced photocatalytic and anticancer activities.

The present work was designed to synthesize Ag2O-supported MgO/rGO nanocomposites (NCs) via green method using Phoenix leaf extract for improved photocatalytic and anticancer activity. Green synthesized Ag2O-supported MgO/rGO NCs were characterized through X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), X-ray photoelectron spectroscopy (XPS), Raman, ultraviolet-visible (UV-vis) spectroscopy, and photoluminescence (PL) spectroscopy, and gas chromatography-mass spectroscopy (GC-MS) was applied to examine the chemical components of the Phoenix leaf extract. Characterization data confirmed the preparation of MgO NPs, Ag2O-MgO NCs, and Ag2O-MgO/rGO NC with particle size of 26-28 nm. UV-vis study exhibited that the band gap energy of MgO NPs, Ag2O-MgO NCs, and Ag2O-MgO/rGO NC were in the range of 3.53-3.43 eV. The photocatalytic results showed that the photodegradation of Rh B dye of Ag2O-supported MgO/rGO NCs (82.81%) was significantly higher than pure MgO NPs. Additionally, the biological response demonstrates that the Ag2O-supported MgO/rGO NCs induced high cytotoxicity against MCF-7 cancer cells for 24 h and 48 h compared with both pure MgO NPs and Ag2O-MgO NCs. This study suggests that the adding of Ag2O and rGO sheets played significant role in the enhanced photocatalytic and anticancer performance of MgO NPs.

Synergistic effect of green synthesis magnesium oxide nanoparticles and seaweed extract on improving water quality, health benefits, and disease resistance in Nile tilapia.

This study aimed to evaluate the effect of adding liquid extract of algae (Hypnea musciformis, Grateloupia acuminata, and Sargassum muticum) (HGS) and Magnesium oxide nanoparticles (MgO NPs) using this extract to rear water of Oreochromis niloticus, on improving culture water indices, growth performance, digestive enzyme, hemato-biochemical characters, immune, antioxidative responses, and resistance after challenged by Aeromonas hydrophila with specific refer to the potential role of the mixture in vitro as resistance against three strains bacteria (Aeromonas sobria, Pseudomonas fluorescens, P. aeruginosa) and one parasite (Cichlidogyrus tilapia). The first group represented control, HGS0, whereas the other group, HGS5, HGS10, and HGS15 mL-1 of liquid extract, as well as all groups with 7.5 µg mL-1 MgO-NPs added to culture water of O. niloticus, for 60 days. Data showed that increasing levels at HGS 10 and HGS15 mL-1 in to-culture water significantly enhanced growth-stimulating digestive enzyme activity and a significantly improved survival rate of O. niloticus after being challenged with A. hydrophila than in the control group. The total viability, coliform, fecal coliform count, and heavy metal in muscle partially decreased at HGS 10 and HGS15 mL-1 than in the control group. Correspondingly, the highest positive effect on hemato-biochemical indices was noticed at levels HGS 10 and HGS15 mL-1. Fish noticed an improvement in immune and antioxidant indices compared to control groups partially at HGS 10 and HGS15 mL-1. Interestingly, fish cultured in rearing water with the mixture provided downregulated the related inflammatory genes (HSP70, TNF, IL-1ß, and IL-8) partially at HGS15 mL-1. In vitro, the mixture showed positive efficiency as an antibacterial and partially antiparasitic at HGS 10 and HGS15 mL-1. This study proposes utilizing a mixture of (HGS) and (MgO-NPs) with optimum levels of 10-15 mL-1 in cultured water to improve water indices, growth, health status, and increased resistance of O. niloticus against bacterial and parasitic infection.

Exploring the diverse performance of nickel and cobalt spinel ferrite nanoparticles in hazardous pollutant removal and gas sensing performance.

