Statistical Reliability Analysis of Ultrasonic Velocity Method for Predicting Residual Strength of High-Strength Concrete under High-Temperature Conditions.

Herein, we conducted a comprehensive statistical assessment of the ultrasonic pulse velocity (UPV) method's effectiveness in predicting concrete strength under diverse conditions, specifically early age, middle age, and high-temperature exposure. The concrete mixtures, with water-to-cement (W/C) ratios of 0.33 and 0.28, were classified as granite aggregate or coal-ash aggregate mixes. Compressive strength and UPV measurements were performed under these conditions, and subsequent statistical analyses treated the identified factors as distinct groups. The results revealed a substantial difference in compressive strength between specimens at early age (average of 13.01) and those at middle age (average of 41.96) and after high-temperature exposure (average of 48.08). Conversely, UPV analysis showed an insignificant difference between the early-age specimens and those after high-temperature exposure. The analysis of the W/C ratio and coarse aggregate demonstrated significant differences (p-value < 0.05) in compressive strength between specimens in middle age and those exposed to high temperatures, excluding the early-age specimens. However, UPV analysis revealed insignificant differences, with p-values of 0.67 and 0.38 between specimens at an early age and post-high-temperature exposure, respectively. Regression analysis identified suitable functions for each scenario, emphasizing the importance of a strength prediction model for concrete after high-temperature exposure, particularly considering the W/C ratio. Since concrete showed statistically different compressive strength, UPV, and strength prediction models in three conditions (early age, middle age, and high temperature), different strength prediction models must be used for the purpose of accurately predicting the strength of concrete.

Evaluation on Early Strength Development of Concrete Mixed with Non-Sintered Hwangto Using Ultrasonic Pulse Velocity.

Currently, in order to reduce the greenhouse gases of global warming, research on alternative cement materials is being actively conducted in the construction industry to reduce cement use, and it is judged to be important to evaluate the timing of form removal for the initial age. Therefore, in this study, we evaluated the initial mechanical properties of concrete in which cement was partially replaced with non-sintered hwangto (NHT). Specimens without NHT (namely, normal mortar (NM) and normal concrete (NC)) and specimens with NHT (namely, non-sintered hwangto mortar (HTM) and non-sintered hwangto concrete (HTC)) were prepared. NHT was substituted for 15% and 30% of cement. Two water-to-binder (W/B) ratios, 41% and 33%, were used to analyze the variation in the mechanical properties according to the cement and NHT content per unit volume of concrete. The compressive strength and ultrasonic pulse velocity (UPV) were measured. Experimental results indicated that compressive strength decreased with an increase in NHT content. The mortar with NHT substitution rates of 15% and 30% exhibited higher UPV than NM at a W/B ratio of 41%, in contrast to the behavior observed for concrete. The UPVs of most specimens were similar regardless of the NHT substitution rate. The correlation between the compressive strength and UPV of HTC was analyzed, and therefrom, exponential equations with a high correlation coefficient (R2) were proposed for strength prediction; the resulting predictions were compared with the results of previous compressive strength prediction models.

Correlation Analysis of Ultrasonic Pulse Velocity and Mechanical Properties of Normal Aggregate and Lightweight Aggregate Concretes in 30-60 MPa Range.

This study classified the strength of normal aggregate concrete (NC) and lightweight aggregate concrete (LC) into three levels (30, 45, and 60 MPa). In particular, the compressive strength, ultrasonic pulse velocity, and elastic modulus were measured and analyzed at the ages of 1, 3, 7, and 28 days to establish the correlation between the compressive strength and the ultrasonic pulse velocity and between the elastic modulus and the ultrasonic pulse velocity. In addition, this study proposed strength and elastic modulus prediction equations as functions of the ultrasonic pulse velocity. The developed equations were compared with previously proposed strength prediction equations. The results showed that the measured mechanical properties of NC tended to be higher at all ages than in LC. However, LC45 exhibited relatively high compressive strength compared to NC45. The relative mechanical properties of LC compared to NC were the highest at 45 MPa and the lowest at 60 MPa. The relative ultrasonic pulse velocity converged at all levels as the age increased. Moreover, the correlation between the compressive strength and the ultrasonic pulse velocity in LC exceeded that of NC, and in LC, the correlation coefficient decreased as the strength increased. The correlation coefficients between the elastic modulus and the ultrasonic pulse velocity were high at all levels except for LC45. Finally, this study proposed compressive strength and elastic modulus prediction equations as an exponential function of LC. The proposed equations outperformed the previously proposed strength prediction equations.

Effect of Thermal Properties of Aggregates on the Mechanical Properties of High Strength Concrete under Loading and High Temperature Conditions.

The effect of the thermal properties of aggregates on the mechanical properties of high-strength concrete was evaluated under loading and high-temperature conditions. For the concrete, granite was selected as a natural aggregate, and ash-clay and clay as lightweight aggregates. The mechanical properties of the concrete (stress-strain, compressive strength, elastic modulus, thermal strain, and transient creep) were evaluated experimentally under uniform heating from 20 to 700 °C while maintaining the load at 0, 20, and 40% of the compressive strength at room temperature. Experimental results showed that the concrete containing lightweight aggregates had better mechanical properties, such as compressive strength and elastic modulus, than that of the concrete with a granite aggregate at high temperature. In particular, the concrete containing lightweight aggregates exhibited high compressive strength (60-80% of that at room temperature) even at 700 °C. Moreover, the concrete containing granite exhibited a higher thermal strain than that containing lightweight aggregates. The influence of the binding force under loaded conditions, however, was found to be larger for the latter type. The transient creep caused by the loading was constant regardless of the aggregate type below 500 °C but increased more rapidly when the coefficient of the thermal expansion of the aggregate was above 500 °C.