RESUMO
The realization of a controllable transparent conducting system with selective light transparency is crucial for exploring many of the most intriguing effects in top-illuminated optoelectronic devices. However, the performance is limited by insufficient electrical conductivity, low work function, and vulnerable interface of traditional transparent conducting materials, such as tin-doped indium oxide. Here, it is reported that two-dimensional (2D) titanium carbide (Ti3 C2 Tx ) MXene film acts as an efficient transparent conducting electrode for the lead sulfide (PbS) colloidal quantum dots (CQDs) photodiode with controllable near infrared transmittance. The solution-processed interface engineering of MXene and PbS layers remarkably reduces the interface defects of MXene/PbS CQDs and the carrier concentration in the PbS layer. The stable Ti3 C2 Tx /PbS CQDs photodiodes give rise to a high specific detectivity of 5.51 × 1012 cm W-1 Hz1/2 , a large dynamic response range of 140 dB, and a large bandwidth of 0.76 MHz at 940 nm in the self-powered state, ranking among the most exceptional in terms of comprehensive performance among reported PbS CQDs photodiodes. In contrast with the traditional photodiode technologies, this efficient and stable approach opens a new horizon to construct widely used infrared photodiodes with CQDs and MXenes.
RESUMO
An electron transport layer is essential for effective operation of planar perovskite solar cells. In this Article, PW12-TiO2 composite was used as the electron transport layer for the planar perovskite solar cell in the device structure of fluorine-doped tin oxide (FTO)-glass/PW12-TiO2/perovskite/spiro-OMeTAD/Au. A proper downward shift of the conduction band minimum (CBM) enhanced electron extraction from the perovskite layer to the PW12-TiO2 composite layer. Consequently, the common hysteresis effect in TiO2-based planar perovskite solar cells was significantly reduced and the open circuit voltage was greatly increased to about 1.1 V. Perovskite solar cells using the PW12-TiO2 compact layer showed an efficiency of 15.45%. This work can contribute to the studies on the electron transport layer and interface engineering for the further development of perovskite solar cells.