A simple sol-gel combustion process was employed for the creation of MFe2O4 (M=Ni, Co) nanoparticles. The synthesized nanoparticles, acting as both photocatalysts and gas sensors, were analyzed using various analytical techniques. MFe2O4 (M=Ni, Co) material improved the degradation of methylene blue (MB) under UV-light irradiation, serving as an enhanced electron transport medium. UV-vis studies demonstrated that NiFe2O4 achieved a 60% degradation, while CoFe2O4 nanostructure exhibited a 76% degradation efficacy in the MB dye removal process. Furthermore, MFe2O4 (M=Ni, Co) demonstrated chemosensitive-type sensor capabilities at ambient temperature. The sensor response and recovery times for CoFe2O4 at a concentration of 100 ppm were 15 and 20, respectively. Overall, the synthesis of MFe2O4 (M=Ni, Co) holds the potential to significantly improve the photocatalytic and gas sensing properties, particularly enhancing the performance of CoFe2O4. The observed enhancements make honey MFe2O4 (M=Ni, Co) a preferable choice for environmental remediation applications.

Insight into mechanism of excellent visible-light photocatalytic activity of CuO/MgO/ZnO nanocomposite for advanced solution of environmental remediation.

Environmental remediation has sought several innovative ways for the treatment of wastewater and captivated researchers around the globe towards it. Through this study, we aim to proceed with the efforts to foster sustainable and feasible ways for the treatment of wastewater. In this work, we report the sol-gel synthesis of CuO/MgO/ZnO nanocomposite and carry out their systematic characterization with the help of state-of-the-art analytical techniques, such as FTIR, SEM, TEM, PL, XRD, Raman, and AFM. The SEM along with TEM and AFM provided useful insights into the surface morphology of the synthesized nanocomposite on both 2D and 3D surfaces and concluded the well-dispersed behavior of the nanocomposite. The characteristic functional groups responsible for carrying out the reaction of Cu-O, Mg-O, and Zn-O were identified by FTIR spectroscopy. On the other hand, crystal size, dislocation density, and microstrain of the nanocomposite were calculated by XRD. For optical studies, photoluminescence spectroscopy was performed. Once the characterization of the nanocomposite was done, they were eventually treated against the toxic organic dye, methylene blue. The calculated rate constant values of k for CuO was 2.48 × 10-3 min-1, for CuO/MgO (2.04 × 10-3 min-1), for CuO/ZnO (1.82 × 10-3 min-1) and CuO/MgO/ZnO was found to be 2.00 × 10-3 min-1. It has become increasingly evident that nanotechnology can be used in various facets of modern life, and its implementation in wastewater treatment has recently received much attention.

Controlled delivery of procyanidin through magnesium oxide nanoparticles (MgO NPs) to improve the activity and mineralization of osteoblasts under oxidative stressin vitro.

Excessive reactive oxygen species (ROS) in the microenvironment of osteoporosis (OP) not only accelerate the bone absorption, but also affect the osteogenic and mineralized effect of osteoblasts. Procyanidins (PC) have been reported to have anti-oxidation effects, but low bioavailability. This study aimed to explore the effect of magnesium oxide nanoparticles (MgO-PC NPs)-loaded PC on the osteogenesis and mineralization of osteoblasts that stimulated by H2O2. PC was loaded onto MgO NPs and characterized by transmission electron microscopy, energy dispersive spectroscopy, dynamic light scattering, and Fourier transform infrared spectroscopy. After primary screening by cytotoxicity assay, MgO-PC NPs containing 20 µM of PC were chosen for further studies. In H2O2-stimulated osteoblasts, dichlorodihydrofluorescein diacetate probe, Cell Counting Kit-8, quantitative real-time polymerase chain reaction, alkaline phosphatase staining/activity and Alizarin red staining were used to detect the ROS production, cell viability and osteogenic and mineralized markers of osteoblasts. PC was loaded onto MgO NPs to successfully receive MgO-PC NPs with a diameter of about 144 nm and negative potential. PC can sustain release from MgO-PC NPs for at least 16 d. The controlled release of PC from MgO-PC NPs can effectively eliminate ROS and thereby promoted the cell activity. Most importantly, the osteogenesis and mineralization of osteoblasts under oxidative stress were also significantly reversed by MgO-PC NPS. Thus, these findings indicate that MgO-PC NPs may be developed as a potential therapeutic strategy for OP.

Low-temperature thermocatalytic removal of formaldehyde in air using copper manganite spinels.

The removal of formaldehyde (FA) is vital for indoor air quality management in light of its carcinogenic propensity and adverse environmental impact. A series of copper manganite spinel structures (e.g., CuMn2O4) are prepared using the sol-gel combustion method and treated with reduction or oxidation pretreatment at 300 °C condition. Accordingly, CuMn2O4-O ("O" suffix for oxidation pre-treatment in air) is identified as the best performer to achieve 100% conversion (XFA) of FA (50 ppm) at 90 °C; its performance, if assessed in terms of reaction kinetic rate (r) at XFA = 10%, is 5.02E-03 mmol g-1 h-1. The FA removal performance increases systematically with decreases in flow rate, FA concentration, and relative humidity (RH) or with increases in bed mass. The reaction pathways and intermediates of FA catalytic oxidation on CuMn2O4-A are studied with density functional theory simulations, temperature-programmed characterization experiments, and in-situ diffuse reflectance infrared Fourier transform spectroscopy. The synergistic combination of large quantities of adsorbed oxygen (OA) species and oxidized metal species (e.g., Cu2+) contribute to the enhanced catalytic performance of CuMn2O4-O to oxidize FA into CO2 with the reaction intermediates of H2CO2 (DOM), HCOO-, and CO. The present study is expected to provide valuable insights into the thermocatalytic oxidation of FA over spinel CuMn2O4 materials and their catalytic performances in relation to the key process variables.

Comparative evaluation of antimicrobial activity of spinel structured transition metal ferrites supported on reduced graphene oxide against pathogenic strains of bacteria and fungi.

One of the global challenges for living things is to provide pollution and harmful microbes-free environment. In this study, magnetically retrievable spinel-structured manganese zinc ferrite (Mn0.5Zn0.5Fe2O4) (MZF) was synthesized by a facile solvothermal method. Further, the MZF with different weight percentages (10 wt%, 50 wt%, and 80 wt%) were supported on reduced graphene oxide (rGO). The phase purity and morphology of MZF and MZF/rGO nanocomposite were confirmed by x-ray diffraction technique and scanning electron microscopy, respectively. The Fourier transform infrared spectroscopy, Raman, UV-visible spectroscopy, and thermogravimetric analyses of the as-synthesized nanocomposites were examined for the detection of various chemical groups, band gap, and thermal properties, respectively. The MZF/rGO nanocomposite exhibited significant antibacterial and antifungal activity againstEggerthella lenta, Enterococcus faecalis, Klebsiella pneumonia, Pseudomonas aeruginosa,andCandida albicanscompared to bare MZF and rGO. The high surface area of rGO plays a crucible role in antimicrobial analysis. Additionally, the antibacterial and antifungal activity is compared by synthesizing various metal ferrites such as MnFe2O4, ZnFe2O4, and Fe3O4. The 50 wt% MZF/rGO nanocomposite exhibits significantly high antibacterial activity. However, 10 wt% MZF/rGO nanocomposite shows good antifungal activity than Fe3O4, MnFe2O4, ZnFe2O4, MnZnFe2O4, 50 wt%, and 80 wt% MZF/rGO nanocomposites. These findings suggest that the prepared ferrite nanocomposites hold promise for microbial inhibition.

Magnetic Graphene Oxide Nanocomposites Boosts Craniomaxillofacial Bone Regeneration by Modulating circAars/miR-128-3p/SMAD5 Signaling Axis.

Background: The ability of nanomaterials to induce osteogenic differentiation is limited, which seriously imped the repair of craniomaxillofacial bone defect. Magnetic graphene oxide (MGO) nanocomposites with the excellent physicochemical properties have great potential in bone tissue engineering. In this study, we aim to explore the craniomaxillofacial bone defect repairment effect of MGO nanocomposites and its underlying mechanism. Methods: The biocompatibility of MGO nanocomposites was verified by CCK8, live/dead staining and cytoskeleton staining. The function of MGO nanocomposites induced osteogenic differentiation of BMSCs was investigated by ALP activity detection, mineralized nodules staining, detection of osteogenic genes and proteins, and immune-histochemical staining. BMSCs with or without MGO osteogenic differentiation induction were collected and subjected to high-throughput circular ribonucleic acids (circRNAs) sequencing, and then crucial circRNA circAars was screened and identified. Bioinformatics analysis, Dual-luciferase reporter assay, RNA binding protein immunoprecipitation (RIP), fluorescence in situ hybridization (FISH) and osteogenic-related examinations were used to further explore the ability of circAars to participate in MGO nanocomposites regulation of osteogenic differentiation of BMSCs and its potential mechanism. Furthermore, critical-sized calvarial defects were constructed and were performed to verify the osteogenic differentiation induction effects and its potential mechanism induced by MGO nanocomposites. Results: We verify the good biocompatibility and osteogenic differentiation improvement effects of BMSCs mediated by MGO nanocomposites. Furthermore, a new circRNA-circAars, we find and identify, is obviously upregulated in BMSCs mediated by MGO nanocomposites. Silencing circAars could significantly decrease the osteogenic ability of MGO nanocomposites. The underlying mechanism involved circAars sponging miR-128-3p to regulate the expression of SMAD5, which played an important role in the repair craniomaxillofacial bone defects mediated by MGO nanocomposites. Conclusion: We found that MGO nanocomposites regulated osteogenic differentiation of BMSCs via the circAars/miR-128-3p/SMAD5 pathway, which provided a feasible and effective strategy for the treatment of craniomaxillofacial bone defects.

Investigations of Major α-Dicarbonyl Content in U.S. Honey of Different Geographical Origins.

α-Dicarbonyls are significant degradation products resulting from the Maillard reaction during food processing. Their presence in foods can indicate the extent of heat exposure, processing treatments, and storage conditions. Moreover, they may be useful in providing insights into the potential antibacterial and antioxidant activity of U.S. honey. Despite their importance, the occurrence of α-dicarbonyls in honey produced in the United States has not been extensively studied. This study aims to assess the concentrations of α-dicarbonyls in honey samples from different regions across the United States. The identification and quantification of α-dicarbonyls were conducted using reverse-phase liquid chromatography after derivatization with o-phenylenediamine (OPD) and detected using ultraviolet (UV) and mass spectrometry methods. This study investigated the effects of pH, color, and derivatization reagent on the presence of α-dicarbonyls in honey. The quantification method was validated by estimating the linearity, precision, recovery, method limit of detection, and quantification using known standards for GO, MGO, and 3-DG, respectively. Three major OPD-derivatized α-dicarbonyls including methylglyoxal (MGO), glyoxal (GO), and 3-deoxyglucosone (3-DG), were quantified in all the honey samples. 3-Deoxyglucosone (3-DG) was identified as the predominant α-dicarbonyl in all the U.S. honey samples, with concentrations ranging from 10.80 to 50.24 mg/kg. The total α-dicarbonyl content ranged from 16.81 to 55.74 mg/kg, with the highest concentration measured for Southern California honey. Our results showed no significant correlation between the total α-dicarbonyl content and the measured pH solutions. Similarly, we found that lower amounts of the OPD reagent are optimal for efficient derivatization of MGO, GO, and 3-DG in honey. Our results also indicated that darker types of honey may contain higher α-dicarbonyl content compared with lighter ones. The method validation results yielded excellent recovery rates for 3-DG (82.5%), MGO (75.8%), and GO (67.0%). The method demonstrated high linearity with a limit of detection (LOD) and limit of quantitation (LOQ) ranging from 0.0015 to 0.002 mg/kg and 0.005 to 0.008 mg/kg, respectively. Our results provide insights into the occurrence and concentrations of α-dicarbonyl compounds in U.S. honey varieties, offering valuable information on their quality and susceptibility to thermal processing effects.

Biodiesel Production by Methanolysis of Rapeseed Oil-Influence of SiO2/Al2O3 Ratio in BEA Zeolite Structure on Physicochemical and Catalytic Properties of Zeolite Systems with Alkaline Earth Oxides (MgO, CaO, SrO).

Alkaline earth metal oxide (MgO, CaO, SrO) catalysts supported on BEA zeolite were prepared by a wet impregnation method and tested in the transesterification reaction of rapeseed oil with methanol towards the formation of biodiesel (FAMEs-fatty acid methyl esters). To assess the influence of the SiO2/Al2O3 ratio on the catalytic activity in the tested reaction, a BEA zeolite carrier material with different Si/Al ratios was used. The prepared catalysts were tested in the transesterification reaction at temperatures of 180 °C and 220 °C using a molar ratio of methanol/oil reagents of 9:1. The transesterification process was carried out for 2 h with the catalyst mass of 0.5 g. The oil conversion value and efficiency towards FAME formation were determined using the HPLC technique. The physicochemical properties of the catalysts were determined using the following research techniques: CO2-TPD, XRD, BET, FTIR, and SEM-EDS. The results of the catalytic activity showed that higher activity in the tested process was confirmed for the catalysts supported on the BEA zeolite characterized by the highest silica/alumina ratio for the reaction carried out at a temperature of 220 °C. The most active zeolite catalyst was the 10% CaO/BEA system (Si/Al = 300), which showed the highest triglyceride (TG) conversion of 90.5% and the second highest FAME yield of 94.6% in the transesterification reaction carried out at 220 °C. The high activity of this system is associated with its alkalinity, high value of the specific surface area, the size of the active phase crystallites, and its characteristic sorption properties in relation to methanol.

Application of some inorganic metal oxide nanoparticles to control E. coli in raw milk.

Background: Nanoparticles are regarded as magical bullets because of their exclusive features. Recently, the usage of nanoparticles has progressed in almost all aspects of science and technology due to its ability to revolutionize certain fields. In the field of food science and technology, the application of nanoparticles is being researched in many various areas thus provides the dairy industry with a variety of new attitudes for developing the quality, prolong shelf life, ensure the safety and healthiness of foods. Aim: This study aimed to focus on the application of some inorganic metal oxide nanoparticles (zinc oxide (ZnO), magnesium oxide (MgO), and calcium oxide (CaO)) to control E. coli in raw milk and ensure its safety. Methods: The antibacterial action of certain nanoparticles (ZnO, MgO, and CaO) with multiple concentrations (0.1, 0.05, 0.025, 0.0125, 0.006, and 0.003 mg/ml) was evaluated against E. coli strains in ultra heat treated (UHT) milk samples. Also, storage temperature and storage period effects were studied. Results: The findings of the current research revealed that inorganic metal oxide nanoparticles had a significant antibacterial role against E. coli, in the following order; ZnO, MgO, and CaO, respectively. The antibacterial effect of inorganic metal oxide nanoparticles is more noticeable at lower temperatures. Conclusion: Inorganic metal nanoparticles can be used in the food industry for the purpose of the control of E. coli, and extension of the shelf life of dairy products.

Butyrate increases methylglyoxal production through regulation of the JAK2/Stat3/Nrf2/Glo1 pathway in castration­resistant prostate cancer cells.

Cancer cells are characterized by increased glycolysis, known as the Warburg effect, which leads to increased production of cytotoxic methylglyoxal (MGO) and apoptotic cell death. Cancer cells often activate the protective nuclear factor erythroid 2­related factor2 (Nrf2)/glyoxalase1 (Glo1) system to detoxify MGO. The effects of sodium butyrate (NaB), a product of gut microbiota, on Nrf2/Glos/MGO pathway and the underlying mechanisms in prostate cancer (PCa) cells were investigated in the present study. Treatment with NaB induced the cell death and reduced the proliferation of PCa cells (DU145 and LNCap). Moreover, the protein kinase RNA-like endoplasmic reticulum kinase/Nrf2/Glo1 pathway was greatly inhibited by NaB, thereby accumulating MGO-derived adduct hydroimidazolone (MG-H1). In response to a high amount of MGO, the expression of Nrf2 and Glo1 was attenuated, coinciding with an increased cellular death. NaB also markedly inhibited the Janus kinase 2 (JAK2)/Signal transducer and activator of transcription 3 (Stat3) pathway. Conversely, co­treatment with Colivelin, a Stat3 activator, significantly reversed the effects of NaB on Glo1 expression, MG-H1 production, and the cell migration and viability. As expected, overexpression of Stat3 or Glo1 reduced NaB­induced cell death. The activation of calcium/calmodulin dependent protein kinase II gamma and reactive oxygen species production also contributed to the anticancer effect of NaB. The present study, for the first time, demonstrated that NaB greatly increases MGO production through suppression of the JAK2/Stat3/Nrf2/Glo1 pathway in DU145 cells, a cell line mimicking castration­resistant PCa (CRPC), suggesting that NaB may be a potential agent for PCa therapy.

Synthesis of struvite-enriched slow-release fertilizer using magnesium-modified biochar: Desorption and leaching mechanisms.

To improve the retention and slow-release abilities of nitrogen (N) and phosphorus (P), an 82 %-purity struvite fertilizer (MAP-BC) was synthesized using magnesium-modified biochar and a solution with a 2:1 concentration ratio of NH4+ to PO43- at a pH of 8. Batch microscopic characterizations and soil column leaching experiments were conducted to study the retention and slow-release mechanisms and desorption kinetics of MAP-BC. The slow-release mechanism revealed that the dissolution rate of high-purity struvite was the dominant factor of NP slow release. The re-adsorption of NH4+ and PO43- by biochar and unconsumed MgO prolonged slow release. Mg2+ ionized by MgO could react with PO43- released from struvite to form Mg3(PO4)2. The internal biochar exhibited electrostatic attraction and pore restriction towards NH4+, while magnesium modification and nutrient loading formed a physical antioxidant barrier that ensured long-term release. The water diffusion experiment showed a higher cumulative release rate for PO43- compared to NH4+, whereas in soil column leaching, the trend was reversed, suggesting that soil's competitive adsorption facilitated the desorption of NH4+ from MAP-BC. During soil leaching, cumulative release rates of NH4+ and PO43- from chemical fertilizers were 3.55-3.62 times faster than those from MAP-BC. The dynamic test data for NH4+ and PO43- in MAP-BC fitted the Ritger-Peppas model best, predicting release periods of 163 days and 166 days, respectively. The leaching performances showed that MAP-BC reduced leaching solution volume by 5.58 % and significantly increased soil large aggregates content larger than 0.25 mm by 24.25 %. The soil nutrients retention and pH regulation by MAP-BC reduced leaching concentrations of NP. Furthermore, MAP-BC significantly enhanced plant growth, and it is more suitable as a NP source for long-term crops. Therefore, MAP-BC is expected to function as a long-term and slow-release fertilizer with the potential to minimize NP nutrient loss and replace part of quick-acting fertilizer.

The utility of Hibiscus sabdariffa L. to prepare metal oxides NPs for clinical application on osteoporosis supported by theoretical study.

Green synthesis of metal oxides as a treatment for bone diseases is still exploring. Herein, MgO and Fe2O3 NPs were prepared from the extract of Hibiscus sabdariffa L. to study their effect on vit D3, Ca+2, and alkaline phosphatase enzyme ALP associated with osteoporosis. Computational chemistry was utilized to gain insight into the possible interactions. These oxides were characterized by X-ray diffraction, SEM, FTIR, and AFM. Results revealed that green synthesis of MgO and Fe2O3 NPs was successful with abundant. MgO NPs were in vitro applied on osteoporosis patients (n = 35) and showed a significant elevation of vit D3 and Ca+2 (0.0001 > p < 0.001) levels, compared to healthy volunteers (n = 25). Thus, Hibiscus sabdariffa L. is a good candidate to prepare MgO NPs, with a promising enhancing effect on vit D3 and Ca+2 in osteoporosis. In addition, interactions of Fe2O3 and MgO NPs with ALP were determined by molecular docking study.